In this study, thermo and pH-sensitive multifunctional poly (N-isopropylacrylamide-co- N,N'-methylenebisacrylamide, Poly(NIPAAm-co-MBA) - (N-4-amino-2-methylene-4-oxobutanoic acid, IAM) named as (PNM@IAM) core-shell microgels are synthesized by inverse microemulsion polymerization technique using two monomers, N-isopropylacrylamide (NIPAAm) and N-4-amino-2-methylene-4-oxobutanoic acid (IAM). The formation of the microgels are confirmed by 1H nuclear magnetic resonance (1H NMR) and attenuated total reflection fourier transform infrared (ATR-FTIR) spectra. The light transmittance study shows that the microgels prepared at different concentrations and pHs exhibit different physical properties. The phase transition temperature is increased with the addition of IAM. Dynamic light scattering (DLS) analysis reveals that the swelling of the microgels at basic environment is due to the deprotonation of the weak acid groups in IAM. The metal ion chelating test shows that the core-shell PNM@IAM could effectively absorb metal ions in highly basic environment. The absorption and release of heavy metal ions from aqueous solution could be controlled by adjusting the pH of the reaction environment. [ABSTRACT FROM AUTHOR]

In this study, we report a novel approach to fabricate an organic/inorganic magnetic hybrid system capable of self-healing, wherein a polycaprolactone-poly(furfuryl glycidyl ether) copolymer (PCLF) serving as the structure template was first synthesized, followed by the incorporation of iron oxide nanoparticles-decorated multiwalled carbon nanotubes (IONPs-MWCNTs) and 1,1′-(methylenedi-4,1-phenylene)bismaleimide (BMI) into the polymer matrix to form a covalently crosslinked hybrid network via a Diels−Alder (DA) reaction. For this system, the reactive combination of diene and dienophile from furan/maleimide, MWCNT/furan, and MWCNT/maleimide could facilely induce multiple DA reactions that imparted a versatile route to efficiently introduce IONPs-MWCNTs into the organic polymer hosts, resulting in a uniform distribution of IONPs-MWCNTs that led to a hybrid system with superparamagnetic properties. Beside the magnetic behavior, such material synergistically exhibited a superior ability for healing scratch defects via a retro-DA reaction. Therefore, this crosslinked PCLF/BMI/IONPs-MWCNTs hybrid system which exhibits multifunctional properties including superparamagnetic behavior and self-repairability can serve as an intelligent material for developing advanced electromagnetic applications. [ABSTRACT FROM AUTHOR]

This work investigated the cyclization possibility and melt spinnability of carbon fiber precursors, poly(acrylonitrile-co-methyl acrylate) (AN/MA) and poly(acrylonitrile-co-dimethyl itaconate) (AN/DMI). The onset temperature of cyclization of the AN/DMI copolymer is lower than that of the AN/MA copolymer and also the polyacrylonitrile (PAN) homopolymer. The enthalpy (ΔH) of the AN/DMI copolymer is about 3–4 times that of the PAN homopolymer and about 1.8 times that of the AN/MA copolymer, indicating that the degree of cyclization of the AN/DMI copolymer is relatively higher. The melt dwell time of the AN/DMI copolymer is increased to about 3–5 times that of the AN/MA copolymer, especially when synthesized with a feed molar ratio of AN/DMI = 85/15. The AN/DMI copolymer (AN/DMI = 85/15) has the longest melt dwell time, 24.8 min, at the lowest melting temperature, 190oC, among all the PAN-related copolymers synthesized herein. Furthermore, the AN/DMI copolymer (AN/DMI = 85/15) can be rapidly cyclized at the cyclization temperature of 260℃, which is 25℃ lower than that of the AN/MA copolymer (AN/MA = 85/15). In short, this work demonstrates that the carbon fiber precursor made by the AN/DMI copolymer (AN/DMI = 85/15) will be superior to that of the AN/MA copolymer (AN/MA = 85/15) with respect to the melt spinnability and cyclization at low temperature. [ABSTRACT FROM AUTHOR]

