Search

The crystal growth, optical spectra and lifetime of Dy:CaGdAlO 4 crystal were investigated for the first time to our best knowledge. Single Dy:CaGdAlO 4 crystal with size of Φ4 × 40 mm 3 was grown by floating zone method. The peak absorption cross-sections were calculated to be 2.43 × 10 −21 cm 2 and 1.28 × 10 −21 cm 2 at 453 nm for σ and π polarizations. The Judd-Ofelt (JO) parameters of Ω 2 , Ω 4 and Ω 6 were calculated to be 1.8 × 10 −20 cm 2 , 1.0 × 10 −20 cm 2 and 0.5 × 10 −20 cm 2 , respectively. The emission cross-sections were calculated to be 0.51 × 10 −20 cm 2 and 0.55 × 10 −20 cm 2 for σ and π polarizations. The fluorescence decay time is 222 μs. The results indicate that the Dy:CaGdAlO 4 crystal is a potential candidate for yellow laser operation. [ABSTRACT FROM AUTHOR]

Sm:YAlO 3 (Sm:YAP) crystal with size of Φ28 × 80 mm3 was grown by Czochralski (Cz) method. Polarized absorption spectra and fluorescence spectra of Sm:YAP crystal were discussed for the first time. The peak emission cross-sections were calculated to be 0.80 × 10−21 cm2 (604 nm for a-polarization), 1.82 × 10−21 cm2 (604 nm for b-polarization) and 1.63 × 10−21 cm2 (610 nm for c-polarization), respectively. The Judd-Ofelt (JO) intensity parameters were calculated to be Ω 2 = 2.59 × 10−20 cm2, Ω 4 = 1.78 × 10−20 cm2 and Ω 6 = 2.98 × 10−20 cm2, respectively. The decay lifetime of 4G 5/2 energy level was measured to be 2.51 ms. All above results indicate the Sm:YAP crystal may be a potential candidate of reddish-orange laser pumped directly by the GaN/InGaN laser diode. • Sm:YAlO 3 crystal was grown by Cz method. • Polarized optical spectra of Sm:YAlO 3 crystal were investigated. • The transitions of 4G 5/2 → 6H 7/2 have the highest branching ratio value, which is suitable for reddish-orange laser. [ABSTRACT FROM AUTHOR]

Pr 3+ -doped YAlO 3 (YAP) single crystal was successfully grown by the Czochralski (Cz) method. Polarized absorption and polarized fluorescence spectra were measured at the room temperature. The spectroscopic parameters based on the polarized absorption spectra were calculated by Judd-Ofelt (J-O) theory for the first time. The fluorescence lifetime of 3 P 0 energy level was fitted to be 19.16 μs with the quantum efficiency of 95.8%. Through the analyzing of the spectroscopic properties, Pr:YAP crystal was demonstrated to be a promising candidate for solid state laser operation. [ABSTRACT FROM AUTHOR]

In this paper, the Floating zone technique was used to grow high-quality Cr3+:YScO 3 crystals. The absorption cross-sections of the 4A 2 →4T 1 transition and 4A 2 →4T 2 transitions were calculated to be 1.71 × 10−20 cm2 at 488 nm and 0.72 × 10−20 cm2 at 666 nm, respectively. The crystal field strength Dq, Racah parameters B, and C were calculated to be 1502 cm−1, 533 cm−1, and 3362 cm−1, respectively. In the Cr3+:YScO 3 crystal, the effective phonon energy and Huang-Rhys factor S were calculated to be 284 cm−1 and 8.62, respectively. The emission cross-section at 988 nm corresponding to the 4T 2 →4A 2 transition was calculated to be 1.44 × 10−20 cm2 with full width at half maximum (FWHM) of 318 nm. All the results show that Cr3+:YScO 3 crystal has the potential to be a tunable and ultrafast laser crystal. • Cr:YScO 3 crystals were successfully grown by the Floating zone technique(FZ) method. • Broad emission spectrum with full width at half maximum (FWHM) of 318 nm in Cr:YScO 3 crystals was observed. • Spectral properties and crystal field parameters of Cr:YScO 3 crystals were investigated and analysed. [ABSTRACT FROM AUTHOR]

LaMgAl 11 O 19 (LMA) crystal with nominal Sm3+ concentrations of 8 at.% was grown by the Czochralski method. Polarized absorption spectra, polarized emission spectra and fluorescence decay curve of Sm:LMA crystal were recorded at room temperature. The absorption cross-sections at 404 nm were calculated to be 2.33 × 10−20 cm2 and 0.86 × 10−20 cm2 for σ and π polarization, respectively. The spontaneous transition rates, branching ratios and the radiative lifetime of the 4G 5/2 multiplet, were calculated. The Judd-Ofelt theory has been applied to evaluate the Ω t (t = 2, 4, 6) intensity parameters. The highest stimulated emission cross-sections for the 4G 5/2 → 6H 7/2 transition around 594 nm were calculated to be 1.67 × 10−21 cm2 for σ polarization and 1.15 × 10−21 cm2 for π polarization, with full width at half maximum (FWHM) of 7.68 nm and 7.27 nm, respectively. The fluorescence lifetime of the 4G 5/2 manifold was 1.84 ms. All the results show that Sm:LMA crystal would be a promising orange-red solid state laser material. • The most intensive absorption line of Sm3+ ion, suitable for 405 nm InGaN laser diode. • The rigidity of Sm:LMA crystal is higher than some host crystals. • The value Ω 2 of Sm:LMA crystal is comparable to Sm:LiYF 4. • The large parameter σ em τ of Sm3+ in LMA is beneficial for the solid state laser. [ABSTRACT FROM AUTHOR]