Search

The aim was to evaluate the shear strength by extrusion and check the type of fiberglass pin failure who received different surface treatments to test the Single Bond Universal® multi-purpose adhesive (3M ESPE). Eighty bovine incisors with endodontic treatment were randomly divided into four groups. Group I: the pins received application of silane; Group II: no treatment; Group III: Silane and Adhesive; And Group IV: adhesive only. The groups were submitted to thermal cycling for 5,000 cycles, the roots were sectioned and submitted to the push out test. With the silanization and the application of the adhesive, the resistance between the fiberglass pin and the dentin of any of the root thirds was significantly lower. The silane-adhesive association caused significant damage to the adhesion. Silanization alone constituted the treatment that improved adhesion. Adhesive defects were the most prevalent. El objetivo fue evaluar la resistencia al cizallamiento por extrusión y verificar el tipo de falla de postes de fibra de vidrio que han recibido diferentes tratamientos de superficie, y testar el adhesivo multiuso Single Bond Universal® (3M ESPE). Métodos: Ochenta incisivos bovinos con tratamiento endodóntico fueran aleatoriamente repartidos en cuatro grupos; Grupo I: los postes recibieron aplicación de silano; Grupo II: ningún tipo de tratamiento; Grupo III: silano y adhesivo; y Grupo IV: solamente adhesivo. Los grupos fueran sometidos a ciclaje térmico por 5.000 ciclos, las raíces seccionadas y sometidas al teste push out. Resultados: Con la silanización y la aplicación del adhesivo, la resistencia entre el poste de fibra de vidrio y la dentina ha sido significativamente menor en relación solamente la silanización. La asociación silano-adhesivo causó perjuicio a la unión. Conclusiones: La silanización por si solo es que se constituyó en el tratamiento que mejoró la resistencia unión. Fallas adhesivas fueran las más prevalentes. O objetivo foi avaliar a resistência ao cisalhamento por extrusão e verificar o tipo de falha do pino de fibra de vidro que recebeu diferentes tratamentos superficiais para testar o adesivo multiuso Single Bond Universal® (3M ESPE). Oitenta incisivos bovinos com tratamento endodôntico foram divididos aleatoriamente em quatro grupos. Grupo I: os pinos receberam aplicação de silano; Grupo II: sem tratamento; Grupo III: Silano e Adesivo; E Grupo IV: somente adesivo. Os grupos foram submetidos à ciclagem térmica por 5.000 ciclos, as raízes foram seccionadas e submetidas ao teste de push out. Com a silanização e a aplicação do adesivo, a resistência entre o pino de fibra de vidro e a dentina de qualquer um dos terços radiculares foi significativamente menor. A associação silano-adesivo causou danos significativos à adesão. A silanização sozinha constituiu o tratamento que melhorou a adesão. Defeitos adesivos foram os mais prevalentes.

Fiberglass pins or fused metal cores are used in dentistry as intraradicular retainers and have the main purpose of replacing the lost dental structure, in addition to facilitating the support and retention of the crown. The purpose of the review was to analyze the literature in relation to the comparison between fiber pins and fused metal cores. An integrative literature review was developed in the SciELO and LILACS databases, using the descriptors: “Mouth Rehabilitation”, “Dental pins” and “Post and Core Technique” individually and then the crossing with the Boolean operator AND. The inclusion criteria used in the selection of articles were: articles published in Portuguese available in full that portrayed the problem researched, articles published and indexed in the referred databases in the last fifteen years (2005 to 2020). Twenty articles were found and from them it was verified that the use of fused metal cores is decreasing, due to the success of aesthetic pins. Root fracture is less in teeth restored with fiberglass pins due to the better distribution of forces. Despite this, it is a fact that both fused metal cores and fiberglass pins have good results when used correctly, but fiberglass pins have greater resistance to fracture. Further studies can be done with several brands in use in the market, to better guide the dentist about the materials in use. Los pines de fibra de vidrio o núcleos de metal fundido se utilizan em odontología como retenedores intrarradiculares y tienen el propósito principal de reemplazar la estructura dental perdida, además de facilitar el soporte y retención de la corona. El propósito de la revisión fue analizar la literatura em relación a la comparación entre pines de fibra y núcleos de metal fundido. Se desarrolló una revisión integradora de la literatura em las bases de datos SciELO y LILACS, utilizando los descriptores: “Rehabilitación Bucal”, “Pins Dentales” y “Técnica de Perno Muñón” individualmente y luego el cruce conel operador booleano AND. Los criterios de inclusión utilizados em la selección de artículos fueron: artículos publicados em português disponibles em su totalidad que retrataran el problema investigado, artículos publicados e indexados em las referidas bases de datosenlos últimos quinceaños (2005 a 2020). Se encontraron veinte artículos y de ellos se comprobó que el uso de núcleos de metal fundido está disminuyendo, debido al éxito de los pines estéticos. La fractura de laraíz es menor em los dientes restaurados conpasadores de fibra de vidrio debido a la mejor distribución de fuerzas. A pesar de esto, es unhecho que tanto los núcleos de metal fundido como los pines de fibra de vidrio tienen buenos resultados cuando se usan correctamente, pero los pines de fibra de vidrio tienen una mayor resistencia a la fractura. Se pueden realizar más estudios con varias marcas en uso en el mercado, para orientar mejor al dentista sobre los materiales en uso. Os pinos de fibra de vidro ou núcleos metálicos fundidos são utilizados na odontologia como retentores intrarradiculares e tem como principal intuito repor a estrutura dental que foi perdida, além de facilitar o suporte e a retenção da coroa. A revisão teve por objetivo analisar a literatura em relação à comparação entre os pinos de fibra e os núcleos metálicos fundidos. Foi desenvolvida uma revisão integrativa da literatura nas bases de dados SciELO e LILACS, utilizando os descritores: “Reabilitação bucal”, “Pinos dentários” e “Técnica para retentor intrarradicular” individualmente e em seguida o cruzamento com o operador booleano AND. Os critérios de inclusão utilizados na seleção dos artigos foram: artigos publicados em português disponíveis na íntegra que retratassem o problema pesquisado, artigos publicados e indexados nos referidos bancos de dados nos últimos quinze anos (2005 a 2020). Foram encontrados 20 artigos e a partir deles verificado que o uso de núcleos metálicos fundidos está diminuindo, devido ao sucesso dos pinos estéticos. A fratura radicular é menor em dentes restaurados com pinos de fibra de vidro devido à melhor distribuição de forças. Apesar disso, é fato que tanto os núcleos metálicos fundidos quanto os pinos de fibra de vidro apresentam bons resultados quando utilizados corretamente, mas os pinos de fibra de vidro apresentam maior resistência à fratura. Mais estudos podem ser feitos com diversas marcas em uso no mercado, para guiar melhor o cirurgião-dentista sobre os materiais em uso.