In this study, we prepared a series of thermosensitive polymers with low polydispersity index (PDI) values by nitroxidemediated controlled radical polymerization (NMRP) with 2,2,6,6-tetramethyl-1-piperdinyloxy nitroxide (TEMPO) as a stable nitroxide-free radical. Poly(N-isopropyl acrylamide) (PNIPAAm)-block-poly(N-tert-butyl acrylamide) (PNTBA) was successfully synthesized, first, through polymerization with N-isopropyl acrylamide to obtain the reactive polymer PNIPAAm-TEMPO and, second, through polymerization by the addition of N-tert-butyl acrylamide (NTBA). The added molar fraction of NTBA during the second polymerization was adjusted accordingly to obtain the final polymerization product, a thermosensitive polymer (PNIPAAm-block- PNTBA), which had a targeted lower critical solution temperature (LCST). The result shows that the synthesis method used in this study effectively controlled the formation of the polymer to obtain a low PDI. The thermosensitive block copolymer, PNIPAAm-b- PNTBA (molar ratio = 9:1), with LCSTs in the range 27.7-39.8°C, was obtained through controlled living radical polymerization with PNIPAAm-TEMPO. Specifically, the 5 wt % aqueous solution of PNIPAAm-b-PNTBA (molar ratio = 9:1) had an LCST of 37.4°C; this was close to body temperature, 37°C. The 5 wt % aqueous solution of PNIPAAm-b-PNTBA (molar ratio59:1) showed potential for use in biomedical applications. [ABSTRACT FROM AUTHOR]

ABSTRACT Poly( N-isopropylacrylamide) (NIPAAm) is well known as a smart material with good thermal sensitivity and favorable biocompatibility. A series of new smart hydrogels, NIPAAm copolymerized with IAM (itaconamic acid; 4-amino-2-methylene-4-oxobutanoic acid), were synthesized through radical solution polymerization in this work. Poly(NIPAAm- co-IAM) can respond to the changes of temperature as well as pH value. Such a characteristic is due to the fact that IAM contains not only a hydrophilic acrylic acid moiety but also an acrylamide moiety to be thermal and pH sensitive. The experimental results show that the lower critical solution temperature (LCST) of the copolymer increases as the molar fraction of IAM increases. Moreover, based on the current experimental data, 3 wt % of Poly(NIPAAm- co-IAM) aqueous solution in this study exhibits a phase transition temperature (37.8°C) close to the human body temperature in the buffer solution of pH 7 possibly to be useful in drug delivery. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 42367. [ABSTRACT FROM AUTHOR]

In this study, a novel biobased poly(ethylene brassylate)-poly(furfuryl glycidyl ether) copolymer (PEBF) copolymer was synthesized and applied as a structure-directing template to incorporate graphene and 1,1′-(methylenedi-4,1-phenylene)bismaleimide (BMI) to fabricate a series of self-healing organic/inorganic hybrid materials. This ternary material system provided different types of diene/dienophile pairs from the furan/maleimide, graphene/furan, and graphene/maleimide combinations to build a crosslinked network via multiple Diels–Alder (DA) reactions and synergistically co-assembled graphene sheets into the polymeric matrix with a uniform dispersibility. The PEBF/graphene/BMI hybrid system possessed an efficient self-repairability for healing structural defects and an electromagnetic interference shielding ability in the Ku-band frequency range. We believe that the development of the biobased self-healing hybrid system provides a promising direction for the creation of a new class of materials with the advantages of environmental friendliness as well as durability, and shows potential for use in advanced electromagnetic applications. [ABSTRACT FROM AUTHOR]

