Polymer-infiltrated ceramic network materials (PICNs) have high mechanical compatibility with human enamel. However, the wear properties of PICN against natural human enamel have not yet been clarified. We investigated the in vitro two-body wear behaviors of PICNs and an enamel antagonist. Two PICNs were used: Experimental PICN (EXP) prepared via the infiltration of methacrylate-based resin into the porous silica ceramic network and commercial Vita Enamic (ENA). Two commercial dental ceramics, lithium disilicate glass (LDS) and zirconia (ZIR), were also characterized, and their wear performance was compared to PICNs. The samples were subjected to Vickers hardness tests and two-body wear tests that involve the samples being cyclically impacted by enamel antagonists underwater at 37 °C. The results reveal that the Vickers hardness of EXP (301 ± 36) was closest to that of enamel (317 ± 17). The volumetric wear losses of EXP and ENA were similar to those of LDS but higher than that of zirconia. The volumetric wear loss of the enamel antagonist impacted against EXP was moderate among the examined samples. These results suggest that EXP has wear behavior similar to that of enamel. Therefore, PICNs are mechanically comparable to enamel in terms of hardness and wear and are excellent tooth-restoration materials. [ABSTRACT FROM AUTHOR]

Polymer infiltrated ceramic network (PICN) composites are an increasingly popular dental restorative material that offer mechanical biocompatibility with human enamel. This study aimed to develop a novel PICN composite as a computer-aided design and computer-aided manufacturing (CAD/CAM) block for dental applications. Several PICN composites were prepared under varying conditions via the sintering of a green body prepared from a silica-containing precursor solution, followed by resin infiltration. The flexural strength of the PICN composite block (107.8–153.7 MPa) was similar to a commercial resin-based composite, while the Vickers hardness (204.8–299.2) and flexural modulus (13.0–22.2 GPa) were similar to human enamel and dentin, respectively. The shear bond strength and surface free energy of the composite were higher than those of the commercial resin composites. Scanning electron microscopy and energy dispersive X-ray spectroscopic analysis revealed that the microstructure of the composite consisted of a nanosized silica skeleton and infiltrated resin. The PICN nanocomposite block was successfully used to fabricate a dental crown and core via the CAD/CAM milling process. [ABSTRACT FROM AUTHOR]