Search

Reducing the self-heating of SiC- and GaN/SiC-based high-powered devices by integrating diamond films offers promising performance enhancement of these devices. However, such a reduction strategy faces serious problems, such as diamond nucleation on SiC and stress accumulation greater than 10 GPa. In this work, a SiN x dielectric layer (∼50 nm) was coated onto the C polar face of a 4H–SiC wafer using microwave plasma chemical vapor deposition (MPCVD) to improve direct dense diamond nucleation and growth, significantly reduce the stress, and build Si–C(SiC)⋯Si⋯C(diamond) bond bridges. This SiN x thin layer, prepared by activating Si ions under Ar/N plasma during magnetron sputtering, gave rise to local Si 3 N 4 crystal features and a low effective work function (EWF) for promoting surface dipoles with electronegative carbon-containing groups. In the H plasma environment during diamond growth, the local Si 3 N 4 crystal was amorphized, and the N atoms escaped as a result of atomic H and the high temperature. At the same time, C atoms diffused into the SiN x and formed C–Si bonds (49.7% of the total C bonds) by replacing N–Si and Si–Si, thus increasing the direct nucleation density of the diamond grains. The diamond thin film grew rapidly and uniformly, with a grain size of approximately 2 μm in mixed orientation, and the stress of the 2-inch SiC-on-diamond wafer was extremely low (to ∼0.1–0.2 GPa). In comparison, partially connected diamond grains (>10 μm) on the bare SiC in the preferential (110) orientation resulted in a film with twin-grain features and significant stress, which was associated with the hexagonal lattice interface of 4H–SiC. These results are considered the material and surface/interface bases for actively controlling wafer fabrication and enhancing the heat dissipation of SiC and GaN/SiC electronics. [ABSTRACT FROM AUTHOR]

Electronic and mechanical properties, and their biocompatibility, make diamond-based materials promising biomedical applications. The cost required to produce high quality single crystalline diamond films is still a hurdle to prevent them from commercial applications, but the emergence of polycrystalline diamond (PCD) films grown by chemical vapour deposition (CVD) method has provided an affordable strategy. PCD films grown on silicon wafer have been used throughout and were fully characterised by SEM, XPS, Raman spectroscopy and FTIR. The samples contain nearly pure carbon, with impurities originated from the CVD growth and the silicon etching process. Raman spectroscopy revealed it contained tetrahedral amorphous carbon with small tensile stress. The sp2 carbon content, comprised between 16.1 and 18.8%, is attributed to the diamond grain boundaries and iron-catalysed graphitisation. Antibacterial properties of PCD films were performed with two model bacteria, i.e. Escherichia coli (Gram-negative) and Staphylococcus aureus (Gram-positive) using direct contact and shaking flask methods. The samples showed strong bacteriostatic properties against S. aureus and E. coli with the direct contact method and no influence on planktonic bacterial growth. These results suggest that the bacteriostatic mechanism of PCD films is linked to their surface functional groups (carbon radicals and –NH 2 and –COOH groups) and that no diffusible molecules or components were involved. [ABSTRACT FROM AUTHOR]