This work presents the results of comparative studies using complementary methods, such as scanning electron microscopy (SEM), X-ray photoemission spectroscopy (XPS), and thermal desorption spectroscopy (TDS) to investigate the local surface morphology and chemistry of flower-like ZnO nanostructures synthesized by the thermal oxidation technique on native Si/SiO2 substrates. SEM studies showed that our flower-like ZnO nanostructures contained mostly isolated and irregular morphological low-dimensional forms, seen as rolled-up floss flowers, together with local, elongated, complex stalks similar to Liatris flowers, which contained joined short flosses in the form of nanodendrites. Beyond this, XPS studies showed that these nanostructures exhibited a slight surface nonstoichiometry, mostly related to the existence of oxygen-deficient regions, combined with strong undesired C surface contamination. In addition, the TDS studies showed that these undesired surface contaminations (including mainly C species and hydroxyl groups) are only slightly removed from the surface of our flower-like ZnO nanostructures, causing an expected modification of their nonstoichiometry. All of these effects are of great importance when using our flower-like ZnO nanostructures in gas sensor devices for detecting oxidizing gases because surface contamination leads to an undesired barrier for toxic gas adsorption, and it can additionally be responsible for the uncontrolled sensor aging effect. [ABSTRACT FROM AUTHOR]

Novel insight on the local surface properties of ZnO nanowires (NW) deposited by the evaporation-condensation method on Ag-covered Si substrates is proposed, based on the results of comparative studies by using the scanning electron microscopy (SEM), x-ray photoemission spectroscopy (XPS) and thermal desorption spectroscopy (TDS) methods, respectively. SEM studies showed that ZnO nanowires (nanoribbons) are mostly isolated and irregular, having the average length μm and the average at the level of tens nm, respectively. Our XPS studies confirmed their evident surface non-stoichiometry, combined with strong C surface contaminations, which was related to the existence of oxygen-deficient regions. Additionally, TDS studies showed that undesired surface contaminations (including C species and hydroxyl groups) on the surface of ZnO NWs can be removed almost completely, leading to an increase of the final non-stoichiometry. Both effects are of great importance when using ZnO NWs for the detection of oxidizing gases, because the undesired C contaminations (including C–OH species) play the role of undesired barriers for the gas adsorption, especially at the low working temperature, additionally affecting the uncontrolled sensor ageing effect. [ABSTRACT FROM AUTHOR]