Search

Polyvinylidene fluoride (PVDF) electrospun nanofibrous membranes (ENMs), consolidated with a heatpress process and of various thicknesses were fabricated and tested in a DCMD cell at five different operating conditions. Membranes as thin as 27 μm were sufficiently robust for evaluation and gave a transmembrane flux as high as 60 L/h m 2 . An analytical model was created to estimate the optimal membrane thickness for DCMD operations. It is found that the value of optimal thickness increases with reduced heat transfer coefficients; decreased feed inlet temperature; increased membrane permeability; and increased salinity. Even for 10% NaCl the predicted optimum was estimated to be 13 μm which was too thin for experimental confirmation. Based upon this analysis but with due allowance for the variation of heat transfer coefficients with temperature dependent physical properties a single Matlab model was created to fit the five sets of data. With the introduction of a structural derivation factor, which reflected the experimentally determined variation of porosity and pore size with thickness, the model was found to fit the data very well. [ABSTRACT FROM AUTHOR]

Porous hydrophobic polyvinylidene fluoride (PVDF) membranes have been extensively used in direct-contact membrane distillation (DCMD) processes. However, these PVDF membranes are vulnerable to membrane fouling and pore wetting in low surface tension feeds, restricting its application for water recovery from challenging industrial wastewaters. Therefore, it is of paramount importance to engineer fouling- and wetting-resistant MD membranes for robust long-term applications. In this study, a superoleophobic composite hollow fiber membrane with sandwich structure has been developed via accelerated oxidant-induced polydopamine (PDA) deposition on both the outer and inner surfaces of a commercial hydrophobic PVDF membrane under slightly acidic conditions (pH = 5). The modified surface prevents organics adhesion ascribing to its underwater superoleophobicity while the unmodified pores remain hydrophobic for vapor transport. The long-term robustness of the PDA-decorated membrane in highly saline feeds containing low surface tension contaminants has been evaluated via bench-scale DCMD experiments. In contrast to the pristine PVDF membrane, the PDA-decorated membrane exhibits excellent fouling- and wetting-resistant properties in different surfactant solutions as well as oil-in-water emulsion. The PDA-decorated membrane has also been used for seawater desalination, during which it maintains a stable flux and high salt rejection rate. Furthermore, the PDA-decorated membrane presents a flux enhancement of up to 70% over the pristine PVDF membrane in 3.5 wt% NaCl solution at 333 K. This study demonstrates the potential of the PDA-decorated membrane for extended DCMD applications such as water recovery from industrial wastewater containing low surface tension substances. [ABSTRACT FROM AUTHOR]

Polyvinylidene fluoride (PVDF)/polytetrafluoroethylene (PTFE) hollow fiber membranes were developed via thermally induced phase separation (TIPS) method for direct contact membrane distillation (DCMD). The effects of PTFE addition on the thermal behavior of the dope mixtures and membrane formation were investigated. It was found that the crystallization of PVDF was significantly enhanced with increased nucleation sites provided by PTFE particles, leading to promoted formation of smaller spherulites in a greater density. Furthermore, the improved uniformity and increased amount of cavity between the spherical crystallites coherently facilitated the formation of smaller pores ranging from 0.08 to 0.12 μm. With certain PTFE loading, the membranes exhibited improved porosity, water permeability and hydrophobicity as well as enhanced tensile strength of 9.4 ± 0.3 MPa. To examine the DCMD performance, the membranes were tested under various conditions using 3.5 wt% NaCl solution. A stable permeation flux of 28.3 kg m − 2 h − 1 at the feed temperature of 60 °C with 99.99% NaCl rejection for over 50 h of operation was achieved, which is comparable with similar type of PVDF membranes while the newly developed membrane exhibited better mechanical strength. This study suggests that the as-spun PVDF/PTFE hollow fiber membranes have potential for DCMD applications. [ABSTRACT FROM AUTHOR]

Increasing demand for oil and gas leads to the generation of substantial amount of produced water, bringing about deleterious impacts on the environment. Direct-contact membrane distillation (DCMD) could be a possible option for dewatering oil-in-water (O/W) emulsions because of many benefits brought by the DCMD process. However, these low surface tension solutions pose some difficult issues such as membrane fouling and pore wetting. The mechanisms involved are not fully understood due to the lack of study of the interaction between the emulsions and the membrane surface in the DCMD domain. To address the challenges, this study aims at developing a fundamental understanding of the relationship between surfactant-stabilized O/W emulsions and polyvinylidene fluoride (PVDF) membrane surface in DCMD operations. Effects of surfactant types (Span 20, Tween 20, and sodium dodecyl sulfate), oil concentration, and oil types (petroleum and vacuum pump oil) were systematically studied to better understand the fouling and wetting mechanisms involved. The results reveal that surfactant concentration and hydrophobicity had an influence on the membrane fouling and wetting behaviors. Surfactants with a lower hydrophilic-lipophilic balance (HLB) value could make the PVDF membrane surface less hydrophobic and cause less severe fouling by restraining the adsorption of oil droplets on the membrane surface. These findings suggest that membrane surface modification is required to achieve anti-fouling and anti-wetting properties to make DCMD an energy-efficient and effective technology for treating produced water. [ABSTRACT FROM AUTHOR]

Hydrophobic membranes suffer from wetting and scaling when treating hypersaline brine using membrane distillation (MD). Thus omniphobic membranes with re-entrant surfaces have been developed by diverse modifications to enhance anti-wetting/scaling properties. However, those post-modifications usually sacrifice membrane permeability in spite of improved stability. In this work, omniphobic membranes were fabricated by decorating polyvinylidene fluoride (PVDF) nanofibrous membranes with different silica nanoparticles (SiNPs) followed by fluorination. Compared to unmodified nanofibrous and commercial PVDF membranes, both smaller SiNPs coated membrane #P-Min and larger SiNPs coated membrane #P-Max can perfectly sustain liquids with low surface tensions on their surfaces without wetting. In contrast to #P-Max with an oil contact angle of 136 ± 1°, #P-Min exhibited better oleophobicity with an oil contact angle of 152 ± 1°. In addition, the rigidity of their omniphobic properties was confirmed by testing in harsh conditions. Moreover, #P-Min successfully overcame the trade-off relation between membrane permeability and rejection with an enhanced MD flux due to more effective water evaporation area on membrane surface and a higher membrane porosity. While #P-Max was wetted by a hypersaline feed solution composed of 25 wt% NaCl, #P-Min could maintain a stable flux of 15 L m−2h−1 in a continuous 7-h MD operation, which proved its excellent performance for brine treatment. Furthermore, #P-Min exhibited less scaling tendency when feed was a saturated gypsum solution. Compared to #P-Max , the better anti-scaling properties of #P-Min should be due to its higher surface energy barrier, better slippery property and less solid-liquid contact area, which effectively impede crystal nucleation and attachment. Image 1 • Effects of nano-scaled roughness on membrane omniphobicity were studied. • As-prepared omniphobic membranes were stable under harsh conditions. • Omniphobic membrane coated with smaller NPs exhibited better performance. • It should be due to high surface energy barrier, slippery property and less solid-liquid contact area. [ABSTRACT FROM AUTHOR]