Search

A combination of 89Y and 119Sn NMR spectroscopy and DFT calculations are used to investigate phase evolution, local structure and disorder in Y2Zr2−xSnxO7 ceramics, where a phase change is predicted, from pyrochlore to defect fluorite, with increasing Zr content. The ability of NMR to effectively probe materials that exhibit positional and compositional disorder provides insight into the atomic-scale structure in both ordered and disordered phases and, by exploiting the quantitative nature of the technique, we are able to determine detailed information on the composition of the phase(s) present and the average coordination number (and next-nearest neighbour environment) of the cations. In contrast to previous studies, a more complex picture of the phase variation with composition emerges, with single-phase pyrochlore found only for the Sn end member, and a single defect fluorite phase only for x = 0 to 0.6. A broad two-phase region is observed, from x = 1.8 to 0.8, but the two phases present have very different composition, with a maximum of 13% Zr incorporated into the pyrochlore phase, whereas the composition of the defect fluorite phase varies throughout. Preferential ordering of the anion vacancies in the defect fluorite phase is observed, with Sn only ever found in a six-coordinate environment, while remaining vacancies are shown to be more likely to be associated with Zr than Y. Our findings are then discussed in the light of those from previous studies, many of which utilize diffraction-based approaches, where, in most cases, a single phase of fixed composition has been assumed for the refinement procedure. The significant and surprising differences encountered demonstrate the need for complementary approaches to be considered for a detailed and accurate picture of both the long- and short-range structure of a solid to be achieved. [ABSTRACT FROM AUTHOR]

This study investigated the creep deformation properties of GH3535, a Ni–Mo–Cr corrosion resistant structural alloy being considered for use in future Gen IV molten salt nuclear reactors (MSR) operating at around 700 °C. Creep testing of the alloy was conducted at 650–750 °C under applied stresses between 85–380 MPa. From the creep rupture results the long term creep strain and rupture life of the alloy were estimated by applying the Dorn Shepard and Larson Miller time-temperature parameters and the alloy's allowable ASME design stresses at the MSR's operating temperature were evaluated. The material's microstructural degradation at creep rupture was characterised using scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). The microstructural study revealed that the material failure was due to wedge cracking at triple grain boundary points and cavitation at coarse secondary grain boundary precipitates, nucleated and grown during high temperature exposure, leading to intergranular crack propagation. EBSD local misorientation maps clearly show that the root cause of cavitation and crack propagation was due to large strain localisation at the grain boundaries and triple points instigated by grain boundary sliding during creep deformation. This caused the grain boundary decohesion and subsequent material failure. [ABSTRACT FROM AUTHOR]

A combination of (89)Y and (119)Sn NMR spectroscopy and DFT calculations are used to investigate phase evolution, local structure and disorder in Y2Zr2-xSnxO7 ceramics, where a phase change is predicted, from pyrochlore to defect fluorite, with increasing Zr content. The ability of NMR to effectively probe materials that exhibit positional and compositional disorder provides insight into the atomic-scale structure in both ordered and disordered phases and, by exploiting the quantitative nature of the technique, we are able to determine detailed information on the composition of the phase(s) present and the average coordination number (and next-nearest neighbour environment) of the cations. In contrast to previous studies, a more complex picture of the phase variation with composition emerges, with single-phase pyrochlore found only for the Sn end member, and a single defect fluorite phase only for x = 0 to 0.6. A broad two-phase region is observed, from x = 1.8 to 0.8, but the two phases present have very different composition, with a maximum of 13% Zr incorporated into the pyrochlore phase, whereas the composition of the defect fluorite phase varies throughout. Preferential ordering of the anion vacancies in the defect fluorite phase is observed, with Sn only ever found in a six-coordinate environment, while remaining vacancies are shown to be more likely to be associated with Zr than Y. Our findings are then discussed in the light of those from previous studies, many of which utilize diffraction-based approaches, where, in most cases, a single phase of fixed composition has been assumed for the refinement procedure. The significant and surprising differences encountered demonstrate the need for complementary approaches to be considered for a detailed and accurate picture of both the long- and short-range structure of a solid to be achieved.

