Search

Ultrathin superhydrophobic–superoleophilic fibrous poly (vinylidene fluoride) (PVDF) membranes were prepared by means of electrospinning technique for the purpose of low-cost, high-efficiency water–oil separation. The ultrathin electrospun fibrous PVDF membranes exhibited a high water contact angle up to 153° and nearly zero oil (diesel) contact angle. The surface morphology and hydrophobicity of the membranes can be conveniently tuned by adjusting the PVDF concentration of the electrospinning solutions. The obtained ultrathin fibrous PVDF membranes showed excellent performance in separation of water-in-oil emulsions. [ABSTRACT FROM AUTHOR]

Abstract: This paper reports the fabrication and electrochemical properties of novel high-performance pseudosupercapacitor electrodes made of graphene-beaded carbon nanofibers (G/CNFs) surface-coated with nanostructured conducting polymers. The G/CNFs were produced by electrospinning the precursor graphene-beaded polymer nanofibers, followed by controlled pyrolysis. In situ polymerization in aqueous solution was utilized to coat an ultrathin layer of thorn-like polyaniline (PANI) nanorods onto the G/CNFs to form ternary PANI-coated G/CNFs (PANI-G/CNFs). The highly porous network morphology of PANI-G/CNFs exhibited a very large specific surface area, low internal resistance, and fast redox rate. Electrochemical characterization indicated that the PANI-G/CNF based pseudosupercapacitors carried a high value of specific capacitance up to 637 F g−1 at a current density of 0.15 A g−1 and still maintained the high value of specific capacitance of 478 F g−1 (only 25% decrease) even at a high current density of 6 A g−1. The pseudosupercapacitor showed a very good cycling stability of 87% after 1000 charge/discharge cycles at a very high current density of 15 A g−1. The experimental results indicated that the novel hierarchical, porous PANI-G/CNFs are a promising electrode material for use in high-performance energy storage devices. [Copyright &y& Elsevier]

This paper reports the fabrication and filtration characterization of advanced fibrous cellulose acetate (CA) membranes for high-flux water filtration. The ultrathin nonwoven fibrous CA membranes with varying fiber diameter and areal weight were produced by electrospinning and post-processed by hot-press. The filtration efficiency of the ultrathin fibrous CA membranes was characterized by controlled water-filtration tests based on artificial colloids prepared via dispersing polystyrene (PS) particles of the diameters of 5 μm, 2 μm, 500 nm, and 100 nm in water, respectively. Natural river water was further used for evaluating the filtration capability of the electrospun fibrous CA membranes. Experimental results show that the rejection rate of the present fibrous CA membranes to PS particles with the diameter of 2 μm was up to 99.8%. In addition, the filtration efficiency of the electrospun fibrous CA membranes increased with increasing areal weight of the membranes. In the case of the filtering electrospun fibrous CA membranes with the fiber diameter of ∼800 nm and membrane areal weight ∼0.005 g/cm 2 , the measured turbidity of natural river water after filtration can reach as low as 0.135 nephelometric turbidity unit (NTU) while the initial flow flux can reach up to 20,455 L/m 2 h at the feed pressure 14 psi. The study suggests that low-cost electrospun fibrous membranes can be used for stable, high-flux water microfiltration with the filtration efficiency. [ABSTRACT FROM AUTHOR]