Search

Perovskite quantum dots (PeQDs) are seen as the credible alternative to traditional QDs ascolor converter in liquid crystal display (LCD). Unfortunately, PeQDs sufferfrom instability and color separation, and the prepared PeQDs enhanced films(PQDFs) need the protection of expensive barrier layers, which significantly increases price and limits their application. Herein, large‐area yellow monolithic PQDF is fabricated with both green CsPbBr3 and red CsPbBr1I2QDs encapsulated in the dual matrices of inorganic glass and polypropylene (PP) via an industrialized melt extruding & rolling method. The PQDF shows high photoluminescence quantum yield (PLQY) of 92% and narrow full width at half maximum (FWHM) of 19 nm (green) and 33 nm (red). Importantly, the bare PQDF without barrier layers can pass harsh aging test at 85 °C/85% RH and reach anoperating T90 lifetime over 1000 h. Finally, a white backlit unit is designed by coupling yellow monolithic PQDF with blue light guide panel, and the constructed prototype display shows superior color rendering performance forits narrow green/red emissions, reaching a color gamut of 110% National Television System Committee (NTSC). This work provides a novel and easy‐to‐industrialize route to prepare PQDFs to realize their commercial application in backlit display. [ABSTRACT FROM AUTHOR]

Robust amorphous glass protected CsPbBr3 (CsPbBr3@glass) perovskite quantum dots (PeQDs) with ultra‐pure green emission and superior long‐term stability are highly desirable for developing wide‐color‐gamut liquid crystal displays. However, most of the reported CsPbBr3@glass nanocomposites are subject to low external quantum efficiency (EQE). This work demonstrates that ZrO2 additive has an "accumulation" effect on the borosilicate glass network structure to promote in situ nucleation/growth of PeQDs inside glass rather than self‐crystallization. This effect is beneficial in reducing surface defects, improving the quality of PeQDs, and thus boosting radiative recombination of excitons. As a consequence, the as‐prepared CsPbBr3@glass shows a record EQE of up to 75% and can pass the accelerated aging tests at 85 °C/85% RH for 1000 h and blue light irradiation over 2000 h. Finally, a prototype display using CsPbBr3@glass‐based straight‐down backlit unit is designed and gains more favorable responses in blind selection tests for its high brightness of 2647 cd m−2 and high color purity of 88%. The findings will pave the way for realizing the commercial application of CsPbBr3@glass nanocomposite in PeQDs‐converted backlit display. [ABSTRACT FROM AUTHOR]

Perovskite quantum dots are considered an ideal alternative to traditional phosphor color converters because of their excellent optical properties. However, the bottleneck problem of instability has tremendously limited their practical applications. In the present work, we fabricate green-emitting CsPbBr 3 @glass and red-emitting CsPbBr 1.5 I 1.5 @glass nanocomposites via an in-situ nucleation/growth method. Importantly, the CsPbX 3 @glass (X 3 = Br 3 , Br 1.5 I 1.5) samples exhibit striking thermal reversibility in the heating/cooling cycle experiments. Furthermore, CsPbX 3 monolithic films with high photoluminescence quantum yields (PLQYs) of 80–95% and narrow full-width at half-maximum (FWHM) down to 16 nm are achieved by dispersing ground CsPbX 3 @glass particles in polydimethylsiloxane (PDMS) matrix. Benefiting from dual encapsulation of inorganic glass matrix and organic polymer matrix, the film can endure harsh accelerated aging tests (at 85 °C/85%RH for 500 h). Finally, combining the as-prepared yellow monolithic film with blue chips as the backlight endows the liquid crystal display (LCD) with a wide color gamut (a color gamut of 146% of commercial LCD, 101% of NTSC after passing the color filters), demonstrating great prospects in the display industry. • CsPbX 3 (X 3 = Br 3 , Br 1.5 I 1.5) QDs were in-situ precipitated inside glass matrix via controlling nucleation/growth process. • CsPbX 3 monolithic films exhibited high PLQY of 80–95% and FWHM down to 16 nm. • The CsPbX 3 @glass@PDMS composite films possessed extremely excellent moisture and heat resistance. • A white LED backlit unit was simply achieved by coupling a yellow composite film with blue chips. • The color gamut of screen reached 101% NTSC 1953 standard and 146% commercial LCD after passing the color filters. [ABSTRACT FROM AUTHOR]