High intrinsic ionic conductivity and a theoretical capacity of MoS 2 is well appreciated and gathered great attention for an electrode asset for energy storage applications. The MoS 2 layers inter connected with one-dimensional carbon nanofibers (CNFs) are successfully prepared to give a conductive three-dimensional network for the robust charge transfer kinetics. The MoS 2 nanosheets adhered together to form micro flowers accomplished by a simple hydrothermal process. Further, the nanosheets are allowed to grow over the electrospun CNFs directly. The structural, functional, and morphological characterizations unanimously revealed the nanocomposite formation. Also, the surface area has been determined by BET analysis and subjected to electrochemical studies as an electrode for supercapacitors. The nanocomposite deposited on the graphite sheet (1 × 1 cm2) displays the high capacitance counterparts of 903.9 Fg-1 achieved by a lower current density of 1 Ag-1 and maintained 94% efficiency even 5000 cycles after a charge-discharge process. This process was examined with the potential range of 0.8 V (−0.4 to +0.4 V) in 1 M KCl electrolyte. These results confirms the prepared nanocomposite can be used as a proficient electrode for the creation of high capacitance supercapacitors with good cyclability. Image 1 • Direct growth of MoS 2 on carbon nanofibers attained by facile hydrothermal process. • FESEM and XRD results confirms the MoS 2 encapsulated CNFs with hexagonal phase. • CV were employed with different electrolytes to evaluate the influence of ion size. • The prepared MoS 2 /CNF exhibits the specific capacitance of 903.9 Fg-1 at a current density 1 Ag-1. • It maintains 94% efficiency even after 5000 cycles. [ABSTRACT FROM AUTHOR]

Porous carbon nanofibers (CNFs) with high energy storage performance were fabricated with a single precursor polymer, 6FDA-TFMB, without the use of any pore-generating materials. 6FDA-TFMB was synthesized, electrospun, and thermally treated to produce binder-free CNF electrodes for electrochemical double-layer capacitors (EDLCs). Highly porous CNFs with a surface area of 2213 m2 g−1 were prepared by steam-activation. CNFs derived from 6FDA-TFMB showed rectangular cyclic voltammograms with a specific capacitance of 292.3 F g−1 at 10 mV s−1. It was also seen that CNFs exhibit a maximum energy density of 13.1 Wh kg−1 at 0.5 A g−1 and power density of 1.7 kW kg−1 at 5 A g−1, which is significantly higher than those from the common precursor polymer, polyacrylonitrile (PAN). [ABSTRACT FROM AUTHOR]