In this work, a smart copolymer, Poly(nipam-co-IAM) was synthesized by copolymerization of N-isopropylacrylamide (nipam) and itaconamic acid (IAM) through reversible addition-fragmentation chain-transfer (RAFT) polymerization. Poly(nipam-co-IAM) has been studied previously synthesized via radical polymerization without stereo-control, and this work used cumyl dithiobenzoate and Ytterbium(III) trifluoromethanesulfonate as RAFT and stereo-control agents, respectively. The stereo-control result in this work shows that tacticity affects the lower critical solution temperature (LCST) and/or the profile of phase separation of Poly(nipam-co-IAM). In the pH 7 and pH 10 buffer solutions, the P(nipam-co-IAM) copolymer solutions showed soluble–insoluble–soluble transitions, i.e., both LCST and upper critical solution temperature (UCST) transitions, which had not been found previously, and the insoluble to soluble transition (redissolved behavior) occurred at a relatively low temperature. The insoluble to soluble transition of P(nipam-co-IAM) in alkaline solution occurred at a temperature of less than 45 °C. However, the redissolved behavior of P(nipam-co-IAM) was found only in the pH 7 and pH 10 buffer solutions and this redissolved behavior was more prominent for the atactic copolymers than in the isotactic-rich ones. In addition, the LCST results under our experimental range of meso content did not show a significant difference between the isotactic-rich and the atactic P(nipam-co-IAM). Further study on the soluble-insoluble-soluble (S-I-S) transition and the application thereof for P(nipam-co-IAM) copolymers will be conducted. [ABSTRACT FROM AUTHOR]

A series of semi-interpenetrating polymer network (semi-IPN) hydrogels were synthesized and investigated in this study. Linear copolymer poly(N-isopropylacrylamide-co-itaconamic acid) p(NIPAM-co-IAM), which is formed by copolymerization of N-isopropylacrylamide (NIPAM) and itaconamic acid (IAM, 4-amino-2-ethylene-4-oxobutanoic acid), was introduced into a solution of NIPAM to form a series of pH and thermo dual-responsive p(NIPAM-co-IAM)/pNIPAM semi-IPN hydrogels by free radical polymerization. The structural, morphological, chemical, and physical properties of the linear copolymer and semi-IPN hydrogels were investigated. The semi-IPN hydrogel showed high thermal stability according to thermal gravimetric analyzer (TGA). Scanning electronic microscopy (SEM) images showed that the pore size was in the range of 119~297 µm and could be controlled by the addition ratio of the linear copolymer in the semi-IPN structure. The addition of linear copolymer increased the fracture strain from 57.5 ± 2.9% to 91.1 ± 4.9% depending on the added amount, while the compressive modulus decreased as the addition increased. Moreover, the pH and thermo dual-responsive properties were investigated using differential scanning calorimetry (DSC) and monitoring the swelling behavior of the hydrogels. In deionized (DI) water, the equilibrium swelling ratio of the hydrogels decreased as the temperature increased from 20 °C to 50 °C, while it varied in various pH buffer solutions. In addition, the swelling and deswelling rates of the hydrogels also significantly increased. The results indicate that the novel pH-thermo dual-responsive semi-IPN hydrogels were synthesized successfully and may be a potential material for biomedical, drug delivery, or absorption application. [ABSTRACT FROM AUTHOR]

A novel aliphatic PA6 copolyamide (PA6(BAEA/AA))-based hot melt adhesive was synthesized from ε-caprolactam with the organic salt of bis(2-aminoethyl) adipamide (BAEA) and adipic acid (AA), with BAEA/AA content ranges from 5 to 15 mol%. The chemical structures of BAEA diamine, BAEA/AA organic salt, PA6(BAEA/AA) copolyamides, and neat PA6 were obtained using FT-IR and 1H NMR. Determined by the comonomer compositions, the relative viscosity (η r) and molecular weight (M w) of the PA6(BAEA/AA) were from 2.29 to 2.74 and from 14,530 to 19,500 g mol−1, respectively. Adding the BAEA/AA structure strongly affected the crystallization behavior and thermal properties of the copolyamides. DSC results revealed that the melting temperature (T m) of the copolyamides declined as the mole% of BAEA/AA increased in the range 5–15 mol%, and a TGA test revealed that the thermal decomposition of the copolyamides was similar to that of neat PA6. The T m , glass transition temperature (T g), and thermal stability (T d5%) with a BAEA/AA salt content of 10 mol% had the lowest values of 162.2, 40.3, 354.6 °C, respectively, while the fusion enthalpy (ΔH m) was lowest at 15 mol% (21.2 J g−1). Most remarkably, PA6(BAEA/AA) exhibits much better mechanical properties such as tensile strength (33.6–52.6 MPa) and elongation at breakage (114.7–584.5%), than the PA6 homopolymer. The peel strength of PA6 reached a maximum value of 53.4 N cm−1 at 10 mol% of BAEA/AA salt, and this value is better than those of commercial hot melt adhesives. [ABSTRACT FROM AUTHOR]

