Search

Dy3+-doped CaF2-SrF2 crystals with various Dy3+ dopant concentrations were synthesized by multicrucible temperature gradient technology (MC-TGT). Dy:CaF2-SrF2 crystals were fluorite structured and crystallized in cubic F m 3 ¯ m space group, as characterized by X-ray diffraction. The crystallographic site concentration was calculated from the measured density by Archimedes' hydrostatic weighing principle. The optical transmission reached over 90% with a sample thickness of 1.0 mm. The Sellmeier dispersion formula was obtained following the measured refractive index in a mid-IR range of 1.7–11 μm. Absorption coefficients of 6.06 cm−1 and 12.71 cm−1 were obtained at 804 nm and 1094 nm in 15% Dy:CaF2-SrF2 crystal. The fluorescence spectra of 15 at.% Dy:CaF2-SrF2 showed the strongest wavelength peak at 2919 nm with a full width at half maximum (FWHM) of 267 nm under an excitation wavelength of 808 nm. The fluorescence lifetimes were illustrated for different Dy3+ dopant levels of 5%, 10% and 15%. The results indicate that the Dy:CaF2-SrF2 crystal is a promising candidate for compact mid-IR lasers. [ABSTRACT FROM AUTHOR]

Tm3+-doped calcium niobium gallium garnet (Tm:CNGG) single crystals have been successfully grown by the micro-pulling-down (μ-PD) method. The crystal structure, absorption spectra, fluorescence spectra and lifetimes of Tm:CNGG crystals were investigated. The absorption and emission bandwidths of Tm:CNGG crystals are larger than those of other Tm3+ doped garnet crystals, which will be beneficial for laser diode (LD) pumping and ultrashort pulse generation. Additionally, continuous wave (CW) laser operation around 2 μm was achieved in the 2.0 at.% Tm:CNGG crystal by LD pumping. [ABSTRACT FROM AUTHOR]

A series of 0.5 at.% Tm:Ca 1-x Y x F 2+x (x = 0, 0.01, 0.04, 0.06, 0.08, 0.12) crystals have been successfully grown by the temperature gradient technique (TGT) method. The absorption spectra, fluorescence spectra, and fluorescence decay curves were measured and analyzed at room temperature. By comparison, it is found that when the concentration of Y3+ ions reaches 8 at.%, the absorption cross section corresponding to the 3H 6 →3H 4 energy level is 2.56 × 10−21 cm2 at 793 nm, which is suitable for GaAlAs LD pumping. The J-O strength parameters Ω 2 , Ω 4 , and Ω 6 were obtained. With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. When the concentration of Y3+ ions reaches 8 at.%, the emission cross sections are 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, and the full widths at half maximum (FWHM) are 76 nm and 195 nm, respectively. The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. • With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. • When the concentration of Y3+ ions reaches 8 at.%, the emission cross section is 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, respectively. • The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. [ABSTRACT FROM AUTHOR]

• A series of 0.6 at% Pr:CaF 2 -RF 3 (R= Y3+, Gd3+, Lu3+) crystals were successfully grown by the temperature gradient technique(TGT) method. • By co-doping R3+ ion (R=Y3+, Gd3+, Lu3+), the spectral performance of the crystals could be significantly improved and the function effect is also different. • The spectral performance and spectral quality factor of the crystals were systematically described and compared for the first time. • The spectral modulation effect caused by Y3+, Gd3+ and Lu3+ co-doping ion was discussed. A series of 0.6 at% Pr:CaF 2 -RF 3 (R = Y3+, Gd3+, Lu3+) crystals have been successfully grown by the temperature gradient technique(TGT). The absorption spectra, fluorescence spectra, and fluorescence decay curves were measured and analyzed at room temperature. When the R3+ concentration is higher than a certain value, the diffraction peaks of Pr:CaF 2 -RF 3 crystals were well indexed to the (Ca,Y)F 2 phase. By co-doping R3+ ion (R=Y3+, Gd3+, Lu3+), the spectral performance of the crystals could be significantly improved and the function effect is also different. For 0.6 at% Pr, 28.5 at% Y:CaF 2 crystal, the fluorescence lifetime of 3P 0 energy level was fitted to be 45.46 µs, and the emission cross sections of 3P 0 →3H 6 (605 nm), and 3P 0 →3F 2 (641 nm) were calculated to be 1.78 × 10−20 cm2, and 4.61 × 10−20 cm2 with the full width at half (FWHM) of 20.1 nm and 6.8 nm, respectively. The 0.6 at% Pr, 28.5 at% Y:CaF 2 crystal could be favorble laser medium for ultra-fast laser opreration at 605 nm and 641 nm. For 0.6 at% Pr, 18 at% Gd:CaF 2 and 0.6 at% Pr, 10 at% Lu:CaF 2 crystals, the spectral quality factors σ em• τ f of 3P 0 →3F 2 transition (642 nm) were calculated to be 614.18 × 10−20 cm2•µs and 506.36 × 10−20 cm2•µs with the FWHM of 3.7 nm and 5.3 nm. All the results show that 0.6 at% Pr, 18 at% Gd:CaF 2 and 0.6 at% Pr, 10 at% Lu:CaF 2 crystals are promising gain media for high-efficiency visible laser output at 642 nm, which would compete with commercial Pr: YLF crystal in the future. [ABSTRACT FROM AUTHOR]

