Search

Germanium combined with high-k dielectrics is put forth as a potential replacement for planar silicon transistors by the semiconductor industry. A study is carried out on the atomic layer deposition (ALD) of HfO2 high-k dielectric layers on HF-cleaned Ge substrates.

The effect of reduction temperature on the the surface composition of Cu/ZnO and Cu/ZnO/SiO2 catalysts was investigated using Low-Energy Ion Scattering. Results showed that the copper and zinc signals can be separated by applying isotopic enrichment and that lead originated from the 68ZnO raw material and segregated to the surface during catalyst reduction. Findings also suggested that the reduction at high-temperature causes the zinc oxide to be segregated to the surface.

Atomic layer deposition (ALD) is used in applications where inorganic material layers with uniform thickness down to the nanometer range are required. For such thicknesses, the growth mode, defining how the material is arranged on the surface during the growth, is of critical importance. In this work, the growth mode of the zirconium tetrachloride/water and the trimethyl aluminum/water ALD process on hydrogen-terminated silicon was investigated by combining information on the total amount of material deposited with information on the surface fraction of the material. The total amount of material deposited was measured by Rutherford backscattering, x-ray fluorescence, and inductively coupled plasma–optical emission spectroscopy, and the surface fractions by low-energy ion scattering. Growth mode modeling was made assuming two-dimensional growth or random deposition (RD), with a “shower model” of RD recently developed for ALD. Experimental surface fractions of the ALD-grown zirconium oxide and aluminum oxide films were lower than the surface fractions calculated assuming RD, suggesting the occurrence of island growth. Island growth was confirmed with transmission electron microscopy (TEM) measurements, from which the island size and number of islands per unit surface area could also be estimated. The conclusion of island growth for the aluminum oxide deposition on hydrogen-terminated silicon contradicts earlier observations. In this work, physical aluminum oxide islands were observed in TEM after 15 ALD reaction cycles. Earlier, thicker aluminum oxide layers have been analyzed, where islands have not been observed because they have already coalesced to form a continuous film. The unreactivity of hydrogen-terminated silicon surface towards the ALD reactants, except for reactive defect areas, is proposed as the origin of island growth. Consequently, island growth can be regarded as “undesired surface-selective ALD.” [ABSTRACT FROM AUTHOR]

Low energy ion scattering is used to selectively probe the outermost atomic layer of the surface. The development of double toroidal analyzers has improved the detection sensitivity of low energy ion scattering by orders of magnitude. The features of these analyzers are discussed. It is shown that the absence of matrix effects makes it possible to quantify the surface density of fluorine in polymers with a LiF(1 0 0) surface. The extreme surface sensitivity of LEIS also enables one to study intramolecular segregation processes. As an example the aging of a polypropylene surface that has been activated with atomic oxygen is described. As an example of the LEIS analysis of highly dispersed isolating surfaces, the formation of coke on a commercial three-way catalyst is discussed. [Copyright &y& Elsevier]