As potential waste forms for immobilizing actinide‐rich radioactive wastes, Eu2Ti2O7 (Eu as a surrogate for minor actinides) pyrochlore glass‐ceramics were fabricated via hot isostatic pressing (HIPing) at 1200°C. The structure and microstructure at the reaction interface between the glass‐ceramic waste form and the stainless steel (SS) canister under HIPing conditions were carefully investigated with scanning electron microscopy (SEM), transmission electron microscopy (TEM), and synchrotron single crystal X‐ray diffraction (SC‐XRD). The interactions at the reaction interface led to the formations of a ~10‐µm‐thick Cr2O3 layer as the oxidation front of the SS and a layer of a mixed oxide phase (Eu1.25SiCr0.8Ti1.2O7.5) on the glass‐ceramic side of the reaction interface. The crystal structure of such a unique mixed oxide phase was revealed indubitably with a combination of synchrotron SC‐XRD and TEM assisted with a focused ion beam (FIB) SEM system. The improved structural understanding of the reaction interface will help to support the utilization of HIPing as a versatile hot consolidation process for the treatment of radioactive wastes. [ABSTRACT FROM AUTHOR]

[Display omitted] Pyrochlore glass ceramics have been fabricated via in-situ crystallization under reducing conditions by both sintering and hot isostatic pressing (HIPing) as candidate wasteforms for the acidic waste biproduct of Mo-99 radiopharmaceutical production. The tailored wasteform demonstrates flexibility in the wasteform design to receive the required waste variability, it also suitably passes high-level waste performance requirement, and successfully scales to 1 kg scale with 45 wt.% waste loading. U-rich pyrochlore as the major phase was confirmed by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy, with residual glass and minor secondary phases. The presence of both U4+ and U5+ valences in the wasteforms was revealed by diffuse reflectance spectroscopy. Addition of glass content had little influence on the pyrochlore composition but facilitated minor perovskite formation. The up-scaled dense, HIPed sample showed elemental releases of < 2 g/L for all elements in durability experiments. [ABSTRACT FROM AUTHOR]