Search

The objective of this study is to evaluate the impact of the thickness and translucency of various computer-aided design/computer-aided manufacturing (CAD/CAM) materials on the polymerization of dual-cure resin cement in endocrown restorations. Three commercially available CAD/CAM materials—lithium disilicate glass (e.max CAD), resin composite (CERASMART), and a polymer-infiltrated ceramic network (ENAMIC)—were cut into plates with five different thicknesses (1.5, 3.5, 5.5, 7.5, and 9.5 mm) in both high-translucency (HT) and low-translucency (LT) grades. Panavia V5, a commercial dual-cure resin cement, was polymerized through each plate by light irradiation. Post-polymerization treatment was performed by aging at 37 °C for 24 h under light-shielding conditions. The degree of conversion and Vickers hardness measurements were used to characterize the polymerization of the cement. The findings revealed a significant decrease in both the degree of conversion and Vickers hardness with increasing thickness across all CAD/CAM materials. Notably, while the differences in the degree of conversion and Vickers hardness between the HT and LT grades of each material were significant immediately after photoirradiation, these differences became smaller after post-polymerization treatment. Significant differences were observed between samples with a 1.5 mm thickness (conventional crowns) and those with a 5.5 mm or greater thickness (endocrowns), even after post-polymerization treatment. These results suggest that dual-cure resin cement in endocrown restorations undergoes insufficient polymerization. [ABSTRACT FROM AUTHOR]

The use of dental resin composites adapted to computer-aided design/computer-aided manufacturing (CAD/CAM) processes for indirect tooth restoration has increased. A key factor for a successful tooth restoration is the bond between the CAD/CAM composite crown and abutment tooth, achieved using resin-based cement. However, the optimal pairing of the resin cement and CAD/CAM composites remains unclear. This study aimed to identify the optimal combination of a CAD/CAM composite and resin cement for bonding. A commercial methyl methacrylate (MMA)-based resin cement (Super-Bond (SB)) and four other composite-based resin cements (PANAVIA V5; PV, Multilink Automix (MA), ResiCem EX (RC), and RelyX Universal Resin Cement (RX)) were tested experimentally. For the CAD/CAM composites, a commercial polymer-infiltrated ceramic network (PICN)-based composite (VITA ENAMIC (VE)) and two dispersed filler (DF)-based composites (SHOFU BLOCK HC (SH) and CERASMART300 (CE)) were used. Each composite block underwent cutting, polishing, and alumina sandblasting. This was followed by characterization using scanning electron microscopy, inorganic content measurement, surface free energy (SFE) analysis, and shear bond strength (SBS) testing. The results demonstrated that the inorganic content and total SFE of the VE composite were the highest among the examined composites. Furthermore, it bonded highly effectively to all the resin cements. This indicated that PICN-based composites exhibit unique bonding features with resin cements. Additionally, the SBS test results indicated that MMA-based resin cement bonds effectively with both DF- and PICN-based composites. The combination of the PICN-based composite and MMA-based resin cement showed the best bonding performance. [ABSTRACT FROM AUTHOR]

Polymer infiltrated ceramic network (PICN) composites are an increasingly popular dental restorative material that offer mechanical biocompatibility with human enamel. This study aimed to develop a novel PICN composite as a computer-aided design and computer-aided manufacturing (CAD/CAM) block for dental applications. Several PICN composites were prepared under varying conditions via the sintering of a green body prepared from a silica-containing precursor solution, followed by resin infiltration. The flexural strength of the PICN composite block (107.8–153.7 MPa) was similar to a commercial resin-based composite, while the Vickers hardness (204.8–299.2) and flexural modulus (13.0–22.2 GPa) were similar to human enamel and dentin, respectively. The shear bond strength and surface free energy of the composite were higher than those of the commercial resin composites. Scanning electron microscopy and energy dispersive X-ray spectroscopic analysis revealed that the microstructure of the composite consisted of a nanosized silica skeleton and infiltrated resin. The PICN nanocomposite block was successfully used to fabricate a dental crown and core via the CAD/CAM milling process. [ABSTRACT FROM AUTHOR]