In this work, a smart copolymer, Poly(nipam-co-IAM) was synthesized by copolymerization of N -isopropylacrylamide (nipam) and itaconamic acid (IAM) through reversible addition-fragmentation chain-transfer (RAFT) polymerization. Poly(nipam-co-IAM) has been studied previously synthesized via radical polymerization without stereo-control, and this work used cumyl dithiobenzoate and Ytterbium(III) trifluoromethanesulfonate as RAFT and stereo-control agents, respectively. The stereo-control result in this work shows that tacticity affects the lower critical solution temperature (LCST) and/or the profile of phase separation of Poly(nipam-co-IAM). In the pH 7 and pH 10 buffer solutions, the P(nipam-co-IAM) copolymer solutions showed soluble⁻insoluble⁻soluble transitions, i.e., both LCST and upper critical solution temperature (UCST) transitions, which had not been found previously, and the insoluble to soluble transition (redissolved behavior) occurred at a relatively low temperature. The insoluble to soluble transition of P(nipam-co-IAM) in alkaline solution occurred at a temperature of less than 45 °C. However, the redissolved behavior of P(nipam-co-IAM) was found only in the pH 7 and pH 10 buffer solutions and this redissolved behavior was more prominent for the atactic copolymers than in the isotactic-rich ones. In addition, the LCST results under our experimental range of meso content did not show a significant difference between the isotactic-rich and the atactic P(nipam-co-IAM). Further study on the soluble-insoluble-soluble (S-I-S) transition and the application thereof for P(nipam-co-IAM) copolymers will be conducted.

Copolymerization of N -isopropylacrylamide (NIPAM), itaconamic acid (IAM; 4-amino-2-methylene-4-oxobutanoic acid) and β-cyclodextrin was investigated in this study. β-cyclodextrin was at first modified by reacting with allyl glycidyl ether to substitute its OH end groups with moieties containing double bonds to facilitate the subsequent radical copolymerization with NIPAM and IAM. It was reported that poly(NIPAM-IAM) can respond to the change of temperature as well as pH value. In this study, the structure of β-cyclodextrin was introduced to poly(NIPAM-IAM) copolymers because of its cavity structure capable of encapsulating a variety of drug molecules. The tri-component copolymers, poly(CD-NIPAM-IAM), were synthesized with different monomeric ratios of NIPAM/IAM/β-CD and the hydrogels of the tri-component copolymers were also synthesized by additionally adding N , N '-methylenebisacrylamide as a cross-linking agent. The results show that the lower critical solution temperature (LCST) of the copolymer (or hydrogel) increases as the molar fraction of IAM increases. The transmission electron microscopic (TEM) images of linear copolymers (no cross-linking) show that molecules undergo self-assembly to have a distinct core-shell structure, compared to poly(CD-NIPAM) which contains no IAM. On the other hand, the scanning electron microscopic (SEM) images of hydrogels show that the pores gradually become sheet-like structures as the molar fraction of IAM increases to enhance the water absorption capacity. In order to exhibit the thermal and pH sensitivities of poly(CD-NIPAM-IAM) as the drug carrier, the drug release of the newly synthesized hydrogels at 37 °C and different pH values, pH = 2 and pH = 7.4, was investigated using atorvastatin which was used primarily as a lipid-lowering drug. The drug release experimental result shows that poly(CD-NIPAM-IAM) as a drug carrier was pH-sensitive and has the largest release rate at pH = 7.4 at 37 °C, indicating it is useful to release drugs in a neutral or alkaline (intestinal) environment.