This paper focuses on the self-synchronization control of cascaded-type STATCOM. One module is controlled as the current source, and the rest are regulated as voltage sources. The low-bandwidth communication is just used to transmit the given reactive powers. Via the carrier of common grid current acquired locally, the self-synchronized operation of all modules is realized. When a short interruption in communication occurs, the stable operation of the system is unaffected. Thus, the system reliability is improved in case of communication failure. The small-signal stability of the proposed scheme is proven. Finally, the effectiveness of the proposed scheme is verified by both simulation and hardware-in-the-loop results. [ABSTRACT FROM AUTHOR]

Ti-15Nb-25Zr-(0, 4, 8)Fe (mol.%) alloys were prepared via spark plasma sintering (SPS) for 10 min at 800, 1000, and 1200 °C to study the effect of sintering temperatures and Fe content on the mechanical properties of alloys. The main phase of the alloys sintered at 800 °C is α phase. When the temperature is increased to 1000 and 1200 °C, the alloys are mainly β phase. Raising the sintering temperature can promote the diffusion of elements. Therefore, high strength and high plasticity are obtained in the alloys sintered at high temperature. The compressive strength of Ti-15Nb-25Zr sintered at 1200 °C is 1604 MPa, and the fracture strain is around 35%. The strength and plasticity are influenced by the complex effects of elemental diffusion, grain boundary and solid-solution strengthening. Adding Fe can improve the diffusion of elements, promote the formation of β grains and supply solid-solution strengthening effect. As the sintering temperature is increased, the compressive strength of Ti-15Nb-25Zr-4Fe shows an increasing trend and the plasticity is almost not changed. The Fe content is excessive in Ti-15Nb-25Zr-8Fe, which leads to some disadvantages including intermetallic compounds formation and grain boundary coarsening. The mechanical properties of Ti-15Nb-25Zr-8Fe are not always better than those of Ti-15Nb-25Zr-4Fe. The compressive strength of Ti-15Nb-25Zr-8Fe shows an increasing trend and the plasticity firstly increases and then decreases when the temperature is raised from 800 up to 1200 °C. Although the sintering time of SPS is short, Ti-15Nb-25Zr-(4, 8)Fe sintered at 1000 °C and Ti-15Nb-25Zr-(0, 4)Fe sintered at 1200 °C show good combination of strength and plasticity. [ABSTRACT FROM AUTHOR]