Search

A highly efficient Cu2ZnSn(S,Se)4 (CZTSSe)-based thin-film solar cell (9.9 %) was prepared using an electrochemical deposition method followed by thermal annealing. The Cu-Zn-Sn alloy films was grown on a Mo-coated glass substrate using a one-pot electrochemical deposition process, and the metallic precursor films was annealed under a mixed atmosphere of S and Se to form CZTSSe thin films with bandgap energies ranging from 1.0 to 1.2 eV. The compositional modification of the S/(S+Se) ratio shows a trade-off effect between the photocurrent and photovoltage, resulting in an optimum bandgap of roughly 1.14 eV. In addition, the increased S content near the p-n junction reduces the dark current and interface recombination, resulting in a further enhancement of the open-circuit voltage. As a result of the compositional and interfacial modification, the best CZTSSe-based thin-film solar cell exhibits a conversion efficiency of 9.9 %, which is among the highest efficiencies reported so far for electrochemically deposited CZTSSe-based thin-film solar cells. [ABSTRACT FROM AUTHOR]

Highly efficient copper-zinc-tin-selenide (Cu2ZnSnSe4; CZTSe) thin-film solar cells are prepared via the electrodepostion technique. A metallic alloy precursor (CZT) film with a Cu-poor, Zn-rich composition is directly deposited from a single aqueous bath under a constant current, and the precursor film is converted to CZTSe by annealing under a Se atmosphere at temperatures ranging from 400 °C to 600 °C. The crystallization of CZTSe starts at 400 °C and is completed at 500 °C, while crystal growth continues at higher temperatures. Owing to compromises between enhanced crystallinity and poor physical properties, CZTSe thin films annealed at 550 °C exhibit the best and most-stable device performances, reaching up to 8.0 % active efficiency; among the highest efficiencies for CZTSe thin-film solar cells prepared by electrodeposition. Further analysis of the electronic properties and a comparison with another state-of-the-art device prepared from a hydrazine-based solution, suggests that the conversion efficiency can be further improved by optimizing parameters such as film thickness, antireflection coating, MoSe2 formation, and p-n junction properties. [ABSTRACT FROM AUTHOR]

A highly efficient Cu2 ZnSn(S,Se)4 (CZTSSe)-based thin-film solar cell (9.9%) was prepared using an electrochemical deposition method followed by thermal annealing. The Cu-Zn-Sn alloy films was grown on a Mo-coated glass substrate using a one-pot electrochemical deposition process, and the metallic precursor films was annealed under a mixed atmosphere of S and Se to form CZTSSe thin films with bandgap energies ranging from 1.0 to 1.2 eV. The compositional modification of the S/(S+Se) ratio shows a trade-off effect between the photocurrent and photovoltage, resulting in an optimum bandgap of roughly 1.14 eV. In addition, the increased S content near the p-n junction reduces the dark current and interface recombination, resulting in a further enhancement of the open-circuit voltage. As a result of the compositional and interfacial modification, the best CZTSSe-based thin-film solar cell exhibits a conversion efficiency of 9.9%, which is among the highest efficiencies reported so far for electrochemically deposited CZTSSe-based thin-film solar cells., (© 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.)