Search

Recently, an exciting discovery of orientation-dependent superconductivity was made in two-dimensional electron gas (2DEG) at the interfaces of LaAlO$_3$/KTaO$_3$ (LAO/KTO) or EuO/KTaO$_3$ (EuO/KTO). The superconducting transition temperature can reach a $T_c$ of up to $\sim$ 2.2 K, which is significantly higher than its 3$d$ counterpart LaAlO$_3$/SrTiO$_3$ (LAO/STO) with a $T_c$ of $\sim$ 0.2 K. However, the underlying origin remains to be understood. To uncover the nature of electrons in KTO-based interfaces, we employ x-ray absorption spectroscopy (XAS) and resonant inelastic x-ray spectroscopy (RIXS) to study LAO/KTO and EuO/KTO with different orientations. We reveal the absence of $dd$ orbital excitations in all the measured samples. Our RIXS results are well reproduced by calculations that considered itinerant $5d$ electrons hybridized with O $2p$ electrons. This suggests that there is a lack of localized Ta $5d^1$ electrons in KTO interface superconductors, which is consistent with the absence of magnetic hysteresis observed in magneto-resistance (MR) measurements. These findings offer new insights into our understanding of superconductivity in Ta $5d$ interface superconductors and their potential applications., Comment: 8 pages, 6 figures

A compact spectrometer for medium-resolution resonant and non-resonant X-ray emission spectroscopy in von Hámos geometry is described. The main motivation for the design and construction of the spectrometer is to allow for acquisition of non-resonant X-ray emission spectra while measuring non-resonant X-ray Raman scattering spectra at beamline ID20 of the European Synchrotron Radiation Facility. Technical details are provided and the performance and possible use of the spectrometer are demonstrated by presenting results of several X-ray spectroscopic methods on various compounds., Journal of Synchrotron Radiation, 30, ISSN:0909-0495, ISSN:1600-5775

We investigated the effect of nickel doping on the electronic structure and performance of nanostructured La0.6Sr0.4Co0.2Fe0.8-0.03Ni0.03O3-delta prepared by the one-pot sol gel method. The commercial undoped La0.6Sr0.4Co0.2Fe0.8O3-delta (ISCF0.8) was used as reference. Moreover, for comparison, Ni (3 mol %) was deposited by wetness impregnation over the La0.6Sr0.4Co0.2Fe0.8O3-delta. We show by in situ X-ray absorption spectroscopy at 900 degrees C under air flow that nickel enters the B perovskite site of the material and favors the stabilization of the cobalt oxidation state, as evidenced by the delay in the decrease of the average Co valence with respect to undoped samples. Our results are further supported by in situ X-ray Raman spectroscopy (YRS) that allowed us to monitor the temperature evolution of the 0 Kedge. XRS evidences that nickel-doped LSCF shows unmodified O2p-TM3d density of states, which proves that the Co oxidation state is preserved. Electrochemical impedance spectroscopy measurements were carried out over half-cell systems consisting of LSCF-based materials deposited onto a Ce0.8Gd0.2O2-delta electrolyte. The improvement of the electrochemical performances of the Ni-doped La0.6Sr0.4Co0.2Fe0.8-0.03Ni0.03O3-delta sample with respect to a reference Ni-impregnated LSCF is attributed to the stabilisation of the TM-O-6 structural units, which were recently proposed as the functional units for oxygen reduction.