Search

The flashover failure and damage of polypropylene (PP) and polyester (PET) films under nanosecond current pulses were experimentally investigated. A nanosecond pulse current test platform was established to study the flashover characteristics, performance degradation, and structural damage of dielectric films under repeated nanosecond current pulses. The accumulation and emission of surface charge influenced by field distortion and trap distribution were analyzed to clarify the mechanism by which the flashover voltage increases linearly with gas pressure at low pressure and saturates at high pressure. The significant effects of pulse energy, gas pressure, and discharge gap on film damage behavior were investigated. The damage pattern of PP and PET films includes surface deformation, reduced flash-voltage tolerance, molecular chain breakage, and group shedding. The damage of PP films is manifested as fine furrows, while PET corresponds to mountainous bumps. With the increasing number of discharges, the breakdown voltage of PP films decreased significantly, while the flash tolerance performance of PET films was more stable. Under the conditions of high pulse current amplitude, small discharge gap, and low air pressure, the damage degree of the film intensifies, which is characterized by severe destruction to the molecular structure and a significant decrease in flashover withstand voltage. Polymer films, flashover, nanosecond current pulses; performance degradation; microstructural damage. [ABSTRACT FROM AUTHOR]

Coaxial peaking capacitor is a key component in high-altitude electromagnetic pulse (EMP) simulators with fast front pulse output. It poses significant technical and engineering challenges in limiting radiation field amplitude and test space. This paper presents the design and testing of a 180 pF, 3 MV coaxial peaking capacitor with improved insulation performance. In the insulation design, the length of the dielectric film is extended to reduce the background electric field on the flashover path. The electric field threshold obtained from image diagnosis is used as a reference. During capacitor testing, the insulation characteristics are diagnosed using both direct and indirect methods. The voltage measured by a D-dot probe, the output waveform of the Marx generator in the primary source, and the radiation field waveform are analyzed to understand the flashover characteristics of the capacitor and to improve the reliability of the test results. The experimental results demonstrate that the peaking capacitor can operate stably at 3.0 MV. If flashover occurring on the dropping edge of the pulse is permitted, the operating voltage can be greater than 3.7 MV without significantly affecting the radiation field waveform. The analysis on the surface flashover morphology of the peaking capacitor reveals that the flashover mainly occurs at the dropping edge of the capacitor's waveform, indicating that the damage to the film is not serious. This research significantly increases the working voltage of coaxial peaking capacitors and contributes to the development of high-altitude EMP simulation technology. [ABSTRACT FROM AUTHOR]

The polymer film dielectric has been widely used in high voltage equipment for bulk insulation owing to the excellent insulation performance. Martin’s empirical formula for bulk breakdown is frequently used to predict the breakdown field strength of multilayer thin film with different electrode areas. In this article, based on the academic consensus that the cumulative breakdown probability of single-layer film obeys the Weibull distribution, the relationship between the cumulative breakdown probability of film dielectric under different electrode areas and the applied electrical field is deduced. Moreover, the relationship between the cumulative breakdown probability of film dielectric with various numbers of film layers and the applied electrical field is obtained and simplified. On these bases, combined with the experimental results of the average breakdown field of film dielectric with smaller electrode areas and fewer layers, a prediction model of the average breakdown field strength of film dielectric with different electrode areas and film layers is established. To obtain the solution of the prediction model concerning the number of film layer, an effective approximate solution method is proposed to solve the calculation problem with ultralarge and ultrasmall data, which significantly reduces the complexity of the solution process. A coaxial film capacitor is developed and tested to verify the prediction model with the “Chenguang” accelerator. The experimental breakdown field strength of 54 layers of 15 $\mu \text{m}$ biaxially oriented polypropylene (BOPP) film with an electrode area of 218.1 cm2 is 355.6 V/ $\mu \text{m}$ , which is comparable to the predicted result of 374 V/ $\mu \text{m}$. The prediction model presented in this article is of certain reference significance for the insulation design of film dielectrics. [ABSTRACT FROM AUTHOR]