The correlation between the microstructure and soft magnetic properties under the direct current (DC) mode of dual-phase FeCoNi(CuAl)0.8RE0.05(RE = Nd, Y) high-entropy alloys (HEAs) was investigated. X-ray diffraction (XRD) and electron backscattered diffraction (EBSD) results show that all samples consist of face-centered cubic (FCC) and body-centered cubic (BCC) phases. In comparison to the volume fraction of BCC phase of the RE-free HEA (25.3%), Nd and Y additions dramatically increase it to 42.0% and 43.3%, which leads to an increase of the saturation magnetization. RE addition reduces the average grain size from 7.26 μm of the RE-free HEA to 5.42 μm of RE = Nd HEA and 4.88 μm of RE = Y HEA. Stripe magnetic domain structure is observed in both FCC and BCC phases in the RE-free and RE-containing HEAs. The additives of Nd and Y both decrease the stripe pattern width in FCC and BCC phases. The refined structure and finely spaced stripe domain by RE addition can decrease the remanence. Compared with the RE-free HEA, RE addition can effectively enhance the DC soft magnetic property by decreasing the remanence, the coercivity, and the hysteresis loss.

•A user-friendly and adaptive intelligent agent was proposed for the optimal scheduling.•The intelligent agent can autonomously identify model parameters for various users.•The intelligent agent has strong adaptivity to adapt to the changing conditions.•Experimental studies on a laboratory-based smart home energy system were performed.