Alginates are renewable materials with excellent biocompatibility and cost-effectiveness in comparison with other biodegradable polymers. However, these hydrogels have poor mechanical properties that restrict their applications in biomedical fields such as skin tissue engineering. In this regard, the study follows an enhanced engineering route to produce alginate-based films reinforced with different amounts (0, 0.1, 0.5, 1 and 2% w / w) of carbon nanofibers (CNFs) and characterize their physical and biological properties. The results of this study showed that these composites possess similar biological properties to neat alginate hydrogels. Thus, none of the synthesized composite materials were cytotoxic and no cell adhesion was observed on the films. Water sorption at the body temperature did not suffer strong changes with the incorporation of CNFs into the alginate matrix. The dynamic mechanical and tensile/compressive properties of calcium alginate significantly improved with the addition of even a very low amount of CNFs. Thus, the tensile and compression modulus of the calcium alginate films in the dry and hydrated state increases up to three and six times, respectively, with the addition of 2% w / w CNFs. In addition, the composites reinforced with the lowest CNFs content have the advantage of possessing more transparency and lower production costs. Unlabelled Image • Reinforced alginate-based composites for biomedical applications • Enhancement of dynamic mechanical and tensile/compressive performance • Nanocomposites with similar biological behavior than neat alginate hydrogels • Non-cytotoxic nanocomposites in human keratinocyte HaCaT cells [ABSTRACT FROM AUTHOR]

A series of alginate films was synthesised with several calcium chloride cross-linker contents (from 3 to 18% w/w) with and without a very low amount (0.1% w/w) of carbon nanofibers (CNFs) in order to reduce the production costs as much as possible. The results of this study showed a very significant enhancement of liquid water diffusion and mechanical compressive modulus for high calcium chloride contents when this minuscule amount of CNFs is incorporated into calcium alginate hydrogels. These excellent results are attributed to a double cross-linking process, in which calcium cations are capable of cross-linking both alginate chains and CNFs creating a reinforced structure exhibiting ultrafast water diffusion through carbon nanochannels. Thus, these excellent results render these new alginate composites very promising for many bioengineering fields in need of low-cost advanced hydrogels with superior water diffusion and compression properties. [ABSTRACT FROM AUTHOR]