Search

Reducing the self-heating of SiC- and GaN/SiC-based high-powered devices by integrating diamond films offers promising performance enhancement of these devices. However, such a reduction strategy faces serious problems, such as diamond nucleation on SiC and stress accumulation greater than 10 GPa. In this work, a SiN x dielectric layer (∼50 nm) was coated onto the C polar face of a 4H–SiC wafer using microwave plasma chemical vapor deposition (MPCVD) to improve direct dense diamond nucleation and growth, significantly reduce the stress, and build Si–C(SiC)⋯Si⋯C(diamond) bond bridges. This SiN x thin layer, prepared by activating Si ions under Ar/N plasma during magnetron sputtering, gave rise to local Si 3 N 4 crystal features and a low effective work function (EWF) for promoting surface dipoles with electronegative carbon-containing groups. In the H plasma environment during diamond growth, the local Si 3 N 4 crystal was amorphized, and the N atoms escaped as a result of atomic H and the high temperature. At the same time, C atoms diffused into the SiN x and formed C–Si bonds (49.7% of the total C bonds) by replacing N–Si and Si–Si, thus increasing the direct nucleation density of the diamond grains. The diamond thin film grew rapidly and uniformly, with a grain size of approximately 2 μm in mixed orientation, and the stress of the 2-inch SiC-on-diamond wafer was extremely low (to ∼0.1–0.2 GPa). In comparison, partially connected diamond grains (>10 μm) on the bare SiC in the preferential (110) orientation resulted in a film with twin-grain features and significant stress, which was associated with the hexagonal lattice interface of 4H–SiC. These results are considered the material and surface/interface bases for actively controlling wafer fabrication and enhancing the heat dissipation of SiC and GaN/SiC electronics. [ABSTRACT FROM AUTHOR]

[Display omitted] • The La-doped Er 2 O 3 anti-reflection films was prepared by the power of magnetron sputtering. • The compound of La 2 O 3 formed along the grain boundary of the columnar crystal structure of the polycrystalline film. • The highest hardness and yield strength of the La-doped Er 2 O 3 film was two times higher than that of pure Er 2 O 3 film. • The transmittance of the La-doped Er 2 O 3 anti-reflection films only decreased 1% after erosion. The composition and microstructure consisting of anti-reflection films was obtained by the power of magnetron sputtering. X-ray photoelectron spectroscopy (XPS) and High-resolution transmission electron microscopy (HRTEM) provided evidence to support that the doping La element exists as oxide in the grain boundaries of the matrix Er 2 O 3 films. The undoped and La-doped Er 2 O 3 films show a columnar crystal structure of the main cubic (2 2 2) plane. Twinning and a large number of dislocations show up in the undoped Er 2 O 3 films due to the competitive growth of the columnar crystal. In addition, the La-doped Er 2 O 3 films show a lower roughness (RMS) value in comparison with undoped Er 2 O 3 films. The grain size of columnar crystals decreases significantly with increasing La concentration in the La-doped Er 2 O 3 films. The fine grains resulted in the La-doped Er 2 O 3 films developing high mechanical and impact resistance properties, with an increase in hardness from 12.6 ± 2.1 GPa to 26.1 ± 3.4 GPa and the eroding area rate decreasing from 38.9 % to 1.9 %. Moreover, the La-doped Er 2 O 3 anti-reflection films on the chemical vapor deposition (CVD) diamond substrate maintained 74 % transmittance in the long-wavelength infrared range of 8–12 μm after sand eroding. [ABSTRACT FROM AUTHOR]