This work presents the results of comparative studies using complementary methods, such as scanning electron microscopy (SEM), X-ray photoemission spectroscopy (XPS), and thermal desorption spectroscopy (TDS) to investigate the local surface morphology and chemistry of flower-like ZnO nanostructures synthesized by the thermal oxidation technique on native Si/SiO2 substrates. SEM studies showed that our flower-like ZnO nanostructures contained mostly isolated and irregular morphological low-dimensional forms, seen as rolled-up floss flowers, together with local, elongated, complex stalks similar to Liatris flowers, which contained joined short flosses in the form of nanodendrites. Beyond this, XPS studies showed that these nanostructures exhibited a slight surface nonstoichiometry, mostly related to the existence of oxygen-deficient regions, combined with strong undesired C surface contamination. In addition, the TDS studies showed that these undesired surface contaminations (including mainly C species and hydroxyl groups) are only slightly removed from the surface of our flower-like ZnO nanostructures, causing an expected modification of their nonstoichiometry. All of these effects are of great importance when using our flower-like ZnO nanostructures in gas sensor devices for detecting oxidizing gases because surface contamination leads to an undesired barrier for toxic gas adsorption, and it can additionally be responsible for the uncontrolled sensor aging effect. [ABSTRACT FROM AUTHOR]

This work presents, for the very first time, very promising nitrogen dioxide (NO2) sensing characteristics of SnOx nanolayers obtained by the innovative and unique rheotaxial growth and vacuum oxidation (RGVO) processing technique. The NO2 gas sensing experiments were performed using the novel surface photovoltage gas sensing device. The measured detection limit at room temperature (RT) is as low as 10 ppb NO2 in synthetic air, whereas the detection limit calculated on the basis of signal to noise ratio is around 6 ppb NO2. For the complementary study of surface chemistry of RGVO SnOx nanolayers, including nonstoichiometry, presence of carbon contamination and surface bondings, the X-ray photoelectron spectroscopy (XPS) method was applied. The SnOx RGVO samples reveal nonstoichiometry because the relative concentration [O]/[Sn] equals 0.94 for the as deposited sample and increases upon subsequent air exposure and NO2 sensing. Moreover, carbon contamination has been recognized after exposing the RGVO SnOx nanolayers to the air and during the NO2 detection. [ABSTRACT FROM AUTHOR]