Search

Abstract: Structure and property of a nanocomposite consisting of modified carbon nanofibers (MCNFs), homogenously dispersed in an elastomeric ethylene/propylene (EP) random copolymer (84.3wt% P) matrix, were studied by in situ synchrotron X-ray diffraction during uniaxial deformation. The MCNF acted as a nucleating agent for crystallization of the α-form of isotactic polypropylene (iPP) in the matrix. During deformation at room temperature, strain-induced crystallization took place, while the transformation from the γ phase to α phase also occurred for both unfilled and 10wt% MCNF-filled samples. The tensile strength of the filled material was consistently higher than that of pure copolymer. However, when compared with pure copolymer, the highly stretched nanocomposite exhibited a higher amount of unoriented crystals, a lower degree of crystal orientation and a higher amount of γ crystals. This behavior indicated that polymer crystals in the filled nanocomposite experienced a reduced load, suggesting an effective load transfer from the matrix to MCNFs. At elevated temperatures, the presence of MCNFs resulted in a thermally stable physically cross-linked network, which facilitated strain-induced crystallization and led to a remarkable improvement in the mechanical properties. For example, the toughness of the 10wt% nanocomposite was found to increase by a factor of 150 times at 55°C. [Copyright &y& Elsevier]

Abstract: The tensile and dynamic mechanical properties of a nanocomposite, containing modified carbon nanofibers (MCNFs) homogenously dispersed in an elastomeric ethylene/propylene (EP) copolymer semicrystalline matrix (84.3wt% P), have been correlated with the structure development. These properties were characterized by in situ synchrotron X-ray diffraction during stretching, dynamic mechanical analysis and X-ray analysis techniques over a wide temperature range. Upon sequential drawing, the tensile strength of the nanocomposite film was notably higher than that of the unfilled polymer even though both samples exhibited a similar amount of crystal fraction and the same degree of crystal orientation, revealing the effect of nanofiller reinforcement in the semicrystalline matrix. The mechanical spectra of the 10wt% MCNF filled samples in both stretched and non-stretched states showed broadening of the elastic modulus at high temperatures, where the corresponding crystallinity index also decreased. It is conceivable that a significant fraction of chain orientation is induced in the vicinity of the nanofillers during stretching, and these stretched chains with reduced mobility significantly enhance the thermal mechanical properties. [Copyright &y& Elsevier]

An in situ study of structural formation of amorphous poly(ethylene terephthalate) (PET) during uniaxial deformation above its Tg (at 90 °C) was carried out by wide-angle X-ray diffraction (WAXD) with synchrotron radiations. Results indicate that the relationships between structure and mechanical property can be divided into three zones: I, II and III. In Zone I, oriented mesophase is induced by strain, where the applied load remains about constant but the amount of mesophase increases with strain. In Zone II, crystallization is initiated from the mesophase through nucleation and growth, where the load starts to increase marking the beginning of the strain-hardening region. The initial crystallites are defective but they form an effective three-dimensional network to enhance the mechanical property. The perfection of the crystal structure and the orientation of the crystals all increase with strain in this zone. In Zone III, the ratio between load and strain is about constant, while the stable crystal growth process takes place until the breaking of the sample. The sample damage is probably dominated by the chain pull-out mechanism from the crystal amorphous interface. The increase in molecular weight was found to enhance the overall mechanical properties such as the load to induce the mesophase and the ultimate tensile strength before breakage. [Copyright &y& Elsevier]