Search

1 recurso en línea (páginas 51-61)., We report structural analysis, surface morphology, magnetic ordering, dielectric response, optical feature and the electronic structure of the Dy2BiFeO6 novel complex perovskite. The samples were produced by the standard solid-state reaction recipe. Crystallographic analysis was performed by Rietveld refinement of experimental X-ray diffraction patterns. Results show that this material crystallizes in a perovskite with orthorhombic structure, which corresponds to the Pnma (#62) space group. From the Curie-Weiss fitting on the curve of susceptibility as a function of temperature we establish that the ordering corresponds to a paramagnetic-antiferromagnetic transition, with a Weiss temperature θ=-18,5 K, which is compatible with the behavior of the inverse of susceptibility as a function of temperature, and a Néel temperatura TN=50,8 K. The Curie constant allowed for us to obtain an effective magnetic moment of 15,7 μB. The result of magnetization as a function of the applied field, measured at T=50 K, shows a magnetic hysteresis behavior that corroborate the magnetic ordering present for this temperature value. Measurements of the dielectric constant as a function of applied frequencies at room temperature give as a result a high relative dielectric constant (ε=780). The reflectance curve as a function of the wavelength reveals the typical behavior of a double perovskite-like material and permits to obtain the energy gap 2,74 eV, which is characteristic of a semiconductor material., En este trabajo reportamos el análisis estructural, morfología superficial, ordenamiento magnético, respuesta dieléctrica y característica óptica de la nueva perovskita compleja Dy2BiFeO6. Las muestras fueron producidas mediante reacción de estado sólido. El análisis cristalográfico fue realizado a través de refinamiento Rietveld de los patrones experimentales de rayos X. Los resultados muestran que este material cristaliza en una perovskita ortorrómbica correspondiente al grupo espacial Pnma (#62). Por medio del ajuste de Curie-Weiss a la respuesta de la susceptibilidad magnética en función de la temperatura se estableció que el ordenamiento magnético se relaciona con una transición paramagnético-antiferromagnético con una temperatura de Weiss θ=-18,5 K, la cual es acorde con el comportamiento del inverso de la susceptibilidad en función de la temperatura, y una temperatura de Néel TN=50,8 K. La constante de Curie permitió determinar un momento magnético efectivo de 15,7 μB. Medidas de magnetización en función del campo aplicado a T=50 K, muestran un débil comportamiento histerético, que corrobora el ordenamiento magnético presente a esa temperatura. Mediciones de la constante dieléctrica en función de la frecuencia aplicada a temperatura ambiente dan como resultado una alta constante dieléctrica relativa a bajas frecuencias (ε=780). La curva de reflectancia en función de la longitud de onda revela el comportamiento típico de un material de tipo perovskita doble y permite la obtención de la brecha de energía de 2,74 eV característico de un material semiconductor., Bibliografía: páginas 60-61.

Se presenta el método de combustión en solución y su aplicación para la síntesis de YAlO3 (YAP), fueron usados como combustibles para la reacción de combustión y síntesis la urea y glicina, del YAP. Usando las técnicas de difracción de rayos X (XRD) por el método del polvo y microscopia electrónica de barrido (MEB) fueron analizadas la parte estructural y morfológica de las muestras obtenidas. Los difractogramas de Rayos X muestran una excelente correspondencia con lo reportado en la literatura para este material. Se suministran también los resultados de las muestras de material YAlxCrx‐1O3, dopado con Cr3+ con x = 0.001, 0.01, que exhiben picos de difracción dominantes debidos a la fase ortorrómbica de YAlO3 Palabras clave.- YAP, YAlO3, Combustion method. ABSTRACT The solution‐combustion process is presented, as well as its application to the synthesis of YAlO3 (YAP). Urea and glycine were used as fuel for the combustion reaction and synthesis of the YAP. The structure and morphology of the obtained sample were analyzed using the X‐ray diffraction (XRD) powder method and scanning electron microscopy (SEM). The X‐ray patterns showed an excellent agreement with data reported in the literature for this material. Results are also given for samples of YAlxCrx‐1O3 doped with Cr3+, with x = 0.001, 0.01, which showed dominant diffraction peaks due to the orthorhombic phase of YAlO3. Keywords.- YAP, YAlO3, combustion method.

En este trabajo se reporta la síntesis del superconductor YBa2Cu3O7-δ mediante el método no convencional de sinterización por plasma en el rango de descarga luminiscente anormal (DLA). Las muestras se sometieron a diferentes temperaturas y tiempos de sinterización. Como referencia se usó una muestra superconductora obtenida por el método convencional (horno resistivo). La caracterización estructural de estas muestras se hizo por difracción de rayos X y refinamiento con el método de Rietveld. El comportamiento superconductor se determinó mediante el análisis de las curvas de magnetización en función de la temperatura según los procedimientos experimentales de enfriado en campo magnético cero (zero field cooling, ZFC) y enfriado con campo magnético aplicado (field cooling, FC). Las muestras sinterizadas por DLA presentaron características estructurales (ortorrómbica Pmmm) y superconductoras con una temperatura crítica de Tc~ 92 K, similares a las obtenidas por el método convencional, pero con una significativa reducción en las temperaturas y tiempos, bajo un ambiente adecuado de presión en el proceso de sinterización. In this study we synthesized the YBa2Cu3O7-δ superconductor using the unconventional method of plasma sintering in the range of abnormal glow discharge (AGD). The samples were treated with different sintering temperatures and times. As reference we used a superconductor sample obtained by using the conventional method (resistive furnace). The structural characterization of these samples was performed by X-ray diffraction measurements and Rietveld refinements. Superconductivity behavior was determined by analyzing magnetization curves as a function of the temperature according to zero field cooling (ZFC) and field cooling (FC) experimental procedures. The samples sintered by AGD presented structural characteristics (orthorhombic Pmmm) and superconductivity with a critical temperature of Tc ~ 92 K, which were similar to those obtained by the conventional method, but with a significant reduction of temperature and time under proper pressure environment during the sintering process.

In the present work we present geometric models of the most studied MoO3 surfaces, which were obtained using the DTMM 2.0 Molecular Modeller software. MoO3 has an orthorhombic layered structure, with each layer comprised of two interleaved planes of MoO6 octahedral. These layers are parallel to the (010) crystal plane and only oxygen ions are exposed on their surfaces. This situation results in weak van der Waals bonding between layers and in a relatively inert surface. In our approach to surface geometric structure we consider "ideal" crystal surface, in which the bulk atomic arrangement is maintained. These surfaces were generated by imaginary cleavage along appropriate planes in the bulk crystal structure.