Search

The attachment of bacteria and other microbes to natural and artificial surfaces leads to the development of biofilms, which can further cause nosocomial infections. Thus, an important field of research is the development of new materials capable of preventing the initial adhesion of pathogenic microorganisms. In this work, novel polymer/particle composite materials, based on a polythiourethane (PTU) matrix and either spherical (s-ZnO) or tetrapodal (t-ZnO) shaped ZnO fillers, were developed and characterized with respect to their mechanical, chemical and surface properties. To then evaluate their potential as anti-fouling surfaces, the adhesion of two different pathogenic microorganism species, Staphylococcus aureus and Candida glabrata, was studied using atomic force microscopy (AFM). Our results show that the adhesion of both S. aureus and C. glabrata to PTU and PTU/ZnO is decreased compared to a model surface polydimethylsiloxane (PDMS). It was furthermore found that the amount of both s-ZnO and t-ZnO filler had a direct influence on the adhesion of S. aureus, as increasing amounts of ZnO particles resulted in reduced adhesion of the cells. For both microorganisms, material composites with 5 wt.% of t-ZnO particles showed the greatest potential for anti-fouling with significantly decreased adhesion of cells. Altogether, both pathogens exhibit a reduced capacity to adhere to the newly developed nanomaterials used in this study, thus showing their potential for bio-medical applications.

The attachment of bacteria and other microbes to natural and artificial surfaces leads to the development of biofilms, which can further cause nosocomial infections. Thus, an important field of research is the development of new materials capable of preventing the initial adhesion of pathogenic microorganisms. In this work, novel polymer/particle composite materials, based on a polythiourethane (PTU) matrix and either spherical (s-ZnO) or tetrapodal (t-ZnO) shaped ZnO fillers, were developed and characterized with respect to their mechanical, chemical and surface properties. To then evaluate their potential as anti-fouling surfaces, the adhesion of two different pathogenic microorganism species, Staphylococcus aureus and Candida glabrata, was studied using atomic force microscopy (AFM). Our results show that the adhesion of both S. aureus and C. glabrata to PTU and PTU/ZnO is decreased compared to a model surface polydimethylsiloxane (PDMS). It was furthermore found that the amount of both s-ZnO and t-ZnO filler had a direct influence on the adhesion of S. aureus, as increasing amounts of ZnO particles resulted in reduced adhesion of the cells. For both microorganisms, material composites with 5 wt.% of t-ZnO particles showed the greatest potential for anti-fouling with significantly decreased adhesion of cells. Altogether, both pathogens exhibit a reduced capacity to adhere to the newly developed nanomaterials used in this study, thus showing their potential for bio-medical applications. [ABSTRACT FROM AUTHOR]

In this study, polydimethylsiloxane (PDMS)/polythiourethane (PTU) composite reinforced with tetrapodal shaped micro-nano ZnO particles (t-ZnO) was successfully produced by a versatile, industrially applicable polymer blending process. On the surface of this composite, PDMS is distributed in the form of microdomains embedded in a PTU matrix. The composite inherited not only good mechanical properties originating from PTU but also promising fouling-release (FR) properties due to the presence of PDMS on the surface. It was shown that the preferential segregation of PDMS domains at the polymer/air interface could be attributed to the difference in the surface free energy of PDMS and PTU. The PDMS microdomains at the PTU/air interface significantly reduced the barnacle adhesion strength on the composite. Both the pseudo- and natural barnacle adhesion strength on the composite was approximately 0.1 MPa, similar to that on pure PDMS. The pseudo-barnacle adhesion on reference surfaces AlMg3 and PTU reached approximately 4 and 6 MPa, respectively. Natural barnacles could not be removed intact from AlMg3 and PTU surfaces without breaking the shell, indicating that the adhesion strength was higher than the mechanical strength of a barnacle shell (approximately 0.4 MPa). The integrity of PDMS microdomains was maintained after 12 months of immersion in seawater and barnacle removal. No surface deteriorations were found. In short, the composite showed excellent potential as a long-term stable FR coating for marine applications.