Search

Abstract A series of Fe-3 to 18 at.% Cr binary ferritic alloys were neutron irradiated side by side, in the Advanced Test Reactor (ATR) at a temperature of ∼320 °C to a dose of ∼1.8 dpa. Three types of features that form under irradiation are relevant: (i) solute clusters; (ii) α′ precipitates; and, (iii) dislocation loops. The size and number density of the precipitates and loops were measured by transmission electron microscopy (TEM) and compared to previous atom probe tomography (APT) observations. The loop density systematically decreases with increasing Cr, while the number of α′ precipitates increase at 9Cr and above. A major objective of this work is to estimate the dispersed barrier obstacle strength factors (α j) for loops, clusters and α′ precipitates, based on the combined microstructural observations and corresponding irradiation hardening measurements. Standard dispersed barrier-hardening models and computationally derived superposition rules were least square fit to determine the α j. The optimized hardening predictions are in very good agreement with experiment if mixed linear sum and root square sum superposition rules are used. Five increments of 168 h isochronal anneals of the 6Cr alloy between 300 and 400 °C coarsened the loops, while 300 h anneals of the 18Cr at 500 and 600 °C coarsened and dissolved the α′ precipitates, respectively, consistent with the Fe-Cr phase diagram. [ABSTRACT FROM AUTHOR]

Microstructural evolutions in two variants of the F82H 8 wt%Cr tempered martensitic steel under dual (He+ plus Fe3+) ion irradiations at 500 °C have been characterized by transmission electron microscopy. Emphasis is on understanding the combined effects of displacements per atom (dpa) and the helium/dpa ratio (He/dpa) on cavity evolution and void swelling (f v). The dual ion database includes 231 alloy-dpa-He/dpa conditions for irradiations up to ∼ 82 dpa and 3700 appm helium. We hypothesize that the large "scatter" observed in the f v data is primarily due to local microstructural variations, especially those that shield regions at shallower depths from the effects of injected interstitial atoms, which would otherwise reduce f v. More generally, our hypothesis is that the highest f v data, at a specified dpa and He/dpa, provides the most appropriate estimate of swelling for fusion neutron irradiation conditions. The dose dependence of f v can be described by an incubation dpa i , marking the onset of significant void growth, and a post-incubation swelling rate, f v ' = Δf v /Δdpa. Both dpa i and f v ' decrease with increasing He/dpa. The f v ' data are quantitatively consistent with a simple model for defect partitioning between evolving bubble, void, and dislocation sinks strengths and biases. Most notably, the model correctly predicts both the incubation dpa i , and the subsequent f v ', in spite of the fact that they reflect somewhat different physics. Our analysis also suggests that defect recombination is modest at 500 °C. Along with other considerations, this supports the hypothesis that, even at high dpa rates, dual ion irradiations can be used to reasonably emulate void nucleation and growth for a range of fusion-relevant neutron irradiation service conditions. A companion paper incorporates the results of this study in a reduced-order, data-driven void swelling model. [ABSTRACT FROM AUTHOR]

The UCSB database on cavity evolution in 9-12Cr tempered martensitic steels (TMS), includes the results for both dual heavy and helium ion (DII), and High Flux Isotope Reactor (HFIR) in situ helium injection (ISHI) neutron irradiations at 500°C. These results were combined with literature single ion and fission neutron irradiation data to derive a model for the void volume fraction, f v , as a function of displacements per atom (dpa) and transmutant helium concentrations in atomic parts per million (appm). The scientific foundation for the paper is described in a companion paper entitled "Cavity Evolution and Void Swelling in Dual Ion Irradiated Tempered Martensitic Steels ". Here, we show that f v (dpa, He/dpa) is described by the incubation dose, dpa i , for the onset of void growth, and the post-incubation growth rate, f v '(%/dpa). Both dpa i and f v ' decrease with increasing He/dpa at > ∼ 5. The dpa i is also lower for the ISHI neutron irradiations at the same He/dpa. Single heavy ion and fission reactor neutron irradiations, with low He/dpa ratios, have a much larger dpa i. Based on a combined analysis of DII, single ion, ISHI and fission neutron data, we further show that the post-incubation f v data analyzed here have a common empirical curve shape, with f v ' reaching up to ∼ 0.2%/dpa at very high dpa. We also show that f v ' can be predicted based on a physical model of defect partitioning between evolving sinks. At 500°C and fusion relevant He/dpa ≈ 10, the best-fit model predicts nominal swelling, S = f v /(1-f v), of ∼ 1.1, 4.9 and 16% at 50, 100 and 200 dpa, respectively. The physically motivated, data-driven model includes estimated uncertainties for both dpa i and f v '. [ABSTRACT FROM AUTHOR]

