We study the metal-insulator transition in two sets of amorphous Si_{1-x}Ni_x films. The sets were prepared by different, electron-beam-evaporation-based technologies: evaporation of the alloy, and gradient deposition from separate Ni and Si crucibles. The characterization included electron and scanning tunneling microscopy, glow discharge optical emission spectroscopy, and Rutherford back scattering. Investigating the logarithmic temperature derivative of the conductivity, w = d ln sigma / d ln T, we observe that, for insulating samples, w(T) shows a minimum increasing at both low and high T. Both the minimum value of w and the corresponding temperature seem to tend to zero as the transition is approached. The analysis of this feature of w(T,x) leads to the conclusion that the transition in Si_{1-x}Ni_x is very likely discontinuous at zero temperature in agreement with Mott's original views., Comment: RevTex-file: 25 pages, 17 Postscript figures, 1 GIF figure (original Ps file can be obtained on request). Published version. Changes of v2: Sec. VII completed by two paragraphs on nature of transition, several refs. added

Loss of a vimentin network due to gene disruption created viable mice that did not differ overtly from wild-type littermates. Here, primary fibroblasts derived from vimentin-deficient (-/-) and wild-type (+/+) mouse embryos were cultured, and biological functions were studied in in vitro systems resembling stress situations. Stiffness of -/- fibroblasts was reduced by 40% in comparison to wild-type cells. Vimentin-deficient cells also displayed reduced mechanical stability, motility and directional migration towards different chemo-attractive stimuli. Reorganization of collagen fibrils and contraction of collagen lattices were severely impaired. The spatial organization of focal contact proteins, as well as actin microfilament organization was disturbed. Thus, absence of a vimentin filament network does not impair basic cellular functions needed for growth in culture, but cells are mechanically less stable, and we propose that therefore they are impaired in all functions depending upon mechanical stability.