[Display omitted] The tissue engineering is a promising method for cartilage regeneration studies. The rough in vivo initial repair environment of articular cartilage is a challenge for the development of cartilage tissue engineering. Hereon, in this study, a silk fibroin/collagen type II scaffold was designed. The optimal mechanical environment for chondrocyte/scaffold complex in vitro maturation culture was determined and in vitro cultured mature artificial cartilage was evaluated for in vivo defect repair. Our research shows that the silk fibroin/collagen type II scaffold has good performance and can meet the special requirements of cartilage repair. 10 % compressive strain is the optimal compressive loading in vitro. Under optimal compression loading in vitro , chondrocytes can proliferate and grow rapidly on the scaffold to achieve better "maturation". The in vitro cultured chondrocyte/scaffold complex effectively improves the cartilage repair effect after implantation. The compressive elastic modulus of the new tissue reached 0.682 ± 0.010 MPa after 12 weeks of repair (0.714 ± 0.011 MPa for the surrounding host cartilage). Therefore, this study not only enhance the effect of cartilage repair but also provides a promising strategy for mechanical stimulation to promote functional in situ regeneration of articular cartilage. [ABSTRACT FROM AUTHOR]

Cracks may change the mechanical properties of articular cartilage, and further lead to early osteoarthritis. The study aimed to probe the mechanical properties of cracked cartilage under uniaxial tensile loading. The fracture process of cracked cartilage can be divided into two stages, namely crack-tip blunting stage and crack growth stage. The creep strain of cracked cartilage increases rapidly and then slowly with time, and it is well predicted by the nonlinear viscoelastic creep model. Compared with intact cartilage, cracked cartilage shows larger creep strain. During cyclic loading, the mean strain, degree of necking and crack-tip blunting of cracked cartilage increase with the increase of peak stress, while they decrease with the increase of loading frequency. The crack-tip morphology shows that cyclic loading has induced irreversible deformation in cartilage with a large number of collagen fibrils yielding, and further damaged the collagen fibril network of cartilage. However, no obvious crack growth is observed under the testing conditions. [ABSTRACT FROM AUTHOR]