Search

The key requirement in manufacturing flexible organic lightemitting displays (OLEDs) is to protect the deposited electrodes and emitter materials from oxygen and moisture permeation. Multilayered organic/inorganic barrier films can get relatively thick and brittle, and thinner, intrinsically flexible barrier films need to be developed. In this study, we have investigated manufacturing multilayered sol-gel/atomic layer deposition (ALD) structures on poly(ethylene naphthalate) films. The results show improved surface morphology and promising shielding properties against water vapor and oxygen permeation.

Thin (30–40 nm) and highly uniform Al 2 O 3 coatings have been deposited at relatively low temperature of 100 °C onto various polymeric materials employing the atomic layer deposition (ALD) technique, both batch and roll-to-roll (R2R) mode. The applications for ALD have long been limited those feasible for batch processing. The work demonstrates that R2R ALD can deposit thin films with properties that are comparable to the film properties fabricated by in batch. This accelerates considerably the commercialization of many products, such as flexible, printed electronics, organic light-emitting diode lighting, third generation thin film photovoltaic devices, high energy density thin film batteries, smart textiles, organic sensors, organic/recyclable packaging materials, and flexible displays, to name a few.

We present surface modification of thin-film-composite (TFC) polyamide (PA) reverse osmosis (RO) membrane by atomic layer deposition (ALD) process using trimethylaluminium (AlMe 3 ). The aim of the inorganic ALD coating is to improve the anti-fouling performance of TFC PA membranes. The ALD processing parameters were systematically studied because of the lack of previous investigations of the ALD coated RO membranes. Two different processing temperatures (70 °C and 100 °C) and three different ALD cycles (10, 50 and 100) were used to deposit the Al 2 O 3 ALD coatings on TFC PA membranes. The ALD process parameters affected on the hydrophilicity and the surface polarity as well as on the surface roughness of the coated membranes. The bacteria attachment test results indicated that the lowest number of Pseudomonas aeruginosa cells was adhered on the most hydrophilic and polar surface, among the ALD coated membranes. RO tests showed the effect of ALD coating on the water and salt permeability as well as on the salt rejection of the membranes.

Two hybrid coatings synthesized by using alkoxysilanes as precursors in a sol–gel process, differing from each other in terms of the organic components in alkoxysilanes, have been developed to improve the water repellent properties of base paper. The sol–gel-coated base paper samples were characterized by scanning electron microscopy, atomic force microscopy, confocal laser scanning microscopy, X-ray photoelectron spectroscopy, time-of-flight secondary ion mass spectrometry, and contact angle measurements. The sol–gel coatings were found to clearly change the surface properties of base paper. Thin coating layers were formed on base paper surfaces. The topographical data indicated the formation of discontinuous thin films; the time-of-flight secondary ion mass spectrometry analyses confirmed that the coatings were covering the fibres but only partially covered the fibre–fibre intersections. Water and the subsequent heat treatment used as a reference treatment reduced the surface roughness and porosity and slightly changed the surface chemistry of the base paper. The wettability and absorptivity of base paper was clearly reduced by the applied coatings. Copyright © 2011 John Wiley & Sons, Ltd.

The surface morphology and moisture behaviour of pine (Pinus sylvestris) sapwood and heat-treated spruce (Picea abies) deposited with two types of silane-based sol–gel coatings were studied by atomic force microscopy (AFM) and water contact angle measurement. The chemical composition and distribution of sol–gel coatings on wood surfaces were investigated by X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The AFM images revealed that the sol–gel coatings applied by spreading covered the fine structure of the wood substrates. The surface roughness analysis of the AFM topographical images indicated that the sol–gel coatings, especially the one with short aliphatic chain, had a tendency to smooth the wood surface. The XPS results confirmed that the sol–gel coatings had successfully deposited onto pine sapwood and heat-treated spruce changing their surface chemistries. ToF-SIMS images showing Si ion distribution on treated surfaces revealed that the coatings fully covered pine sapwood surfaces. The thin coating layers formed on heat-treated spruce surfaces followed the original wood surface structure. The contact angle measurements indicated that the water repellent properties of both pine and heat-treated spruce were improved to certain extent by the sol–gel coatings.

Corrosion, fouling, and wearing of metal surfaces are the most common problems faced in industry as well as in environmental use. In the recent study, sol–gel based protective coatings were developed and deposited on different copper substrates. Different chemical pretreatments were used to enhance the adhesion and spreadability of coatings on copper surfaces. Substantial improvement of the corrosion resistance of sol–gel coated copper surfaces was obtained by a salt spray test. In addition, the sol–gel coatings increased hydrophobic and easy-to-clean properties of the copper surface. Variation of the curing temperature of the coatings caused changes in the morphology, adhesion, and topography of the sol–gel coatings. On the basis of the important information obtained in this study, the protective properties of sol–gel coatings can be tailored for copper and copper alloy substrates.