Tm3+-doped bismuth germanate crystals (Tm:BGO) with various doping concentrations of 0.5, 0.75, 1.0, 1.5, and 2.0 at.% were grown by the micro-pulling-down method (μ-PD). The effect of thulium concentration on the growth, structure, absorption spectra, emission spectra and fluorescence lifetime of 3H 4 and 3F 4 state was studied. Under excitation of 792 nm, Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. The fluorescence lifetime of 3H 4 state decreased strongly as the thulium concentration increased, while the lifetime of 3F 4 state was relatively constant for all thulium concentrations. • Tm:BGO crystals with different Tm3+ concentration were grown by the micro-pulling-down method. • The effect of Tm3+ concentration on the growth, structure and spectroscopic properties of Tm:BGO crystals was studied. • Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. [ABSTRACT FROM AUTHOR]

Nd:SrAl 11 O 19 (Nd:SRA) crystal has been grown by the Czochralski method. Polarized absorption spectra, polarized fluorescence spectra and fluorescence lifetime were investigated. For σ-polarization, the peak absorption cross section at 798 nm is 2.08 × 10−20 cm2 with full width at half maximum (FWHM) of 10.2 nm and the peak emission cross section is 3.36 × 10−20 cm2 at 1048.5 nm with FWHM of 4.80 nm. The Judd-Ofelt parameters Ω 2,4,6 were obtained to be 0.51 × 10−20 cm2, 2.08 × 10−20 cm2, and 2.12 × 10−20 cm2, respectively. Continuous-wave laser operation of the a-cut and c-cut Nd:SRA sample has been demonstrated. The maximum output power of 8.33 W was achieved from c-cut sample at an absorbed power of 27.73 W, corresponding to a slope efficiency of 31.3%. • Nd:SrAl 12 O 19 crystal has been gown by the Czochralski method. • Spectral parameters of Nd:SrAl 12 O 19 crystal were obtained. • Continuous-wave laser was demonstrated from Nd:SrAl 12 O 19 crystal. [ABSTRACT FROM AUTHOR]

Yb,Pr:CaF 2 crystals have been grown successfully by the temperature gradient technique(TGT). The absorption spectra, fluorescence spectra, fluorescence decay lifetime of Pr3+ ions in CaF 2 crystal sensitized by different Yb3+ ions concentration have been measured. The effective J-O intensity parameters were fitted to be Ω 2 =0.36 × 10−20cm2, Ω 4 =2.89 × 10−20cm2, Ω 6 =6.69 × 10−20cm2 for 0.3 at.%Pr,1.5 at.%Yb:CaF 2. And the emission cross sections of 3P 1 →3H 5 (535 nm), and 3P 0 →3F 4 (750 nm) are calculated to be 2.02 × 10−20cm2, and 2.50 × 10−20cm2 with the FWHM of 17.2 nm, and 10.5 nm, respectively. The fluorescence lifetime of 3P 0 has achieved great increasing by sensitizing of Yb3+ ion. Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed. The results show that Yb,Pr:CaF 2 could be a potential laser gain medium for visible and near-IR laser operation. • Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed by Yb3+ ion sensitizing. • Spectral properties and Judd-Ofelt parameters of Yb,Pr:CaF 2 crystal were investigated and analysed. [ABSTRACT FROM AUTHOR]

GdScO 3 single crystal codoped with Tm3+ and Tb3+ ions was successfully grown by the Edge-defined Film-fed Growth Method (EFG) for the first time. Absorption, fluorescence spectrum and fluorescence lifetimes of the grown crystal at room temperature were measured. The absorption cross-section at 789 nm was calculated to be 8.20 × 10−21 cm2. The emission cross-section was 1.35 × 10−21 cm2 at 1504 nm with the FWHM of 95.3 nm. The fluorescence lifetimes of the 3H 4 state and the 3F 4 state were fitted to be 253 μs and 1460 μs, respectively. Compared with Tm3+ single doped GdScO 3 crystal, the codoping of Tb3+ successfully depopulated the 3F 4 energy level and enhanced the emission at 1.5 μm region. It indicated that Tm,Tb:GdScO 3 could be favorable laser medium for 1.5 μm-laser operation. • Tm3+ and Tb3+ co-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed method (EFG) for the first time. • Spectral parameters and Judd-Ofelt parameters of Tm,Tb:GdScO3 crystal were obtained and compared. • The fluorescence mechanism of Tm3+ and Tb3+ co-doped GdScO 3 crystal has been studied. [ABSTRACT FROM AUTHOR]

High quality 7 at%Er:Y 2 O 3 crystal was successfully grown by Fz method. Judd-Ofelt theory was applied to analyze spectroscopic properties at 2.7 μm. The larger value of Ω 2 shows low local environment symmetry exists in Er:Y 2 O 3 crystal, and the large Ω 4 /Ω 6 indicates better spectral quality. The larger absorption cross-section and FWHM are beneficial to efficient absorption of pump source. The fluorescence spectra and lifetimes of Er:Y 2 O 3 crystal were measured and studied at 2.7 μm. The emission cross-sections at 2723 nm was calculated to be 1.41 × 10−20cm2. Compared with other Er3+ doped crystals, the large spectral quality factors Q and low fluorescence lifetime ratio illustrate that Er:Y 2 O 3 crystal has excellent laser properties at 2.7 μm. In addition, the low inversion ratio also indicates great potential of Er:Y 2 O 3 crystal for laser generation at 2.7 μm. • A high quality 7%Er:Y 2 O 3 laser crystal was successfully grown by Fz method. • Judd-ofelt (J-O) parameterization scheme was applied to analyze the spectroscopic properties of 7%Er:Y 2 O 3 laser crystal at 2.7 μm. • The large spectral quality factors Q with low fluorescence lifetime ratio illustrates that Er:Y 2 O 3 crystal has excellent laser properties at 2.7 µm. • The low inversion ratio indicates great potential of Er:Y 2 O 3 crystal for laser generation at 2.7 μm. [ABSTRACT FROM AUTHOR]