Search

2 at.% Tm, xat.% Dy:Y 2 O 3 (x = 0, 0.1, 0.5 and 1) transparent ceramics were fabricated via vacuum sintering. The microstructural properties of the prepared ceramics were determined using XRD and SEM. The absorption cross-section of 2 at.% Tm, 1 at.% Dy:Y 2 O 3 ceramic was 0.53 × 10−20 cm2 with the FWHM of 43.59 nm. The increased cross-section originates from a large overlapping range appearing in the absorption spectrum of the Dy3+:6H 15/2 → 6F 5/2 and Tm3+:3H 6 →6H 4 transitions. The J-O intensity parameters Ω 2 , Ω 4 and Ω 6 and the fluorescence characteristics of the pivotal luminescent level of the Dy3+ ions were investigated. Under 793 nm excitation, the emission cross section of the Tm,Dy:Y 2 O 3 ceramic at 3094 nm was 3.63 × 10−21 cm2 with the FWHM of 355 nm. The fluorescence lifetimes of Dy3+:6H 13/2 level of 2 at.% Tm, xat.% Dy:Y 2 O 3 (x = 0.1, 0.5 and 1) ceramics were fitted to be 357 μs, 282 μs and 149 μs, respectively. In order to explore the quenching mechanism of Tm3+:3F 4 level, the fluorescence lifetimes of Tm3+:3F 4 of the 2 at.% Tm, xat.% Dy:Y 2 O 3 ceramics (x = 0, 0.1, 0.5 and 1) were measured to be 4.878 ms, 462 μs, 104 μs and 61 μs, respectively. The possible energy transfer mechanisms between Tm3+ and Dy3+ ions are discussed. The results show that adding Tm3+ ions to Dy:Y 2 O 3 ceramics can effectively enhance the 2.9 μm MIR through energy transfer. [ABSTRACT FROM AUTHOR]

YScO 3 single crystal co-doped with Ho3+ and Pr3+ ions has been successfully grown by the Czochralaki method. The absorption spectrum, fluorescence spectrum and fluorescence decay curve were measured at room temperature. The absorption cross section of Ho,Pr:YScO 3 at 649 nm and 1130 nm was calculated to be 0.93 × 10−20 cm2 and 0.32 × 10−20 cm2, respectively. Judd-Ofelt (J-O) theory was performed to evaluate the spontaneous emission probabilities and the radiative lifetimes. Ho,Pr:YScO 3 exhibited strong emission at 2040 nm and 2890 nm with a emission cross section of 0.80 × 10−21 cm2 and 1.22 × 10−20 cm2, respectively. The fluorescence lifetime of the Ho3+:5I 6 and 5I 7 levels were calculated to be 0.31 ms and 5.89 ms, respectively. All the results indicate that the Ho,Pr:YScO 3 crystal could be a potential laser material for 2.9 μm laser operation. • Ho3+,Pr3+ co-doped YScO 3 was grown by the Czochralski method. • The crystal structure, absorption and emission spectra were investigated. • The effect of Pr3+ on the spectroscopic properties of Ho3+ was evaluated. [ABSTRACT FROM AUTHOR]

Tm3+-doped bismuth germanate crystals (Tm:BGO) with various doping concentrations of 0.5, 0.75, 1.0, 1.5, and 2.0 at.% were grown by the micro-pulling-down method (μ-PD). The effect of thulium concentration on the growth, structure, absorption spectra, emission spectra and fluorescence lifetime of 3H 4 and 3F 4 state was studied. Under excitation of 792 nm, Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. The fluorescence lifetime of 3H 4 state decreased strongly as the thulium concentration increased, while the lifetime of 3F 4 state was relatively constant for all thulium concentrations. • Tm:BGO crystals with different Tm3+ concentration were grown by the micro-pulling-down method. • The effect of Tm3+ concentration on the growth, structure and spectroscopic properties of Tm:BGO crystals was studied. • Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. [ABSTRACT FROM AUTHOR]