Search

The mechanical properties and termite and decay resistance performance of wood-based panel used in wooden houses were evaluated. The physical and mechanical properties, along with the resistance levels, of commonly used wood-based panels, including oriented strand board, structural particleboard, and particleboard for use in interior, were compared. The structural particleboard complied with the physical, mechanical, and formaldehyde emission standards of the International Organization for Standardization and Japanese Industrial Standard, surpassing the requirements for oriented strand board. The structural particleboard exhibited excellent water resistance and a consistent performance. Decay tests classified the particleboard and structural particleboard as "Resistant," with mass losses of 7.82 to 12.72% (white rot) and 14.69 to 16.55% (brown rot). Pine (Pinus densiflora) and oriented strand board exhibited no decay resistance, with mass losses exceeding 45%. The particleboard and structural particleboard demonstrated superior termite resistance, resulting in 100% termite mortality in three days without chemical treatment. The structural particleboard exhibited excellent water, decay, and termite resistance, which can be an advantage in wooden-house construction in terms of maintenance. [ABSTRACT FROM AUTHOR]

Internal finishing materials for large auditoriums or public facilities are regulated in South Korea to ensure their flame-retardant performance. Flame-retardant treatment of low-density fiberboard (LDF), an eco-friendly material, was performed to expand its use as a sound absorber by improving its fire safety. In this study, an LDF with a target density of 0.15 g/cm3 was prepared from radiata pine wood fibers and melamine–urea– formaldehyde resin, and recommended amounts of commercially available flame retardants (liquid type) were applied immediately after hot pressing. A powder-type flame retardant was blended with the resin used in LDF manufacture. The surface color and material changed partially depending on the flame-retardant type. The external application method slightly increased the moisture content and density, but it did not affect the physical properties of the LDF. The flame-retardant treatment reduced the emission of formaldehyde, as a scavenger. After treatment, the char area and char length of the LDFs decreased significantly to 9.42–23.64%, and 6.11–11.91%, respectively. The sound absorption performance of the flame-retardant-treated LDFs improved 4.08–9.11%, while their thermal-insulation performance remained unaffected. The flame-retardant-treated LDFs satisfy the regulation of flame retardancy, while maintaining sound absorption and thermal insulation functions. [ABSTRACT FROM AUTHOR]

As the demand increases for low energy green buildings, such as passive housing, the development of new insulation systems based on natural materials is underway. In this study, 20-mm-thick wood fiber insulation board (WIB) samples of different densities were prepared using melamineformaldehyde-urea (MFU) resin adhesives. The resin contents were fixed at 35% and the target densities were 0.10 g/cm³, 0.15 g/cm3, 0.20 g/cm³, and 0.25 g/cm³. The thermal conductivities of the WIBs gradually increased as the density increased. The formaldehyde (HCHO) emissions of all the WIBs indicated that they were of "Super E0" (SE0) grade, but the quantity of the HCHO emissions slightly increased as the density increased. The thickness swelling of all the WIBs was stable at less than 3%, and the bending strength linearly increased as the WIB density increased. A notable decrease in the water absorption rate was observed between the lower and higher density WIB samples. Based on the results of the cone calorimeter tests, the carbonization depth ratio and the weight loss rate remarkably decreased as the density increased. Therefore, the optimum WIB density was in the range of 0.15 g/cm³ to 0.20 g/cm³ to provide adequate insulation performance as well as human and structural safety. [ABSTRACT FROM AUTHOR]

Wood-fiber insulation boards can be utilized as a core construction material. They provide a comfortable and safe residential space and reduce energy consumption because of the ecofriendly nature and high heat insulation. In this study, wood-fiber insulation boards were prepared with different types of adhesive (melamine-urea-formaldehyde (MUF), phenol-formaldehyde (PF), emulsifiable 4,4' methylene diisocyanate (eMDI), and latex resins), and the physical and heat insulation properties, toxic chemical emissions, and combustion characteristics were analyzed. The different adhesive types had no major effects on the insulation. With regard to the toxic emissions, all wood-fiber insulation boards showed the best rating possible except for the PF resin. In the cone-calorimeter test, the wood-fiber insulation board prepared with MUF showed a lower total heat release, mean heat release rate, smoke release, and CO and CO2 yields than the other samples because of the early formation of the carbonized layer. Based on the comprehensive evaluation, the MUF adhesive is the best choice for wood-fiber insulation boards. [ABSTRACT FROM AUTHOR]

The demand for noise control in residential environments is steadily increasing, but the currently available noise-reducing materials used in walls and floors are unsustainable and expensive. As an alternative, woodfiber could be a good resource to manufacture eco-friendly acoustic materials. In this study, fiberboards were prepared by mixing wood-fibers (Pinus densiflora) with melamine-urea-formaldehyde resin adhesive, obtaining specimens with different final densities and resin contents. The acoustic, physical, and morphological properties of the fiberboards were investigated. The sound absorption was greatly influenced by the density of the fiberboard: lower densities showed higher sound absorption performances. Furthermore, the low-frequency absorption coefficient was higher for lower resin contents. The materials met all the criteria required by the Korean standards for fiberboards. As the density increased, the dimensional stability and the bending strength increased; in contrast, the physical properties were not affected by the resin content. Microscopy observations confirmed that specimens with different densities and resin contents had different porosities; the porosity was assumed to be the main property that governs the noise-reducing ability. Due to their ecofriendliness and inexpensiveness, these fiberboards offer themselves as efficient and effective alternative sound-absorbing materials. [ABSTRACT FROM AUTHOR]

As petrochemical products (including plastics) contribute to the destruction of the natural environment, the use of such products must be reduced. Plastics account for 90% of the insulation materials used in Korea, including extruded polystyrene (EPS), expanded polystyrene (XPS), and urethane foam. Wood-fiber insulation board (WIB) is a promising natural alternative to petrochemical insulation. This study aimed to determine the optimal amount of adhesive resin required for manufacturing WIB. Fireresistant WIB was prepared with a melamine-urea-formaldehyde (MUF) resin (ranging from 20% to 35%), and the physicochemical and fireresistant properties were determined. Higher resin content led to improved physical properties, while the thermal conductivity was unaffected. With the exception of 35% resin content in the WIB, the formaldehyde emissions of the WIB samples complied with the Korean Industrial Standards requirements for Super E0 grade (less than 0.3 mg per L). The physicochemical properties of the WIB samples were sufficient for use as an insulating material, even at 20% resin content. A perpendicular flame test revealed that all samples formed a carbonized layer to prevent flame penetration, except for the specimen with 20% of the resin content. The cone calorimeter testing indicated that the MUF adhesives acted as an effective fire retardant at resin contents above 25%. [ABSTRACT FROM AUTHOR]