Life extension of light water reactors requires robust models to predict the embrittlement of reactor pressure vessel (RPV) steels under long-term neutron irradiation. Embrittlement is due to nanoscale precipitation hardening by phases containing Cu, Mn, Ni, and Si, resulting in increases of the ductile to brittle transition temperature. Embrittlement data for low flux, high fluence extended life conditions, up to 80 years or more, are largely not available. Thus, higher flux, accelerated test reactor irradiations have been used to help develop models to predict low flux embrittlement at high fluence. Here flux, or dose rate, is expressed in units of displacements per atom per second (dpa/s). The dose rate can significantly influence precipitate evolution in a way that depends on fluence (dpa), temperature, and alloy composition, as well as flux itself. Here, we explore precipitation in surveillance steels with varying compositions at high fluxes (10−5–10−6 dpa/s) produced using 70 MeV Fe2+ ion irradiations. Atom probe tomography was used to characterize the dose dependence of precipitation at very high ion irradiation dose rates, and to evaluate corresponding similarities or differences compared to neutron irradiated steels at a much lower dose rate of ≈ 5 × 10−9 dpa/s. The data show that, on average, the ion irradiation precipitate volume fractions increase by factors of ∼ 1.5 to 2 between 0.3 dpa and 1.2 dpa. Limited data show that the major effect of neutron versus ion irradiation is the former has lower precipitate number densities and larger sizes. Otherwise, the precipitates are remarkably similar in composition and volume fraction. [ABSTRACT FROM AUTHOR]

• Developing computational methods that accounts for changes in material properties in fusion structures as function of several radiation parameters and temperature simultaneously. • Effect of gradients in the irradiation fields variables and swelling on stress state. • Prediction of various ways a large fusion structure can deform as ages in fusion reactor. • Evolution of stresses and accumulation of plastic strain as function of neutron irradiation dose. • Effect of boundary conditions on stress state, deformation and dimensional stability modes. We assess the effects of neutron irradiation on the deformation and stress evolution of large-scale fusion energy structures. This is accomplished through non-linear finite element structural analysis of the coupled thermal and mechanical fields at the Beginning-Of-Life (BOL), at 45 dpa, and at 90 dpa. Radiation effects include volumetric swelling and the influence of radiation on the mechanical properties. The system studied here is a large section of a full inboard module of an integrated structure comprising the First Wall and Blanket (FW/B) of a Dual Cooled Lithium-Lead (DCLL) energy conversion unit in the Fusion Nuclear Science Facility (FNSF). The structural material is the ferritic/martensitic steel F82H. We analyze several radiation effects phenomena that can lead to significant impact on the mechanical design and lifetime of the structure. These include volumetric swelling effects on the assembly and disassembly of modules and the impact of spatial gradients in neutron damage and helium generation on deformation, stress evolution, and plastic strain accumulation. We show that the stress state is strongly influenced by the accumulation of swelling strains, radiation hardening and softening, and by spatial gradients in displacement damage and helium gas generation. Several key regions in the FW/B structure are identified where severe plastic strains accumulate and may be potential sites for failure, especially during cyclic reactor operations. We finally show that minimum gaps between Inboard (IB) blanket sectors must be present during assembly so as to avoid excessive stress and strain in FW/B modules critical regions and raising chances of failure. A range of structural displacements are shown, from as low as 4 mm at BOL for free side walls to as high as 46 mm at 90 dpa for fully constrained side walls. [ABSTRACT FROM AUTHOR]

