Search

YScO 3 single crystal co-doped with Ho3+ and Pr3+ ions has been successfully grown by the Czochralaki method. The absorption spectrum, fluorescence spectrum and fluorescence decay curve were measured at room temperature. The absorption cross section of Ho,Pr:YScO 3 at 649 nm and 1130 nm was calculated to be 0.93 × 10−20 cm2 and 0.32 × 10−20 cm2, respectively. Judd-Ofelt (J-O) theory was performed to evaluate the spontaneous emission probabilities and the radiative lifetimes. Ho,Pr:YScO 3 exhibited strong emission at 2040 nm and 2890 nm with a emission cross section of 0.80 × 10−21 cm2 and 1.22 × 10−20 cm2, respectively. The fluorescence lifetime of the Ho3+:5I 6 and 5I 7 levels were calculated to be 0.31 ms and 5.89 ms, respectively. All the results indicate that the Ho,Pr:YScO 3 crystal could be a potential laser material for 2.9 μm laser operation. • Ho3+,Pr3+ co-doped YScO 3 was grown by the Czochralski method. • The crystal structure, absorption and emission spectra were investigated. • The effect of Pr3+ on the spectroscopic properties of Ho3+ was evaluated. [ABSTRACT FROM AUTHOR]

The polarization absorption spectra of Pr3+-doped GdScO 3 have been measured. Polarized emission spectra and fluorescence decay from the 3P 0 upper level have been investigated. The strongest absorption peaks are located at 448 nm for a, b and c polarization, the absorption cross sections are 1.29 × 10−20 cm2, 0.98 × 10−20 cm2 and 1.57 × 10−20 cm2, respectively. The maximum emission cross section is located at 662 nm, which is 18.55 × 10−20 cm2 (a polarization), 12.74 × 10−20 cm2 (b polarization) and 22.41 × 10−20 cm2 (c polarization), and the FWHM is 10.02 nm, 9.38 nm and 10.14 nm, respectively. The fluorescence lifetime of 3P 0 level is 12.39 μs. Those results indicated that Pr3+-doped GdScO 3 crystal grown by the Czochralski method is a potential laser medium for visible laser operation. •The spectra of Pr:GdScO 3 have been measured at room temperature. •Pr3+-doped GdScO 3 crystal is a potential laser medium for 662 nm laser. [ABSTRACT FROM AUTHOR]

A series of 0.5 at.% Tm:Ca 1-x Y x F 2+x (x = 0, 0.01, 0.04, 0.06, 0.08, 0.12) crystals have been successfully grown by the temperature gradient technique (TGT) method. The absorption spectra, fluorescence spectra, and fluorescence decay curves were measured and analyzed at room temperature. By comparison, it is found that when the concentration of Y3+ ions reaches 8 at.%, the absorption cross section corresponding to the 3H 6 →3H 4 energy level is 2.56 × 10−21 cm2 at 793 nm, which is suitable for GaAlAs LD pumping. The J-O strength parameters Ω 2 , Ω 4 , and Ω 6 were obtained. With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. When the concentration of Y3+ ions reaches 8 at.%, the emission cross sections are 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, and the full widths at half maximum (FWHM) are 76 nm and 195 nm, respectively. The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. • With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. • When the concentration of Y3+ ions reaches 8 at.%, the emission cross section is 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, respectively. • The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. [ABSTRACT FROM AUTHOR]