The urinary bladder is an organ which facilitates the storage and release of urine. The bladder can develop tumours and bladder cancer is a common malignancy throughout the world. There is a consensus that there are differences in the mechanical properties of normal and malignant tissues. However, the viscoelastic properties of human bladder tumours at the macro-scale have not been previously studied. This study investigated the viscoelastic properties of ten bladder tumours, which were tested using dynamic mechanical analysis at frequencies up to 30Hz. The storage modulus ranged between 0.052MPa and 0.085MPa while the loss modulus ranged between 0.019MPa and 0.043MPa. Both storage and loss moduli showed frequency dependent behaviour and the storage modulus was higher than the loss modulus for every frequency tested. Viscoelastic properties may be useful for the development of surgical trainers, surgical devices, computational models and diagnostic equipment., (Copyright © 2016 Elsevier Ltd. All rights reserved.)

The aim of this study was to measure the viscoelastic properties of bladder tissue. Porcine bladders were dissected into rectangular strips and loops. Dynamic Mechanical Analysis was used to measure the viscoelastic properties of the bladder tissue (storage and loss stiffness) tested in a frequency range of up to 10 Hz. Storage stiffness was found to be consistently higher than loss stiffness. Average storage stiffness was found to be 1.89 N/mm and 0.74 N/mm for looped and rectangular samples, respectively. Average loss stiffness was found to be 0.24 N/mm and 0.11 N/mm for looped and rectangular samples, respectively. The results of this study are important for computational modelling of the bladder and for ensuring that engineered bladder tissues have physiological viscoelastic properties., (Copyright © 2014 Elsevier Ltd. All rights reserved.)