Search

The microenvironments of metal single‐atoms (SAs) have important effects on their physicochemical properties. However, the understanding of the relationship between the coordination configuration of SAs and their properties is insufficient. Here, a sacrificing template strategy is developed to anchor La‐SAs on interconnected graphene nanocages (La‐N‐Cl/GNC), where La‐SAs are located above the graphene plane and one La atom coordinated with four N atoms in the graphene plane and with one Cl atom along the axial direction. Theoretical calculations demonstrated that asymmetrically La‐SAs are more conducive to breaking local charge symmetry. Consequently, additional electrical dipoles along the axial direction are generated, leading to unprecedented dipolar polarization loss and strong electromagnetic wave absorption properties. Moreover, the film constructed by asymmetrically‐coordinated La‐N‐Cl/GNC with a mass density of 0.084 g cm−3 exhibits superior flexibility, excellent mechanical strength, and moderate thermal insulation properties, guaranteeing its practical applications in harsh environments. These findings not only shed light on the relationships between asymmetrically coordinated SAs and their dielectric properties at the atomic level but also provide an efficient method for preparing multifunctional films. [ABSTRACT FROM AUTHOR]

The kinetics and durability of conversion‐based anodes greatly depend on the intrinsic stress regulating ability of the electrode materials, which has been significantly neglected. Herein, a stress dissipation strategy driven by multi‐interface built‐in electric fields (BEFs) and architected structure, is innovatively proposed to design ultrafast and long‐term sodium ion storage anodes. Binary Mo/Fe sulfide heterostructured nanorods with multi‐interface BEFs and staggered cantilever configuration are fabricated to prove our concept. Multi‐physics simulations and experimental results confirm that the inner stress in multiple directions can be dissipated by the multi‐interface BEFs at the micro‐scale, and by the staggered cantilever structure at the macro‐scale, respectively. As a result, our designed heterostructured nanorods anode exhibits superb rate capability (332.8 mAh g−1 at 10.0 A g−1) and durable cyclic stability over 900 cycles at 5.0 A g−1, outperforming other metal chalcogenides. This proposed stress dissipation strategy offers a new insight for developing stable structures for conversion‐based anodes. [ABSTRACT FROM AUTHOR]

Aiming at the problems of long reaction time and the risk of explosion polymerization of acrylate resin, a small amount of ferrocene (Fc) is added to the existing dibenzoyl peroxide (BPO)/N,N‐dimethylaniline (DMA) initiators, and the compound redox initiators (BPO/DMA/ (Fc)) are proposed for acrylate resin polymerization at room temperature. The effect of the content of Fc in the resin on the reaction efficiency and the molding quality of products is researched, and the initiation mechanism of the compound redox initiators is analyzed. It is found that with the addition of Fc, the reaction time of the resin can be shortened by 68% at maximum, the heat release temperature of the resin can be reduced by 40% at maximum, the molecular weight of the reaction products can be increased by 74% at maximum, the tensile and bending properties of the resin castings are increased by 23% and 35% at maximum, respectively, and the bending strength and bending modulus are increased by 57% and 27% at maximum, respectively. The compound redox initiators proposed in this paper can improve the molding efficiency and quality of the product, lay a foundation for the application of acrylic resin in the field of pultrusion molding, perfusion molding, and other in situ molding of thermoplastic composites. [ABSTRACT FROM AUTHOR]

Ice accumulation on airfoils and engines seriously endangers fight safety. The design of anti-icing/de-icing systems calls for an accurate measurement of the adhesion strength between ice and substrates. In this research, a test bench for adhesion strength measurement is designed and built. Its reliability and accuracy are verified by the calibration. The adhesion strength is first measured at different loading speeds and freezing times, and the most suitable values are determined based on the results. Then, the variation in adhesion strength with heating temperatures at different initial substrate temperatures and different heating powers is investigated. Parameter AW is defined to evaluate the heating power from the point of view of energy consumption and adhesion strength. As a result, the loading speed and the freezing time are determined to be 0.5 mm/s and 90 min, respectively. The adhesion strength degrades as the heating temperature increases. As the initial temperature drops, the adhesion strength decreases more slowly. Furthermore, the temperature of WAS (Weak Adhesion State) under heating varies with the initial temperature. Heating with a high power will yield more reduction in adhesion strength for the same temperature increase. The values of AW illustrate that a medium power heating is more favorable to reduce the adhesion strength with a low energy consumption. [ABSTRACT FROM AUTHOR]