Search

In this work, chopped carbon fibers (CCFs) with different lengths were added to graphite/polypropylene (PP) composite materials to achieve high conductivity and flexural strength performances, which are required for use in proton exchange membrane fuel cells. The effects of CCF length (2–4 mm), CCF content (0–5 wt.%), graphite type‐natural flake graphite (NFG) and synthetic graphite (SG), and graphite particle size (18–106 µm) on the graphite/PP/CCFs composites are examined. The conductivities of the composites decrease significantly with increasing CCF length above 3 wt.%. CCFs improve the composite's strength, with a maximum strength of 45.8 MPa being achieved with 5 wt.% of 4 mm long CCFs. Composite with NFG exhibits superior conductivity to the one with SG but lacks flexural strength. The NFG particle size significantly affects the conductivity of the composite at high graphite contents, with a particle diameter of 75 µm resulting in maximum conductivity. An optimal composition with 38 µm/82 wt.% NFG and 2 mm/3 wt.% CCF, electrical conductivity, and flexural strength of 189.4 S/cm and 30.2 MPa, respectively, were achieved. Also, this composite exhibited interfacial contact resistance 2.52mΩ·cm2$2.52\;{\rm{m}}\Omega \cdot {\rm{c}}{{\rm{m}}^{\rm{2}}}$ and contact angles of 111°, which showed favorable interfacial conductivity and hydrophobicity performances. [ABSTRACT FROM AUTHOR]

An in-depth understanding of the local mass transport process is essential for precisely regulating the catalyst layer structure in fuel cells. The ionomer on the Pt surface in the catalyst plays a crucial role in the local transport of oxygen and protons. While most models assume that Pt is completely covered by ionomer, experiments have indicated that Pt is partially covered by ionomer in some cause. In this paper, an improved local mass transport model is proposed to investigate the effect of ionomer coverage on internal mass transport process and fuel cell performance. The results show that the current density first increases and then decreases as the ionomer coverage rises from 10% to 90% under 0.6 V. The optimal performance is achieved with a coverage of 40%. Oxygen is more easily transported in water, while ionomer is a better proton conductor. Variations in ionomer coverage lead to different distances for oxygen and proton transfer, which have an important effect on reactant concentration. Furthermore, further study reveals that the current density is greatest at the interface between water and ionomer. Increasing the interface can effectively reduce the comprehensive transport distance of reactants in ionomer and water to improve performance, which is more pronounced than increasing the oxygen transfer coefficient in the ionomer. Overall, this study provides new ideas for the design of high-performance catalyst layers. • An improved fine-structure model of local mass transport in CCL is developed. • Simulate the effect of local oxygen and proton transport on cell performance. • The best cell performance is obtained with an ionomer coverage of 40% under 0.6 V. • Increasing the ionomer/water interface can significantly improve cell performance. • Increasing interface is more effective than enhancing oxygen diffusion in ionomer. [ABSTRACT FROM AUTHOR]