The production of hydrocarbon (C7-C20) and alcohol (C11-C19) from fatty acid methyl esters (FAMEs) compound are produced from the transesterification of the seed oil of the Nyamplung that has been conducted by the catalytic hydrocracking using Al-MCM-41 and Pd2+-impregnated-Al-MCM-41 catalysts. The performance of catalysts were compared by various analysis including the acidity that was determined by pyridine and FTIR, the crystal structure observed by XRD, the surface area and pore volume analyzed by BET/BJH, the surface morphology observed by TEM, the metal on the surface of catalyst observed by XPS and the product of the hydrocracking analyzed by GC-MS. Hexagonal structure of the MCM-41(100) was shown in the 2θ = 3o-5o of the diffractogram. The presence of impregnated Al and Pd observed at the 2θ = 20o and 34o, respectively. The Pd/Al-MCM-41 catalyst was more acidic than Al-MCM-41 catalyst. The surface area and pore volume of the catalyst decreased after the impregnation process. The tendency of catalytic hydrocracking of hydrocarbon produced was indicated that more amount of Palladium have more hydrocarbons aliphatic than alcohol.

SnO2 nanoparticles have been synthesized by high voltage electrolysis. Tin bare was used for anode and cathode. The effect of potentials and electrolyte were studied. The particles obtained after electrolysis was characterized using X-ray Diffraction (XRD). The diffractogram is in agreement with the standard diffraction pattern of SnO2 which is identified as tetragonal structure. The Fourier Transform Infrared (FTIR) spectrum indicates that there is a vibration of Sn–O asymmetric at 580 cm-1. The optimum potential for SnO2 nanoparticles synthesis is 60 V at 0.06 M HCl which shows the highest UV-Vis spectrum. The absorption peak of SnO2 nanoparticles by UV-Vis spectrophotometer appears at about 207 nm. The particle size analysis shows that the SnO2 nanoparticles obtained have the size distribution in a range of 25-150 nm with the highest volume at 83.11 nm.