Search

The effect of polysilazane on the densification and mechanical properties of SiC f /SiC composites was examined thoroughly. The polysilazane was infiltrated into the fiber area, followed by pyrolysis at 1450°C for 4 h in an argon atmosphere. Furthermore, the SiC fabrics contain the pyrolyzed polysilazane was infiltrated by β-SiC slurry and sintered at 1750°C for 2 h in an argon atmosphere. The density of SiC f /SiC composites with and without the addition of polysilazane was 2.65 and 3.05 g/cm 3 , respectively. The pores in the fiber area were observed for the SiC f /SiC composites with the addition of polysilazane. However, the fine-grained size in the matrix area was obtained by the addition of polysilazane. The average grain size of the SiC f /SiC composite with and without the addition of polysilazane was 253 and 740 nm, respectively. Indeed, the hardness of the matrix area for SiC f /SiC composites with the addition of polysilazane (31.6 ± 1.8 GPa) was higher compared to SiC f /SiC composites without polysilazane (27.4 ± 1.6 GPa).