Search

In this contribution, the relaxation and diffusional behaviors of low viscous fluids, water and methanol confined into mesoporous silica and controlled size pore glass were investigated. The engineered porous systems are relevant to geologically important subsurface energy materials. The engineered porous proxies were characterized by Brunauer–Emmett–Teller (BET) surface analyzer, nuclear magnetic resonance (NMR) spectroscopy, and electron microscopy (EM) to determine surface area, pore-wall protonation and morphology of these materials, respectively. The confined behavior of the low viscous fluids was studied by varying pore diameter, fluid-to-solid ratio, temperature, and pressure, and then compared to bulk liquid state. Both relaxation and diffusion behaviors for the confined fluids showed increasing deviation from pure bulk fluids as the fluid-to-solid ratio was decreased, and surface-to-volume ratio (S/V) was varied. Variable pressure deuteron NMR relaxation of confined D2O and confined methanol, deuterated at the hydroxyl or methyl positions, were performed to exploit the sensitivity of the deuteron quadrupole moment to molecular rotation. The methanol results demonstrated greater pressure dependence than those for water only in bulk. The deviations from bulk liquid behavior arise from different reasons such as confinement and the interactions between confined fluid and the nano-pore wall. The results of the present report give insight into the behavior of low viscosity fluid in nano-confined geometries under different state conditions. [ABSTRACT FROM AUTHOR]

We investigate dynamics of water (H2O) and methanol (CH3OH and CH3OD) inside mesoporous silica materials with pore diameters of 4.0, 2.5, and 1.5 nm using low-field (LF) nuclear magnetic resonance (NMR) relaxometry. Experiments were conducted to test the effects of pore size, pore volume, type of fluid, fluid/solid ratio, and temperature on fluid dynamics. Longitudinal relaxation times (T1) and transverse relaxation times (T2) were obtained for the above systems. We observe an increasing deviation in confined fluid behavior compared to that of bulk fluid with decreasing fluid-to-solid ratio. Our results show that the surface area-to-volume ratio is a critical parameter compared to pore diameter in the relaxation dynamics of confined water. An increase in temperature for the range between 25 and 50°C studied did not influence T2 times of confined water significantly. However, when the temperature was increased, T1 times of water confined in both silica-2.5 nm and silica-1.5 nm increased, while those of water in silica-4.0 nm did not change. Reductions in both T1 and T2 values as a function of fluid-to-solid ratio were independent of confined fluid species studied here. The parameter T1/T2 indicates that H2O interacts more strongly with the pore walls of silica-4.0 nm than CH3OH and CH3OD.

We investigate dynamics of water (H 2 O) and methanol (CH 3 OH and CH 3 OD) inside mesoporous silica materials with pore diameters of 4.0, 2.5, and 1.5 nm using low-field (LF) nuclear magnetic resonance (NMR) relaxometry. Experiments were conducted to test the effects of pore size, pore volume, type of fluid, fluid/solid ratio, and temperature on fluid dynamics. Longitudinal relaxation times (T 1 ) and transverse relaxation times (T 2 ) were obtained for the above systems. We observe an increasing deviation in confined fluid behavior compared to that of bulk fluid with decreasing fluid-to-solid ratio. Our results show that the surface area-to-volume ratio is a critical parameter compared to pore diameter in the relaxation dynamics of confined water. An increase in temperature for the range between 25 and 50°C studied did not influence T 2 times of confined water significantly. However, when the temperature was increased, T 1 times of water confined in both silica-2.5 nm and silica-1.5 nm increased, while those of water in silica-4.0 nm did not change. Reductions in both T 1 and T 2 values as a function of fluid-to-solid ratio were independent of confined fluid species studied here. The parameter T 1 /T 2 indicates that H 2 O interacts more strongly with the pore walls of silica-4.0 nm than CH 3 OH and CH 3 OD., (Copyright © 2020 Ok, Hwang, Liu, Welch, Sheets, Cole, Liu and Mou.)