Advanced composite materials are widely used in civil and military applications due to their superior specific strength and stiffness. However, they are susceptible to damage during impact loading. In order to improve the impact performance, yarn hybridisation and fibre architecture have been investigated in this study in order to evaluate their influence on the damage tolerance (i.e. post- impact flexural strength) of glass composite laminates. Two types of yarn have been used here, namely, pure glass yarns as a bench-mark and hybrid yarns (glass-polypropylene) to manufacture non-crimp and woven (twill and satin) fabric composites. The composite laminates were then subjected to low-velocity impact tests at various impact energies. Afterwards, post- impact flexural strength has been evaluated with a four-point bending test. It has been observed that the non-crimp and woven hybrid composites laminates displayed smaller damage areas compared to the non-crimp glass composites laminates. In addition, although the hybrid laminates have exhibited lower flexural strength properties than the non-crimp glass laminates, the former has shown higher post-impact flexural strength. Fractography analysis has suggested here that the damage failure modes such as intra-yarn cracks have been produced in the hybrid yarns laminates and intra-yarn and inter-yarn cracks have been produced in hybrid fabric laminates. These damage failures have contributed for absorbing impact energy leading to an enhancement of the damage tolerance of the hybrid laminates. [ABSTRACT FROM AUTHOR]

Recently, advanced composite materials have been widely used in numerous applications due to their superior properties. However, their sensitivities to damages during impact loading event limits their usage. In this regards, the influence of yarn hybridisation on the mechanical and thermal performance of composite laminates have been studied using low velocity impact, compression after impact (CAI), flexural and thermal conductivity tests. Two types of composite laminates were manufactured using hybrid yarns (S-glass and polypropylene [PP]) and S-glass yarns through the combination of commingling and core-wrapping methods and converted to non-crimp cross-ply preforms for both laminates. C-scan tests and cross-section microscopy examinations were adopted to identify the damaged areas of impacted laminates and explain the damage failures, which occurred during impact loadings. Results revealed that the hybrid laminates displayed higher damage area reduction compared to glass composites. Although the hybrid composite laminates illustrated considerably lower compressive strength, their residual compressive strength (damage tolerance) was significantly higher than glass composites. Fractography analysis has illustrated that the new damage failure modes such as intra-yarn cracks have been observed in the hybrid yarns laminates. These damage modes have contributed for higher energy absorpsion leading to an enhancement of the damage tolerance of the hybrid laminates. Furthermore, the incorporation of PP fibres resulted in a reduction of thermal conductivity of hybrid laminates compared to pure glass laminates. [ABSTRACT FROM AUTHOR]