Search

In order to solve the phase separation problem of Na2S2O3·5H2O–CH3COONa·3H2O PCM (phase change material), sodium carboxymethyl cellulose (CMC), hydroxyethyl cellulose (HEC), xanthan gum (XG), sodium polyacrylate (PAAS) and polyacrylamide (PAM) were selected as additives. The effects of different proportions of the above thickeners on the supercooling degree, phase separation, phase change temperature and latent heat of Na2S2O3·5H2O–CH3COONa·3H2O system were studied by using the cooling curve and DSC, so as to screen the best thickener for eutectic PCM. The experimental results show that CMC, XG and PAAS can eliminate the phase separation of Na2S2O3·5H2O–CH3COONa·3H2O. Among them, the optimal ratio of CMC, XG and PAAS is 3 mass%, 3 mass% and 1 mass%, respectively. From the perspective of heat storage performance, PAAS is the optimal thickener for Na2S2O3·5H2O–CH3COONa·3H2O. The phase change temperature is 40.5 °C. The subcooling degree is about 14.7 °C, and the latent heat is about 221 J g−1. The melting time is 15 min. Only PAAS can make Na2S2O3·5H2O–CH3COONa·3H2O eutectic PCM completely exothermic at room temperature, which can not only play the role of thickener to eliminate phase separation, but also is a nucleating agent. After 100 melting-solidification cycles, the change rate of latent heat value was only 5%, and the change rate of phase transition temperature was less than 1%. Considering heat storage performance and cyclic stability, PAAS is the optimal thickener for Na2S2O3·5H2O–CH3COONa·3H2O PCM. [ABSTRACT FROM AUTHOR]

Calcium ions can react with polyethylene glycol (PEG) to form a form-stable phase change material, but the low thermal conductivity hinders its practical application. In this paper, hydroxylated multi-walled carbon nanotubes (MWCNTs) with different mass are introduced into PEG1500·CaCl2 form-stable phase change material to prepare a new type of energy storage material. Carbon nanotubes increased the mean free path (MFP) of phonons and effectively reduced the interfacial thermal resistance between pure PEG and PEG1500·CaCl2 3D skeleton structure. Thermal conductivity was significant improved after increasing MWCNTs mass, while the latent heat decreases. At 1.5 wt%, composite material shows the highest phase change temperature of 42 °C, and its thermal conductivity is 291.30% higher than pure PEG1500·CaCl2. This article can provide some suggestions for the preparation and application of high thermal conductivity form-stable phase change materials. [ABSTRACT FROM AUTHOR]

In order to alleviate the contradiction between the growing energy demand and the limited fossil energy, intensifying research and development of application technologies that utilize renewable energy is necessary. Energy storage technology using PCMs is a frontier research field with great application prospect. As a kind of phase change energy storage materials, organic PCMs (OPCMs) have been widely used in solar energy, building energy conservation and other fields with the advantages of appropriate phase change temperature and large latent heat of phase change. However, low thermal conductivity and liquid leakage problem restrict the further application of OPCMs. Compounding organic materials with other materials can effectively improve this situation. This paper focuses on the compound types of organic PCMs and the principles of various composite technologies. And the development direction of organic composite PCMs in the future and the improvement of composite technology are discussed in the end of the paper. • The types of various organic composite PCMs are reviewed. • The principle of compound ratio between organic phase change materials is reviewed. • The technology and principle of preparing organic shape setting materials by porous materials are reviewed. • The principle of microencapsulation technology in the modification of organic phase change materials is reviewed. • Suggestions for wider application of organic composite PCMs are listed. [ABSTRACT FROM AUTHOR]