Search

Aim The aim of this study was to analyze, by the aid of microbiological analysis and the field emission scanning electron microscopical (FE-SEM) analysis, the role of high-density polytetrafluoroethylene (d-PTFE) membranes in avoiding the microbial colonization of a nanocrystalline hydroxyapatite (nc-HA) bone graft and the involvement of this colonization in the healing process. Materials and methods Six patients underwent extraction of unrecoverable teeth, and a socket preservation technique was carried out with nc-HA synthetic bone graft and then covered with a d-PTFE membrane. After 28 days from surgery, FE-SEM analysis and BioTimer assay technique to assess the microbiological count of streptococci species were carried out. Data were collected and analyzed by the Student's t test (confidence interval: 95%). Results The mean amount of bacteria measured on the upper side of the membrane was 6.52 ± 0.50 CFU, while on the lower side, it was 6.59 ± 0.40 CFU. Significant differences were not found between the two sides of the membrane or between the different sectors (p > 0.05). The FE-SEM analysis revealed structured biofilms on both sides of the membrane: species of cocci, bacilli, and fusobacteria were recognizable in occasional settled vegetations. Conclusion Since the amount of bacteria found was low, the improved impermeability of the d-PTFE membrane permitted the healing process to proceed uneventful and without signs of infection or inflammation. Clinical relevance The infection of the graft site could lead to a failure of the socket preservation technique which could delay or compromise the rehabilitation following procedures. The use of d-PTFE can improve the bone regeneration thanks to its antimicrobial properties.

The aim of this study was to compare a transposed with a repositioned flap by assessing the periodontal effects on the second molar and primary healing after extraction of partially impacted lower third molars. A total of 24 patients requiring partially impacted mandibular wisdom tooth removal were enrolled in the study. The test group (n = 12) underwent a transposed flap procedure, whereas the control group (n = 12) underwent a repositioned flap procedure. Plaque index, probing depth, bleeding on probing, and width of keratinized tissue were recorded the day of surgery (T1) and after 60 days (T4). Wound dehiscence was assessed on the mesio-distal and bucco-lingual directions at days 2 (T2), 7 (T3), and T4. No significant differences have been observed in the periodontal parameters between the groups at T1 and T4 (P > 0.05). Similarly, no difference was found at T2, T3, and T4 in wound dehiscence incidence (P > 0.05). To date, no data exists on the use of transposed flaps in third molar surgery; thus a comparison of results cannot be done. Further studies with larger population are needed to investigate the potential advantages of this type of flap.

Objectives The aim of this study was to investigate the morphological and surface roughness changes in dental root samples following periodontal scaling by hand curette, piezoelectric ultrasonic devices or a combination of these. Methods Twenty-four monoradicular teeth extracted as a result of periodontal disease were divided into 4 groups: Group A was treated by piezoelectric ultrasonic scaler Piezon® Master 400; Group P by piezoelectric ultrasonic scaler PiezoSmart® ; Group C using Gracey curette 7/8; Group AC by a combined technique of piezoelectric ultrasonic scaler Piezon® Master 400 and Gracey curette 7/8. The treated samples were then analysed using a white light interferometer and scanning electron microscopy (SEM). Results Roughness analysis revealed major surface alterations in Group C (Sa = 24.98 μm); the samples treated using the combined technique (Group AC) showed reduced but still significant alteration (Sa = 14.48 μm), while samples treated with the piezoelectric ultrasonic devices (Group A and Group P) presented the lowest roughness values (Sa = 8.99 and Sa = 4.45 μm, respectively). A significant difference was found between groups C and P (P = 0.036). SEM analysis confirmed the roughness analysis revealing non-homogeneous surfaces in Group C, while a less morphological alteration was noted in the other groups. Conclusion All periodontal devices used in this in vitro study produced a certain degree of surface alteration. Hand curettes appear to have a major impact on surface integrity compared with piezoelectric ultrasonic devices.

Purpose: To assess and compare topographic features and preosteoblastic cell responses of a new hydrothermally treated, calcium-incorporated surface against other commercially available implant surfaces. Materials and Methods: Four different surfaces were the subject of comparison in this study: machined (MC), resorbable blast media (RBM), sandblasted/large-grit/acid-etched (SLA), and calcium-incorporated SLA (Ca-SLA). Surface morphology and roughness were first characterized by scanning electron microscope (SEM) and white light interferometer, respectively. Preosteoblastic MC3T3-E1 cells were then cultured on the titanium surfaces. Cell morphology was observed at 24 hours, 48 hours, 7 days, and 15 days by SEM; differentiation was assessed at 7, 11, and 15 days by assaying alkaline phosphatase (ALP) activity and osteocalcin (OCN) levels. Results: Surface characterization revealed nanotopographic features on Ca-SLA. At topographic analysis, SLA and Ca-SLA showed similar roughness values. Significant differences in cell differentiation parameters were found only at 15 days between the SLA surfaces (both Ca-incorporated and nonincorporated) and MC. Conclusion: Collectively, this study demonstrated that hydrothermal treatment determines the formation of nanotopography without altering the SLA microtopography. Moreover, Ca-SLA and SLA induce MC3T3-E1 cell differentiation at comparable levels.

Alveolar ridge preservation has become a very common procedure following tooth extraction. This study presents a clinical, histologic, and histomorphometric analysis of postextraction bone changes using nanocrystalline hydroxyapatite (nc-HA) and exposed high-density polytetrafluoroethylene (d-PTFE) membrane. A total of 10 extraction sockets were treated. Clinical measurements were taken after tooth extraction with a customized acrylic stent to ensure the same measurement points. At 6 months, clinical measurements were repeated and bone specimens taken. An overall bone reduction was observed. The histologic and histomorphometric analysis revealed newly formed bone (25.92% ± 18.78%), soft tissue (28.55% ± 9.73%), and residual graft particles (15.43% ± 11.08%). Further studies are necessary to evaluate the efficacy of this technique over the long term.

Overheating during implant site preparation negatively affects the osseointegration process as well the final outcome of implant rehabilitations. Piezoelectric techniques seem to provide to a gentle implant preparation although few scientific reports have investigated the heat generation and its underlying factors. To investigate, through a proper methodological approach, the main factors influencing temperature rise during piezoelectric implant site preparation. Different piezoelectric tips (IM1s, IM2, P2-3, IM3, Mectron Medical Technology, Carasco, Italy) have been tested. The experimental set-up consisted in a mechanical positioning device equipped with a load cell and a fluoroptic thermometer. The first tip of the sequence (IM1s) generated the highest temperature increasing (ΔT). The diamond tips (IM1s and P2-3) determined higher ΔT values than the smooth tips (IM2 and IM3). Further tests with IM1s suggested that the temperature elevation during the first thirty seconds may be predictive of the maximal temperature as well as of the overall thermal impact. Working load, working movements management and bone features resulted to be the main factors influencing temperature rise during piezoelectric implant site preparation. Irrigant temperature and clogging effect may also synergically contribute to the heat generation.