Search

[Display omitted] • Highly crystalline In 2 O 3 films are grown by pulsed reactive magnetron sputtering. • Substrate heating further improves the film crystallinity and conductivity. • 400 °C is the limit for benefiting to obtain the optimum crystallinity of In 2 O 3 films. • The films deposited at 400 °C yield the lowest resistivity of 1.28 × 10-4 Ω⋅cm. • An average transmittance of greater than 80% are also obtained at 400 °C. A transparent conductive oxide (TCO) should have a combination of high electrical conductivity and optical transmission property to fulfill the challenging demands of industrial applications. So far, doped TCOs have been mostly considered to fulfill the technological challenges. In this study, we demonstrate that indium oxide (In 2 O 3) thin films without intentional doping can be deposited with high crystallinity under specific film growth conditions leading to thin films with high mobility, high electrical conductivity, and high transmittance. In 2 O 3 thin films have been deposited by reactive pulsed direct current magnetron sputtering (pulsed DCMS) from an indium target on substrates in a temperature range from room temperature (RT) to 600 °C. Detailed investigations on In 2 O 3 thin films are performed and the film properties such as crystallinity, microstructure, chemical bonding states, electrical and optical properties are revealed. Enhanced plasma density and ionization degree provided by the employed reactive pulsed DCMS and the intentional substrate heating during the thin film deposition give possibility to deposit highly crystalline thin films which are preferentially oriented in (2 2 2) direction. The substrate heating enhances the crystallinity of the grown films up to a certain optimum temperature: 400 °C. When the substrate temperature is above 400 °C, the carrier concentration and mobility decrease due to the grain refinement effect caused by growth competition of grains in different orientations. The films grown at 400 °C indicate the presence of high oxygen vacancy concentrations, which can directly be associated with a high charge carrier concentration despite the lack of intentional doping. The undoped In 2 O 3 films in this study grown at 400 °C show highly promising and competitive electrical properties such as low resistivity of 1.28 × 10-4 Ω⋅cm and the high carrier mobility of 69 cm2/Vs. The average transmittance of the In 2 O 3 films with the highest conductivity is found to be greater than 80% in the visible to the near-infrared spectral region owing to an enhancement in the carrier mobility and an optical bandgap in the range from 3.61 eV to 3.77 eV. [ABSTRACT FROM AUTHOR]

In this study, the reaction mode of high-power pulsed reactive magnetron sputtering and the crystal structure and infrared transparent conductive properties of SnOx thin films prepared at 600 °C were investigated. The effects of sputtering at different oxygen partial pressures from 10 to 24 sccm were examined. For SnOx films deposited at oxygen partial pressures of 10–14 sccm, the reaction mode was dominated by the metallic mode, and the polar unsaturated (101) plane was the preferred orientation of the film crystals. For SnOx films deposited at oxygen partial pressures of 16–18 sccm, the reaction mode was dominated by the transition mode, showing a preferred (110) plane orientation. In the deposition process, at oxygen partial pressure >18 sccm, the reaction proceeded in poisoning mode. As the oxygen partial pressure was increased, the carrier concentration decreased to 1.140 × 1015 cm−3, mobility increased to 14.93 cm2/Vs, and IR transmittance at 4 μm increased. Furthermore, excess O 2 resulted in deteriorated electrical properties of the prepared SnOx films, with a maximum resistivity of 502.9 Ω·cm. [Display omitted] • SnO x films prepared using high-power pulsed reactive magnetron sputtering at 600 °C • Crystal structures and infrared transparent conductive properties examined • Effects of sputtering at different oxygen partial pressures examined • At 16–18 sccm (O 2 partial pressure), reaction mode dominated by the transition mode • SnO x films with deteriorated electrical properties were formed due to excess O 2 [ABSTRACT FROM AUTHOR]