Search

Metal additive manufacturing technologies, such as electron beam powder bed fusion (PBF-EB), rely on layer heating to overcome the so-called "smoke" phenomenon. When scaled up for industrial manufacturing, PBF-EB becomes less productive due to the lengthy preheating process. Currently, only the electron beam (EB) is used for preheating in PBF-EB, resulting in increased manufacturing times, energy consumption, and in some cases limiting the applicability of the technology. In this study, a new preheating approach is suggested that incorporates a near-infrared radiation (NIR) emitter inside an PBF-EB system. The NIR unit eliminates the need for EB heating, reducing build time and powder charging. Successful builds using 316 L and Ti6Al4V precursor powders validate the feasibility of the proposed approach. The produced samples exhibit similar properties to those obtained by the standard PBF-EB process. The introduction of NIR technology also reduced build cost and increased the service intervals of the electron gun. [ABSTRACT FROM AUTHOR]

Purpose: This study aimed to evaluate how as-built electron beam melting (EBM) surface properties affect the onset of blood coagulation. The properties of EBM-manufactured implant surfaces for placement have, until now, remained largely unexplored in literature. Implants with conventional designs and custom-made implants have been manufactured using EBM technology and later placed into the human body. Many of the conventional implants used today, such as dental implants, display modified surfaces to optimize bone ingrowth, whereas custom-made implants, by and large, have machined surfaces. However, titanium in itself demonstrates good material properties for the purpose of bone ingrowth. Materials and Methods: Specimens manufactured using EBM were selected according to their surface roughness and process parameters. EBM-produced specimens, conventional machined titanium surfaces, as well as PVC surfaces for control were evaluated using the slide chamber model. Results: A significant increase in activation was found, in all factors evaluated, between the machined samples and EBM-manufactured samples. The results show that EBM-manufactured implants with as-built surfaces augment the thrombogenic properties. Conclusion: EBM that uses Ti6Al4V powder appears to be a good manufacturing solution for load-bearing implants with bone anchorage. The as-built surfaces can be used “as is” for direct bone contact, although any surface treatment available for conventional implants can be performed on EBM-manufactured implants with a conventional design. [ABSTRACT FROM AUTHOR]

Metal additive manufacturing (AM) is on its way to industrialization. One of the most promising techniques within this field, electron beam melting (EBM), is nowadays used mostly for the fabrication of high‐performance Ti‐based alloy components for the aerospace and medical industry. Among the industrial applications envisioned for the future of EBM, the fabrication of high carbon steels for the tooling industry is of great interest. In this context, the process windows for dense and crack‐free specimens for a highly alloyed (Cr–Mo–V) cold‐work steel powder are presented in this article. High‐solidification rates during EBM processing lead to very fine and homogeneous microstructures. The influence of process parameters on the resulting microstructure and the chemical composition is investigated. In addition, preliminary results show very promising mechanical properties regarding the as‐built and heat‐treated microstructure of the obtained material. [ABSTRACT FROM AUTHOR]

Purpose – The purpose of this paper is to study the use of the additive manufacturing (AM) method, electron beam melting (EBM), for manufacturing of customized hip stems. The aim is to investigate EBM's feasibility and commercial potential in comparison with conventional machining, and to map out advantages and drawbacks of using EBM in this application. One part of the study concerns the influence on the fatigue properties of the material, when using the raw surface directly from the EBM machine, in parts of the implant. Design/methodology/approach – The research is based on a case study of manufacturing a batch of seven individually adapted hip stems. The stems were manufactured both with conventional machining and with EBM technology and the methods were compared according to the costs of materials, time for file preparation and manufacturing. In order to enhance bone ingrowths in the medial part of the stem, the raw surface from EBM manufacturing is used in that area and initial fatigue studies were performed, to get indications on how this surface influences the fatigue properties. Findings – The cost reduction due to using EBM in this study was 35 per cent. Fatigue tests comparing milled test bars with raw surfaced bars indicate a reduction of the fatigue limit by using the coarse surface. Originality/value – The paper presents a detailed comparison of EBM and conventional machining, not seen in earlier research. The fatigue tests of raw EBM-surfaces are interesting since the raw surface has shown to enhance bone ingrowths and therefore is suitable to use in some medical applications. [ABSTRACT FROM AUTHOR]

In this work, a highly alloyed cold work tool steel, Uddeholm Vanadis 4 Extra, was manufactured via the electron beam melting (EBM) technique. The corresponding material microstructure and carbide precipitation behavior as well as the microstructural changes after heat treatment were characterized, and key mechanical properties were investigated. In the as-built condition, the microstructure consists of a discontinuous network of very fine primary Mo- and V-rich carbides dispersed in an auto-tempered martensite matrix together with ≈15% of retained austenite. Adjusted heat treatment procedures allowed optimizing the microstructure by the elimination of Mo-rich carbides and the precipitation of fine and different sized V-rich carbides, along with a decrease in the retained austenite content below 2%. Hardness response, compressive strength, and abrasive wear properties of the EBM-manufactured material are similar or superior to its as-HIP forged counterparts manufactured using traditional powder metallurgy route. In the material as built by EBM, an impact toughness of 16–17 J was achieved. Hot isostatic pressing (HIP) was applied in order to further increase ductility and to investigate its impact upon the microstructure and properties of the material. After HIPing with optimized protocols, the ductility increased over 20 J. [ABSTRACT FROM AUTHOR]

