Search

This work presents the results of comparative studies using complementary methods, such as scanning electron microscopy (SEM), X-ray photoemission spectroscopy (XPS), and thermal desorption spectroscopy (TDS) to investigate the local surface morphology and chemistry of flower-like ZnO nanostructures synthesized by the thermal oxidation technique on native Si/SiO2 substrates. SEM studies showed that our flower-like ZnO nanostructures contained mostly isolated and irregular morphological low-dimensional forms, seen as rolled-up floss flowers, together with local, elongated, complex stalks similar to Liatris flowers, which contained joined short flosses in the form of nanodendrites. Beyond this, XPS studies showed that these nanostructures exhibited a slight surface nonstoichiometry, mostly related to the existence of oxygen-deficient regions, combined with strong undesired C surface contamination. In addition, the TDS studies showed that these undesired surface contaminations (including mainly C species and hydroxyl groups) are only slightly removed from the surface of our flower-like ZnO nanostructures, causing an expected modification of their nonstoichiometry. All of these effects are of great importance when using our flower-like ZnO nanostructures in gas sensor devices for detecting oxidizing gases because surface contamination leads to an undesired barrier for toxic gas adsorption, and it can additionally be responsible for the uncontrolled sensor aging effect. [ABSTRACT FROM AUTHOR]

The surface chemistry and the morphology of SnO2 nanowires of average length and diameter of several μm and around 100 nm, respectively, deposited by vapor phase deposition (VPD) method on Au-covered Si substrate, were studied before and after subsequent air exposure. For this purpose, surface-sensitive methods, including X-ray photoelectron spectroscopy (XPS), thermal desorption spectroscopy (TDS) and the scanning electron microscopy (SEM), were applied. The studies presented within this paper allowed to determine their surface non-stoichiometry combined with the presence of carbon contaminations, in a good correlation with their surface morphology. The relative concentrations of the main components [O]/[Sn]; [C]/[Sn]; [Au]/[Sn], together with the O-Sn; O-Si bonds, were analyzed. The results of TDS remained in a good agreement with the observations from XPS. Moreover, conclusions obtained for SnO2 nanowires deposited with the use of Au catalyst were compared to the previous obtained for Ag-assisted tin dioxide nanowires. The information obtained within these studies is of a great importance for the potential application of SnO2 nanowires in the field of novel chemical nanosensor devices, since the results can provide an interpretation of how aging effects influence gas sensor dynamic characteristics. [ABSTRACT FROM AUTHOR]

In this paper a novel type of a highly sensitive gas sensor device based on the surface photovoltage effect is described. It is based on the Kelvin probe approach. Porous ZnO nanostructured thin films deposited by the direct current (DC) reactive magnetron sputtering method are used as the active gas sensing electrode material. Crucially, the obtained gas sensing material exhibited a nanocoral surface morphology and surface Zn to O non-stoichiometry with respect to its bulk mass. Among other responses, the demonstrated SPV gas sensor device exhibits a high response to an NO2 concentration as low as 1 ppm, with a signal to noise ratio of about 50 and a fast response time of several seconds under room temperature conditions. [ABSTRACT FROM AUTHOR]

In this paper, the results of detailed X-ray photoelectron spectroscopy (XPS) studies combined with atomic force microscopy (AFM) investigation concerning the local surface chemistry and morphology of nanostructured ZnO thin films are presented. They have been deposited by direct current (DC) reactive magnetron sputtering under variable absolute Ar/O2 flows (in sccm): 3:0.3; 8:0.8; 10:1; 15:1.5; 20:2, and 30:3, respectively. The XPS studies allowed us to obtain the information on: (1) the relative concentrations of main elements related to their surface nonstoichiometry; (2) the existence of undesired C surface contaminations; and (3) the various forms of surface bondings. It was found that only for the nanostructured ZnO thin films, deposited under extremely different conditions, i.e., for Ar/O2 flow ratio equal to 3:0.3 and 30:3 (in sccm), respectively, an evident and the most pronounced difference had been observed. The same was for the case of AFM experiments. What is crucial, our experiments allowed us to find the correlation mainly between the lowest level of C contaminations and the local surface morphology of nanostructured ZnO thin films obtained at the highest Ar/O2 ratio (30:3), for which the densely packaged (agglomerated) nanograins were observed, yielding a smaller surface area for undesired C adsorption. The obtained information can help in understanding the reason of still rather poor gas sensor characteristics of ZnO based nanostructures including the undesired ageing effect, being of a serious barrier for their potential application in the development of novel gas sensor devices. [ABSTRACT FROM AUTHOR]

