Search

The effect of surface modification on enhancing the magnetic heating behavior of magnetic nano fluids were investigated, for this purpose Fe3O4 nanoparticles were synthesized using co-precipitation method and surface modification was done using citric acid, ascorbic acid, tetraethyl orthosilicate (TEOS), polyvinyl alcohol (PVA) and polyethylene glycol (PEG). Experimental heating tests using AC magnetic field were done in the frequency of 100 kHz and different magnetic field (H) intensities. Theoretically the specific absorption rate (SAR) in magnetic nano fluids is independent of nanoparticles concentration but the experimental results showed different behavior. The theoretical SAR value @ H = 12kA.m–1 for Nano fluids containing bare Fe3O4 nanoparticles was 11.5 W/g but in experimental tests the obtained value was 9.72 W/g for nano fluid containing 20,000 ppm of dispersed nanoparticles. The experimental SAR calculation was repeated for sample containing 10,000 ppm of nanoparticles and the results showed increase in experimental SAR that is an evidence of nanoparticles agglomeration in higher concentrations. The surface modification has improved the dispersion ability of the nanoparticles. The Ratio of SAR, experimental, 20000ppm to SAR, experimental, 10000ppm was 0.85 for bare Fe3O4 nanoparticles dispersion but in case of surface modified nanoparticles this ratio has increased up to 0.98 that shows lower agglomeration of nanoparticles as a result of surface modification, although on the other hand the surface modification agents were magnetically passive and so it is expected that in constant concentration the SAR for bare Fe3O4 nanoparticles to be higher than this variable for surface modified nanoparticles. At lower concentrations the dispersions containing bare Fe3O4 nanoparticles showed higher SAR values but at higher concentrations the surface modified Fe3O4 nanoparticles showed better results although the active agent amount was lower at them. Finally, it should be noted that the nanoparticles that were surface modified using polymeric agents showed the highest decrease in experimental SAR amounts comparing theoretical results that was because of the large molecules of polymers comparing other implemented surface modification agents. [ABSTRACT FROM AUTHOR]

Background: Electromagnetic induction hyperthermia is a promising method to treat the deep-seated tumors such as brain and prostatic tumors. This technique is performed using the induction of electromagnetic waves in the ferromagnetic cores implanted at the solid tumor. Objective: This study aims at determining the conditions of the optimal thermal distribution in the different frequencies before performing the in vitro cellular study. Material and Methods: In this experimental study, the i-Cu alloy (70.4-29.6; wt%) was prepared and characterized and then the parameters, affecting the amount of induction heating in the ferromagnetic core, were investigated. Self-regulating cores in 1, 3, 6, and 9 arrangements in the water phantom with a volume of 2 cm3 were used as a replacement for solid tumor. Results: Inductively Coupled Plasma (ICP) analysis and Energy Dispersive X-ray Spectroscopy (EDS) show the uniformity of the alloy after 4 times remeling by vacuum arc remelting furnace. The Vibrating Sample Magnetometer (VSM) shows that the Curie temperature (TC) of the ferromagnetic core is less than 50 °C. Temperature profile with a frequency of 100-400 kHz for 30 min, was extracted by infrared imaging camera, indicating the increase temperature in the range of 42 °C to 46 °C. Conclusion: The optimum conditions with used hyperthermia system are supplied in the frequency of 100 kHz, 200 kHz and 400 kHz with 6, 3 and 1 seeds, respectively. It is also possible to induce a temperature up to 50 °C by increasing the number of seeds at a constant frequency and power, or by increasing the applied frequency at a constant number of seeds. [ABSTRACT FROM AUTHOR]