The hydrolytic stability of lanthanide and actinide selective mono- and polyphosphonate-functionalized mesoporous zirconium titanium oxide adsorbents has been investigated in nitric acid solutions. Hydrolytic degradation of the surfaces, as measured through the fractional loss of phosphorus and elements of the oxide framework, increased by more than an order of magnitude as the nitric acid concentration was increased from 0 to 2 mol/L. The unfunctionalized parent oxide suffered considerable dissolution in 2 mol/L acid over a period of 72 h. Under identical conditions, the fractional Zr and Ti release was reduced to 1 × 10(-2) for monophosphonate functionalized hybrids and reached as low as 1 × 10(-6) for trisphosphonate functionalized variants. The bisphosphonates showed intermediate values. The leaching of P, Zr and Ti was found to be incongruent with the Zr leaching to a lesser extent implying enhanced stability of the Zr-O-P bond. Quantitative analysis of the dissolution kinetics indicated a parabolic dissolution model with a rate constant in the range of 0.5-1.5 mg g(-1) min(-1/2) for the elemental leaching of P, Ti, and Zr. The leaching of Zr from the mesoporous matrix was relatively more complex than for the other elements with evidence of a leaching mechanism involving two processes. ToF-SIMS and DRIFT analysis demonstrated that after leaching in 2 M HNO3 for 24 h, a significant proportion of grafted ligands remained on the surface. The oxide functionalized with amino trismethylenephosphonic acid, which had previously shown excellent (153)Gd(3+) selectivity, was demonstrated to have outstanding stability, with low fractional elemental losses and preservation of mesoporous texture even after leaching for 24 h in 2 M HNO3. This suggests this particular hybrid to be worthy of additional study.

A series of functional hybrid inorganic-organic adsorbent materials have been prepared through postsynthetic grafting of mesoporous zirconium titanate xerogel powders using a range of synthesized and commercial mono-, bis-, and tris-phosphonic acids, many of which have never before been investigated for the preparation of hybrid phases. The hybrid materials have been characterized using thermogravimetric analysis, diffuse reflectance infrared (DRIFT) and 31P MAS NMR spectroscopic techniques and their adsorption properties studied using a 153Gd radiotracer. The highest level of surface functionalization (molecules/nm2) was observed for methylphosphonic acid (∼3 molecules/nm2). The level of functionalization decreased with an increase in the number of potential surface coordinating groups of the phosphonic acids. Spectral decomposition of the DRIFT and 31P MAS NMR spectra showed that each of the phosphonic acid molecules coordinated strongly to the metal oxide surface but that for the 1,1-bis-phosphonic acids and tris-phosphonic acids the coordination was highly variable resulting in a proportion of free or loosely coordinated phosphonic acid groups. Functionalization of a porous mixed metal oxide framework with the tris-methylenephosphonic acid (ATMP-ZrTi-0.33) resulted in a hybrid with the highest affinity for 153Gd3+ in nitric acid solutions across a wide range of acid concentrations. The ATMP-ZrTi-0.33 hybrid material extracted 153Gd3+ with a Kd value of 1×10(4) in 0.01 M HNO3 far exceeding that of the other hybrid phases. The unfunctionalized mesoporous mixed metal oxide had negligible affinity for Gd3+ (Kd<100) under identical experimental conditions. It has been shown that the presence of free or loosely coordinated phosphonic acid groups does not necessarily translate to affinity for 153Gd3+. The theoretical cation exchange capacity of the ATMP-ZrTi-0.33 hybrid phase for Gd3+ has been determined to be about 0.005 mmol/g in 0.01 M HNO3. This behavior and that of the other hybrid phases suggests that the surface-bound ATMP ligand functions as a chelating ligand toward 153Gd3+ under these acidic conditions.

Template synthesis of metal oxides can create materials with highly controlled and reproducible pore structures that can be optimized for particular applications. Zirconium titanium oxides (25:75 mol %) with three different pore structures were synthesized in order to relate polymer loading capacity to macropore architecture. Sol-gel chemistry was used to prepare the materials in conjunction with (i) agarose gel templating, (ii) no template, and (iii) stearic acid templating. The three materials possessed high surface areas (212-316 m(2) g(-1)). Surface modification was performed postsynthetically using propionic acid (a monomer), glutaric acid (a dimer), and three molecular weights of poly(acrylic acid) (2000, 100,000, and 250,000 g mol(-1)). Higher loading (mg g(-1)) was observed for the polymers than for the small molecules. Following surface modification, a perceptible decrease in surface area and mesopore volume was noted, but both mesoporosity and macroporosity were retained. The pore architecture had a strong bearing on the quantity and rate of polymer incorporation into metal oxides. The templated pellet with hierarchical porosity outperformed the nontemplated powder and the mesoporous monolith (in both loading capacity and surface coverage). The materials were subjected to irradiation with (60)Co gamma-rays to determine the radiolytic stability of the inorganic support and the hybrid material containing the monomer, dimer, and polymer. The polymer and the metal oxide substrate demonstrated notable radiolytic stability.