Novel insight on the local surface properties of ZnO nanowires (NW) deposited by the evaporation-condensation method on Ag-covered Si substrates is proposed, based on the results of comparative studies by using the scanning electron microscopy (SEM), x-ray photoemission spectroscopy (XPS) and thermal desorption spectroscopy (TDS) methods, respectively. SEM studies showed that ZnO nanowires (nanoribbons) are mostly isolated and irregular, having the average length μm and the average at the level of tens nm, respectively. Our XPS studies confirmed their evident surface non-stoichiometry, combined with strong C surface contaminations, which was related to the existence of oxygen-deficient regions. Additionally, TDS studies showed that undesired surface contaminations (including C species and hydroxyl groups) on the surface of ZnO NWs can be removed almost completely, leading to an increase of the final non-stoichiometry. Both effects are of great importance when using ZnO NWs for the detection of oxidizing gases, because the undesired C contaminations (including C–OH species) play the role of undesired barriers for the gas adsorption, especially at the low working temperature, additionally affecting the uncontrolled sensor ageing effect. [ABSTRACT FROM AUTHOR]

The surface chemistry and the morphology of SnO2 nanowires of average length and diameter of several μm and around 100 nm, respectively, deposited by vapor phase deposition (VPD) method on Au-covered Si substrate, were studied before and after subsequent air exposure. For this purpose, surface-sensitive methods, including X-ray photoelectron spectroscopy (XPS), thermal desorption spectroscopy (TDS) and the scanning electron microscopy (SEM), were applied. The studies presented within this paper allowed to determine their surface non-stoichiometry combined with the presence of carbon contaminations, in a good correlation with their surface morphology. The relative concentrations of the main components [O]/[Sn]; [C]/[Sn]; [Au]/[Sn], together with the O-Sn; O-Si bonds, were analyzed. The results of TDS remained in a good agreement with the observations from XPS. Moreover, conclusions obtained for SnO2 nanowires deposited with the use of Au catalyst were compared to the previous obtained for Ag-assisted tin dioxide nanowires. The information obtained within these studies is of a great importance for the potential application of SnO2 nanowires in the field of novel chemical nanosensor devices, since the results can provide an interpretation of how aging effects influence gas sensor dynamic characteristics. [ABSTRACT FROM AUTHOR]