Search

[Display omitted] • Ternary PSCs were fabricated with PBDB-TF as third component materials. • The improvement of charge dynamics process of ternary photoactive layer by ternary strategy. • The improved exciton-dissociation at the donor–blend acceptor interface. In this manuscripts, a ternary polymer solar cells (PSCs) are fabricate with two "D18-series" donor (D18-Cl and D18) as blend donor and T6 as acceptor. The effects of D18-Cl and D18 in ternary PSC on the film morphology, photoelectronic properties and charge carrier dynamics were systematically investigated. By finely adjusting the D18 content, a power conversion efficiency (PCE) of 16.66 % is achieved in the optimized ternary PSCs with 35 wt% D18 in donor, resulting from significantly improved short-circuit-current density (J SC) of 26.80 mA cm−2 in comparison with those of D18-Cl:Y6 binary PSCs. The J SC of ternary PSCs monotonously increase along with the incorporation of D18, indicating that D18 is comprehensively optimal short wavelength photon harvesting compared with D18-Cl. Both D18-Cl and D18 are shown similar highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) energy levels, which is beneficial to efficient charge transport at the blend donor domain. Our work indicates that the blend of D18-Cl and D18 as blend donor and Y6 as electron acceptor to boost photovoltaic performance in the ternary PSCs. [ABSTRACT FROM AUTHOR]

Photo-annealing treatment has successfully been demonstrated in organic solar cells (OSCs) with solution-processable titanium (diisopropoxide) bis(2,4-pentanedionate) (TIPD) as an electron extraction layer; this process was shown without thermal annealing treatment. The power conversion efficiency (PCE) is quite low in the initial stage, though it dramatically increases following constant light illumination and reaches a saturated state after 9 min of light illumination. X-ray photoelectron spectroscopy (XPS), Fourier transform infrared (FTIR) and ultraviolet photoemission spectroscopy (UPS) were used, and they showed that the TIPD molecules decomposed and formed stable Ti O bonds. According to photocurrent density-effective voltage curve (J ph - V eff), short-circuit current density (J SC) and open-circuit voltage (V OC) value under different light intensity, the photo-annealed TIPD-based OSCs showed efficient charge transport and suppressed charge recombination. Thus, after a fresh TIPD solution was spin-coated onto the indium tin oxide (ITO) surface and photo-annealed for 9 min, the OSCs showed the highest photovoltaic performance compared to ZnO-based OSCs. [Display omitted] [ABSTRACT FROM AUTHOR]

α-Formamidinium lead iodide (α-FAPbI 3) has become one of the most promising candidate materials for stable perovskite solar cells (PSCs) owing to their outstanding optoelectronic properties and high thermal stability. The crystallinity of the active layer of perovskite is essential to the performance of perovskite solar cells. In this paper, we added lead acetate Pb(Ac) 2 as a grain growth agent into the perovskite precursor solution to prepare high-efficiency and stable perovskite solar cells. It was revealed that the crystals of Pb(Ac) 2 -modified film grew selectively along the [200] direction and that the FAPbI 3 active layer grains were arranged neatly and densely, due to the significant influence of a moderate amount of weakly acidic Ac- on the crystal growth of FAPbI 3. The relative reduction in its grain boundaries led to the decrease in the grain boundary impedance, and it was easier for electrons to perform long-range migration in the perovskite active layer. The beneficial effects of Pb(Ac) 2 were further expiored by femtosecond Fs-TA measurements and density of states (tDOS) analysis, where the carrier lifetimes τ 2 was increased from 482.4 ps to 1340 ps, and the trap density of film states was significantly reduced. The filling factor (FF) and power conversion efficiency (PCE) were increased from 76.5% and 19.7–81.1% and 21.8%, respectively, the Pb(Ac) 2 devices were placed in air for 800 h for the light aging test, and the test results still maintained 90% of the original efficiency, which improved the stability of FAPbI 3 crystals. • Pb(Ac) 2 as an additive to modulate the crystalline quality of perovskite active layer films. • Perovskite solar cell defect reduction and carrier lifetime increase by Pb(Ac) 2 modification. • The Pb(Ac) 2 -modified active layer grains have preferential orientation and orderly arrangement. • 81.1% filling factor and 21.8% efficiency are achieved for a single PSC cell with excellent stability. [ABSTRACT FROM AUTHOR]