Search

We demonstrate the structure, spectroscopy, and laser performance of an Er3+ and Pr3+ co-doped LuYSGG crystal grown by the Cz method. The XRD result shows that it belongs to the cubic system with the space group Ia3¯d. A refractive index curve in the range of 320–3000 nm is obtained by fitting the Sellmeier equation. The lifetimes of the 4I13/2 and 4I11/2 levels are 0.871 and 0.728 ms, and the ratio is reduced obviously from 3.4 to 1.2 due to the doping of deactivator Pr3+. In CW mode, a maximum output power of 1059 mW is achieved with a slope efficiency of 17.58% and laser center wavelength of ∼2.8 μm. Beam quality factors of 1.40/1.34 are achieved. The results suggest that the Er,Pr:LuYSGG crystal is a potential candidate for generating a high-power mid-infrared laser and can be applied in irradiation environments. [ABSTRACT FROM AUTHOR]

We demonstrate the temperature distribution, optical and laser performances of a YAP/Tm:YAP/YAP composite crystal fabricated by thermal bonding technology. The thermal distribution simulations show that the bonded crystal possesses a higher thermal dissipation efficiency than that of the unbonded one. The wavefront distortion of the bonded YAP/Tm:YAP crystal is close to the unbonded Tm:YAP, indicating a high bonding quality. The optical transmission spectra and absorption loss suggest that the bonding region is a uniform transition and almost without scattering interface. Moreover, compared with the un-bonded Tm:YAP crystal, a maximum average output power of 41.2 W and slope efficiency of 49.5% are achieved on the bonded crystal, which are increased by 28.4% and 21.0%, respectively. Therefore, the 1.94 μm laser performance can be effectively improved by combining pure YAP crystals on the Tm:YAP crystal as end-caps. [ABSTRACT FROM AUTHOR]

In this study, we demonstrate the laser performance of LD end-pumped LuYSGG/Er:LuYSGG composite crystal. Thermal distribution simulations by varying the pump spot size indicate that the suitable pump power density is a key factor affecting the laser performance, which is consistent with the experimental result. The maximum output power and slope efficiency achieved were 1266 mW and 24.3% in CW mode, which increased by 39.3% and 12.5%, respectively, compared with unbonded Er:LuYSGG crystal. The laser wavelength location was at 2797.6 nm, and the power fluctuation was about 5.1%. Moreover, the beam quality factors Mx2 and My2 improved to 1.33 and 1.42 from 1.78 and 1.83, respectively. The results suggested that an LD end-pumped LuYSGG/Er:LuYSGG composite crystal with a high beam quality can be applied as a seed source in the mid-infrared (MIR) multi-stage amplification laser apparatus. [ABSTRACT FROM AUTHOR]

Future energy systems must call upon clean and renewable sources capable of reducing associated CO 2 emissions. The present research opens new perspectives for renewable energy-based hydrogen production by water splitting using metal oxide oxidation/reduction reactants. An earlier multicriteria assessment defined top priorities, with MnFe 2 O 4 /Na 2 CO 3 /H 2 O and Mn 3 O 4 /MnO/NaMnO 2 /H 2 O multistep redox cycles having the highest potential. The latter redox system was previously assessed and proven difficult to be conducted. The former redox system was hence experimentally investigated in the present research at the 0.5 to 250 g scale in isothermal thermogravimetry, an electrically heated furnace, and a concentrated solar reactor. Over 30 successive oxidation/reduction cycles were assessed, and the H 2 production efficiencies exceeded 98 % for the coprecipitated reactant after these multiple cycles. Tentative economics using a coprecipitated reactant revealed that 120 cycles are needed to achieve a 1 € per kg H 2 cost. Improving the cheaper ball-milled reactant could reduce costs by approximately 30 %. The initial results confirm that future research is important., Competing Interests: There are no conflicts to declare., (This journal is © The Royal Society of Chemistry.)