This paper presents the results of studies of the local surface properties of pure and highly Nb-doped (12 wt %) TiO2 nanotubes (TNT) using the X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) methods, respectively. XPS analysis showed that the pure TNT exhibit an evident over-stoichiometry combined with high level of undesired C contaminations, which was confirmed by the relative concentration of specific elements O, Ti and C (with respect to all the surface atoms) equal to 0.46, 018 and 0.36, respectively. In turn, for the highly Nb-doped (12 wt %) TNT, a slightly different surface chemistry was observed because the relative concentration of specific elements O and Ti and, with respect to all the surface atoms, is slightly lower, that is, 0.42 and 0.12, respectively; this is directly related to the fact that Nb atoms appeared having the relative concentration at the level of 0.09, whereas the undesired C contaminations reached the same level (0.36), as is the case of pure TNT. In addition, SEM analysis confirms that there are evident free spaces between the specific slops containing several TNT, what was additionally confirmed by the contribution of specific surface bonding coming from the SiO2/Si substrate. The obtained information allowed us a new insight on the potential origin of aging effect at the surface of TNT in atmosphere being the undesired limitation for their potential application as the chemical resistive type sensors or in any other fields of their application related to their surface activity. [ABSTRACT FROM AUTHOR]

This work presents, for the very first time, very promising nitrogen dioxide (NO2) sensing characteristics of SnOx nanolayers obtained by the innovative and unique rheotaxial growth and vacuum oxidation (RGVO) processing technique. The NO2 gas sensing experiments were performed using the novel surface photovoltage gas sensing device. The measured detection limit at room temperature (RT) is as low as 10 ppb NO2 in synthetic air, whereas the detection limit calculated on the basis of signal to noise ratio is around 6 ppb NO2. For the complementary study of surface chemistry of RGVO SnOx nanolayers, including nonstoichiometry, presence of carbon contamination and surface bondings, the X-ray photoelectron spectroscopy (XPS) method was applied. The SnOx RGVO samples reveal nonstoichiometry because the relative concentration [O]/[Sn] equals 0.94 for the as deposited sample and increases upon subsequent air exposure and NO2 sensing. Moreover, carbon contamination has been recognized after exposing the RGVO SnOx nanolayers to the air and during the NO2 detection. [ABSTRACT FROM AUTHOR]

Two highly efficient commercial organic photosensitizers—azure A (AA) and 5-(4-aminophenyl)-10,15,20-(triphenyl)porphyrin (APTPP)—were covalently attached to the glass surface to form a photoactive monolayer. The proposed straightforward strategy consists of three steps, i.e., the initial chemical grafting of 3-aminopropyltriethoxysilane (APTES) followed by two chemical postmodification steps. The chemical structure of the resulting mixed monolayer (MIX_TC_APTES@glass) was widely characterized by X-ray photoelectron (XPS) and Raman spectroscopies, while its photoactive properties were investigated in situ by UV–Vis spectroscopy with α-terpinene as a chemical trap. It was shown that both photosensitizers retain their activity toward light-activated generation of reactive oxygen species (ROS) after immobilization on the glassy surface and that the resulting nanolayer shows high stability. Thanks to the complementarity of the spectral properties of AA and APTPP, the effectiveness of the ROS photogeneration under broadband illumination can be optimized. The reported light-activated nanocoating demonstrated promising antimicrobial activity toward Escherichia coli (E. coli), by reducing the number of adhered bacteria compared to the unmodified glass surface. [ABSTRACT FROM AUTHOR]

In this article, we present results concerning the impact of structural and chemical properties of zinc oxide in various morphological forms and its gas-sensitive properties, tested in an atmosphere containing a very aggressive gas such as chlorine. The aim of this research was to understand the mechanism of chlorine detection using a resistive gas sensor with an active layer made of zinc oxide with a different structure and morphology. Two types of ZnO sensor layers obtained by two different technological methods were used in sensor construction. Their morphology, crystal structure, specific surface area, porosity, surface chemistry and structural defects were characterized, and then compared with gas-sensitive properties in a chlorine-containing atmosphere. To achieve this goal, scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and photoluminescence spectroscopy (PL) methods were used. The sensing properties of obtained active layers were tested by the temperature stimulated conductance method (TSC). We have noticed that their response in a chlorine atmosphere is not determined by the size of the specific surface or porosity. The obtained results showed that the structural defects of ZnO crystals play the most important role in chlorine detection. We demonstrated that Cl2 adsorption is a concurrent process to oxygen adsorption. Both of them occur on the same active species (oxygen vacancies). Their concentration is higher on the side planes of the zinc oxide crystal than the others. Additionally, ZnO sublimation process plays an important role in the chlorine detection mechanism. [ABSTRACT FROM AUTHOR]