Search

In this study, standard diamond bars were prepared using an ultra-thick diamond plate, and the bars had sizes consistent with the International Organization for Standardization (ISO) 14704:2016(E) three-point bending method for measuring the fracture strength. Ultra-thick diamond plate with dimensions of 125 mm (diameter) × 6.5 mm (thickness) were deposited using direct current arc plasma jet chemical vapour deposition. After cutting, grinding, and polishing, 12 diamond bars meeting the requirements of the ISO standard were prepared (36 mm × 4 mm × 3 mm) and tested for fracture strength using the cited ISO standard and elastic modulus using deflection measurements. The fracture strength of the ultra-thick diamond plate was found to be 580 ± 66 MPa. In addition, for comparison, the fracture strengths of standard ZnS, sapphire, and alumina were also analysed. Crucially, this is the first report of the fracture strength of standard-sized diamond plate. The effects of the defects and grain size on the crack formation and failure of the diamond film were analysed. The diamond's fracture strength was affected by the sample thickness, which caused the gradual accumulation of defects as this dimension increased, but not by its length and width. The elastic moduli of sapphire and alumina were compared. Overall, the measurement of the fracture strengths of ultra-thick diamond plate via the ISO standard is important for industrial applications. [ABSTRACT FROM AUTHOR]

In this study, the effect of defects on fracture toughness in different directions was investigated. Two diamond films with a diameter of 122 mm and as-deposited thicknesses of 2.2 and 1.5 mm, respectively, were deposited by DC arc plasma jet chemical vapor deposition. To accurately obtain the fracture toughness, the films were ground and polished to 1.6 and 0.8 mm, respectively. The results indicate that many defects, including pores, are introduced into the films during the growth process, particularly on the side close to the growth surface in thicker film. The size of pores reaches micrometres, which affects the fracture toughness under loading in different directions. Due to the minimum grain size, both films exhibit a maximum toughness of 8.2 and 10.0 MPa·m1/2, respectively, with growth-surface cracks. For the thinner sample, the maximum value is followed by that of the edge-surface cracks. As the grain size of the edge surface falls between that of the growth surface and that of the nucleation surface, the results indicate that fracture toughness is affected by grain size. However, the number of pores near the growth side increases when the thickness exceeds 0.8 mm. Pores reduce the toughness, resulting in the minimum fracture toughness (6 MPa·m1/2) of the thicker diamond film with edge-surface laser cracks. The sample with an edge-surface sharp pre-crack has a similar fracture toughness of 5.6 MPa·m1/2. This study provides guidance for selecting the applied load direction. • Two thick diamond films with thicknesses 2.18 and 1.48 mm were deposited. • Fracture toughnesses of the diamond films in three directions were investigated. • Numerous pores were formed in the diamond films during orientation growth. • Due to the effect of pores, the toughness values among three directions differ. [ABSTRACT FROM AUTHOR]