As one of the most well-known metal nanoparticles, gold nanoparticles (AuNPs) have attracted much attention for the biological applications. This great interest in AuNPs can be attributed to their outstanding physical and chemical properties, such as special optical and electrochemical characteristics, high X-ray attenuation ability, strong X-ray absorption, photothermal effect, stability and biocompatibility. In addition, due to the ease of synthesis and modification of the surface of AuNPs, it is possible to control their shape, size and surface characteristics. All these features suggest that AuNPs can be used for biosensing strategies, drug delivery, photothermal therapy, nanobrachytherapy, enhanced radiotherapy and CT imaging. In addition, they can be used as antibacterial and antifungal agents. This minireview focuses on the key principles, research achievements and new opportunities in the synthesis of AuNPs as well as their biological applications. In fact, the growing progress in the use of AuNPs for the diagnostic and therapeutic applications is described in this survey. Overall, a better understanding of the key aspects of the synthesis methodologies will lead to the development of new protocols that can provide ideas for more cost-effective and reliable approaches to the production of AuNPs. [ABSTRACT FROM AUTHOR]

The effect of surface modification on enhancing the magnetic heating behavior of magnetic nano fluids were investigated, for this purpose Fe 3 O 4 nanoparticles were synthesized using co-precipitation method and surface modification was done using citric acid, ascorbic acid, tetraethyl orthosilicate (TEOS), polyvinyl alcohol (PVA) and polyethylene glycol (PEG). Experimental heating tests using AC magnetic field were done in the frequency of 100 kHz and different magnetic field (H) intensities. Theoretically the specific absorption rate (SAR) in magnetic nano fluids is independent of nanoparticles concentration but the experimental results showed different behavior. The theoretical SAR value @ H = 12kA.m -1 for Nano fluids containing bare Fe 3 O 4 nanoparticles was 11.5 W/g but in experimental tests the obtained value was 9.72 W/g for nano fluid containing 20,000 ppm of dispersed nanoparticles. The experimental SAR calculation was repeated for sample containing 10,000 ppm of nanoparticles and the results showed increase in experimental SAR that is an evidence of nanoparticles agglomeration in higher concentrations. The surface modification has improved the dispersion ability of the nanoparticles. The Ratio of SAR , experimental, 20000ppm to SAR , experimental, 10000ppm was 0.85 for bare Fe 3 O 4 nanoparticles dispersion but in case of surface modified nanoparticles this ratio has increased up to 0.98 that shows lower agglomeration of nanoparticles as a result of surface modification, although on the other hand the surface modification agents were magnetically passive and so it is expected that in constant concentration the SAR for bare Fe 3 O 4 nanoparticles to be higher than this variable for surface modified nanoparticles. At lower concentrations the dispersions containing bare Fe 3 O 4 nanoparticles showed higher SAR values but at higher concentrations the surface modified Fe 3 O 4 nanoparticles showed better results although the active agent amount was lower at them. Finally, it should be noted that the nanoparticles that were surface modified using polymeric agents showed the highest decrease in experimental SAR amounts comparing theoretical results that was because of the large molecules of polymers comparing other implemented surface modification agents., (© 2024. The Author(s).)

Increasing evidence suggests that the presence and spatial localization and distribution pattern of tumor infiltrating lymphocytes (TILs) is associate with response to immunotherapies. Recent studies have identified TGF β activity and signaling as a determinant of T cell exclusion in the tumor microenvironment and poor response to PD-1/PD-L1 blockade. Here we coupled the artificial intelligence (AI)-powered digital image analysis and gene expression profiling as an integrative approach to quantify distribution of TILs and characterize the associated TGF β pathway activity. Analysis of T cell spatial distribution in the solid tumor biopsies revealed substantial differences in the distribution patterns. The digital image analysis approach achieves 74% concordance with the pathologist assessment for tumor-immune phenotypes. The transcriptomic profiling suggests that the TIL score was negatively correlated with TGF β pathway activation, together with elevated TGF β signaling activity observed in excluded and desert tumor phenotypes. The present results demonstrate that the automated digital pathology algorithm for quantitative analysis of CD8 immunohistochemistry image can successfully assign the tumor into one of three infiltration phenotypes: immune desert, immune excluded or immune inflamed. The association between "cold" tumor-immune phenotypes and TGF β signature further demonstrates their potential as predictive biomarkers to identify appropriate patients that may benefit from TGF β blockade., (© 2022 Chinese Pharmaceutical Association and Institute of Materia Medica, Chinese Academy of Medical Sciences. Production and hosting by Elsevier B.V.)