We have investigated magnetic properties for reactor pressure vessel model alloys with variable Cu contents, subjected to neutron irradiation up to a fluence of 9 × 10 19 n cm − 2. Unlike a monotonic increase of microhardness with neutron fluence, the major-loop coercivity decreases at a higher fluence and the decrease becomes larger for the alloy containing a higher amount of Cu. The measurements of first-order reversal curves (FORCs) for the high-Cu alloy show that the position of the FORC distribution peak shifts toward a lower coercivity just after neutron irradiation, followed by a slight increase, associated with the broadening along both the coercivity and interaction field axes. The results can be explained by the enhancement of magnetic inhomogeneity in a matrix due to Cu precipitation and an increasing magnetostatic interaction between local magnetic regions with different coercivity. The magnetic method using FORCs can be a possible technique which provides in-depth information on microstructural changes due to neutron irradiation, which is not obtained by measurements of a conventional major hysteresis loop. [ABSTRACT FROM AUTHOR]

Embrittlement of light water reactor pressure vessel (RPV) steels by fast neutron irradiation may limit extended nuclear plant life. Embrittlement, which is manifested as increases in various indexes of a ductile to brittle transition temperatures (ΔT), is primarily due to hardening by nanoscale precipitates containing Cu, Ni, Mn, and Si, which form under irradiation. In addition to these elements, P has also been found to play a role in embrittlement. While only slightly enriched in the precipitates, hardening and embrittlement increase with trace P concentrations in low-Cu steels. Here, we characterize the individual and synergistic irradiation precipitation and hardening mechanisms in a series of RPV steels containing no to low-Cu and with systematic variations in Ni and P. The steels were irradiated to a fluence of ∼ 1.38×1020 n/cm2 at ∼ 292 °C in the UCSB ATR-2 experiment. In nominally Cu-free medium and high-Ni RPV steels, atom probe tomography shows that P and Ni promote precipitation of P-Mn-Si-Ni and Mn-Si-Ni precipitates, respectively. The precipitate microstructure correlates with the observed irradiation hardening. [ABSTRACT FROM AUTHOR]

The synergism of transmutant helium and irradiation defects is critically important to understand the performance of SiC when in service in nuclear environments. In this study, we exposed 3C-SiC in contact with a 2 μm Ni foil to neutron irradiation at 500 °C to 29 dpa in the high flux isotope reactor to simulate the simultaneous introduction of helium and irradiation defects into SiC. The combination of TEM observations and thermal desorption measurements helps to elucidate the impact of helium on the microstructural evolution in 3C-SiC. Thermal helium desorption spectra from ion-implanted and neutron-irradiated SiC showed a completely different desorption behavior in terms of the peak position and helium desorption flux. The identification of possible helium trapping sites was attempted by applying the first order dissociation model to the measured thermal helium desorption spectra. TEM observations of the neutron-irradiated samples showed that the presence of helium facilitated the stabilization of the defect clusters and promoted the formation of visible helium bubbles in SiC subject to simultaneous neutron irradiation and in-situ He implantation. Following the subsequent heat treatment during the thermal desorption measurements, large faceted helium bubbles were found along grain boundaries in the neutron-irradiated SiC with in-situ He implantation, while the helium bubbles in the grain interior were relatively smaller than those found in the neutron-irradiated sample without in-situ He implantation due to the reduced mobility of He-defect clusters. The He contents contained in the neutron-irradiated samples were quantified based on the experimental data from TEM and thermal desorption measurements. [ABSTRACT FROM AUTHOR]