Electron beam melting (EBM) is currently hampered by the low number of materials available for processing. This work presents an experimental study of process parameter development related to EBM processing of stainless steel alloy 316LN. Area energy (AE) input and beam deflection rate were varied to produce a wide array of samples in order to determine which combination of process parameters produced dense (>99%) material. Both microstructure and tensile properties were studied. The aim was to determine a process window which results in dense material. The range of AE which produced dense materials was found to be wider for 316LN than for many other reported materials, especially at lower beam deflection rates. Tensile and microstructural analysis showed that increasing the beam deflection rate, and consequently lowering the AE, resulted in material with a smaller grain size, lower ductility, lower yield strength, and a narrower window for producing material that is neither porous nor swelling. [ABSTRACT FROM AUTHOR]

This is a study of the micro- and macrostructural variations in samples of stainless steel with the overall composition of the grade 316L, produced using electron beam melting. Electron beam melting is one of the processing methods under consideration for manufacturing some of the International Thermo- Nuclear Experimental Reactor In-Vessel components. Therefore further studies of the homogeneity of the material were conducted. Electron beam melting results in a complicated thermal history of the manufactured part giving a significant impact on the microstructure. A cellular structure that is often observed in samples prepared by selective laser melting was found in the top layers of the specimens. Further down, the structure changed until the cellular structure was almost non-existing, and the grain boundaries had become more pronounced. This revelation of a heterogeneous structure throughout the entire part is crucial for large-scale industrial applications like the Thermo- Nuclear Experimental Reactor to make sure that it is understood that the properties of the material might not be the same at every point, as well as to assure that the correct post-treatment is done. It is also exposed that a significant part of this change is due to molybdenum redistribution inside the sample when it diffuses from the cell boundaries into the cells, and into bigger agglomerates in the grain boundaries. This diffusion seems not to affect the microhardness of the samples. [ABSTRACT FROM AUTHOR]

Mechanical behavior of additively manufactured lattice materials has been mainly investigated under uniaxial compression, while their performance under uniaxial and multiaxial tension are yet to be understood. To address this gap, a generic elastoplastic homogenization scheme with continuum damage model is developed, and three different lattice materials, namely cubic, modified face-center cubic and body-center cubic, are analyzed under uniaxial, biaxial and triaxial tension. The influence of micro-architecture on the material's failure behavior as well as its macroscopic mechanical performance is thoroughly discussed. For validation, a set of uniaxial tensile experiments are conducted on functionally graded cubic lattice samples that are additively manufactured using Electron Beam Melting (EBM) process. Digital image correlation technique is employed to obtain the macroscopic stress–strain curves, and manufacturing imperfections are inspected using light omitting microscopy. It turns out that the behavior of as-built samples could substantially differ from numerical predictions. Thus, a defect-informed numerical model is employed to accommodate the effect of imperfections. The outcome is in a very good agreement with experimental data, indicating that with proper input data, the developed scheme can accurately predict the mechanical and failure behavior of a given lattice material. [ABSTRACT FROM AUTHOR]

Purpose: This study aimed to evaluate how as-built electron beam melting (EBM) surface properties affect the onset of blood coagulation. The properties of EBM-manufactured implant surfaces for placement have, until now, remained largely unexplored in literature. Implants with conventional designs and custom-made implants have been manufactured using EBM technology and later placed into the human body. Many of the conventional implants used today, such as dental implants, display modified surfaces to optimize bone ingrowth, whereas custom-made implants, by and large, have machined surfaces. However, titanium in itself demonstrates good material properties for the purpose of bone ingrowth., Materials and Methods: Specimens manufactured using EBM were selected according to their surface roughness and process parameters. EBM-produced specimens, conventional machined titanium surfaces, as well as PVC surfaces for control were evaluated using the slide chamber model., Results: A significant increase in activation was found, in all factors evaluated, between the machined samples and EBM-manufactured samples. The results show that EBM-manufactured implants with as-built surfaces augment the thrombogenic properties., Conclusion: EBM that uses Ti6Al4V powder appears to be a good manufacturing solution for load-bearing implants with bone anchorage. The as-built surfaces can be used "as is" for direct bone contact, although any surface treatment available for conventional implants can be performed on EBM-manufactured implants with a conventional design.

The purpose of this article was to describe the workflow from imaging, via virtual design, to manufacturing of patient-specific titanium reconstruction plates, cutting guide and mesh, and its utility in connection with surgical treatment of acquired bone defects in the mandible using additive manufacturing by electron beam melting (EBM). Based on computed tomography scans, polygon skulls were created. Following that virtual treatment plans entailing free microvascular transfer of fibula flaps using patient-specific reconstruction plates, mesh, and cutting guides were designed. The design was based on the specification of a Compact UniLOCK 2.4 Large (Synthes(®), Switzerland). The obtained polygon plates were bent virtually round the reconstructed mandibles. Next, the resections of the mandibles were planned virtually. A cutting guide was outlined to facilitate resection, as well as plates and titanium mesh for insertion of bone or bone substitutes. Polygon plates and meshes were converted to stereolithography format and used in the software Magics for preparation of input files for the successive step, additive manufacturing. EBM was used to manufacture the customized implants in a biocompatible titanium grade, Ti6Al4V ELI. The implants and the cutting guide were cleaned and sterilized, then transferred to the operating theater, and applied during surgery. Commercially available software programs are sufficient in order to virtually plan for production of patient-specific implants. Furthermore, EBM-produced implants are fully usable under clinical conditions in reconstruction of acquired defects in the mandible. A good compliance between the treatment plan and the fit was demonstrated during operation. Within the constraints of this article, the authors describe a workflow for production of patient-specific implants, using EBM manufacturing. Titanium cutting guides, reconstruction plates for fixation of microvascular transfer of osteomyocutaneous bone grafts, and mesh to replace resected bone that can function as a carrier for bone or bone substitutes were designed and tested during reconstructive maxillofacial surgery. A clinically fit, well within the requirements for what is needed and obtained using traditional free hand bending of commercially available devices, or even higher precision, was demonstrated in ablative surgery in four patients.